Effect of Nitrogen Doping on the Performance of Mesoporous CMK-8 Carbon Anodes for Li-Ion Batteries

Calcagno, Giulio, 1990 (författare)
Chalmers University of Technology,Chalmers tekniska högskola
Agostini, Marco, 1987 (författare)
Chalmers University of Technology,Chalmers tekniska högskola
Xiong, Shizhao, 1985 (författare)
Chalmers University of Technology,Chalmers tekniska högskola
visa fler...
Matic, Aleksandar, 1968 (författare)
Chalmers University of Technology,Chalmers tekniska högskola
Palmqvist, Anders, 1966 (författare)
Chalmers University of Technology,Chalmers tekniska högskola
Cavallo, Carmen, 1986 (författare)
University of Oslo, Norway,Chalmers University of Technology,Chalmers tekniska högskola
visa färre...
 (creator_code:org_t)
2020
2020
Engelska.
Ingår i: Energies. - 1996-1073. ; 13:19
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • Designing carbonaceous materials with heightened attention to the structural properties such as porosity, and to the functionalization of the surface, is a growing topic in the lithium-ion batteries (LIBs) field. Using a mesoporous silica KIT-6 hard template, mesoporous carbons belonging to the OMCs (ordered mesoporous carbons) family, namely 3D cubic CMK-8 and N-CMK-8 were synthesized and thoroughly structurally characterized. XPS analysis confirmed the successful introduction of nitrogen, highlighting the nature of the different nitrogen atoms incorporated in the structure. The work aims at evaluating the electrochemical performance of N-doped ordered mesoporous carbons as an anode in LIBs, underlining the effect of the nitrogen functionalization. The N-CMK-8 electrode reveals higher reversible capacity, better cycling stability, and rate capability, as compared to the CMK-8 electrode. Coupling the 3D channel network with the functional N-doping increased the reversible capacity to similar to 1000 mAh center dot g(-1) for the N-CMK-8 from similar to 450 mAh center dot g(-1) for the undoped CMK-8 electrode. A full Li-ion cell was built using N-CMK-8 as an anode, commercial LiFePO4, a cathode, and LP30 commercial electrolyte, showing stable performance for 100 cycles. The combination of nitrogen functionalization and ordered porosity is promising for the development of high performing functional anodes.

Ämnesord

NATURVETENSKAP  -- Kemi (hsv//swe)
TEKNIK OCH TEKNOLOGIER  -- Kemiteknik (hsv//swe)
NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)
ENGINEERING AND TECHNOLOGY  -- Chemical Engineering (hsv//eng)

Nyckelord

lithium-ion batteries (LIB)
ordered mesoporous carbon (OMC)
CMK-8
nitrogen doping
functional materials

Publikations- och innehållstyp

ref (ämneskategori)
art (ämneskategori)

Hitta via bibliotek

  • Energies (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy