Coated stainless steel 441 as interconnect material for solid oxide fuel cells: Oxidation performance and chromium evaporation

Grolig, Jan Gustav,1986Oorganisk miljökemi,Institutionen för kemi- och bioteknik,Chalmers tekniska högskola,Environmental Inorganic Chemistry,Department of Chemical and Biological Engineering,Chalmers University of Technology (författare)

Reactive Element (RE) and RE/cobalt-coated stainless steel AISI 441 was exposed at Solid Oxide Fuel Cell (SOFC) cathode conditions (850 degrees C in air with 3% water content) for up to 500 h. The chromium evaporation was measured by applying the denuder technique. Uncoated material exhibited severe spallation which could be successfully prevented by using cerium or lanthanum coatings. By applying double layer coatings of cerium or lanthanum in combination with cobalt the oxidation rate was decreased and the chromium volatilisation was also about 90% lower than the uncoated material.

Froitzheim, Jan,1981Oorganisk miljökemi,Institutionen för kemi- och bioteknik,Chalmers tekniska högskola,Environmental Inorganic Chemistry,Department of Chemical and Biological Engineering,Chalmers University of Technology(Swepub:cth)froitzhe (författare)
Svensson, Jan-Erik,1965Oorganisk miljökemi,Institutionen för kemi- och bioteknik,Chalmers tekniska högskola,Environmental Inorganic Chemistry,Department of Chemical and Biological Engineering,Chalmers University of Technology(Swepub:cth)jes (författare)
Oorganisk miljökemiInstitutionen för kemi- och bioteknik (creator_code:org_t)

Av författaren/redakt...: Grolig, Jan Gust ...; Froitzheim, Jan, ...; Svensson, Jan-Er ...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst. Hantera kakor