1.	Hameed, Arslan, et al. (författare) ZIF-12/Fe-Cu LDH Composite as a High Performance Electrocatalyst for Water Oxidation 2021 Ingår i: Frontiers in Chemistry. - : Frontiers Media S.A.. - 2296-2646. ; 9 Tidskriftsartikel (refereegranskat)abstract Layered double hydroxides (LDH) are being used as electrocatalysts for oxygen evolution reactions (OERs). However, low current densities limit their practical applications. Herein, we report a facile and economic synthesis of an iron-copper based LDH integrated with a cobalt-based metal-organic framework (ZIF-12) to form LDH-ZIF-12 composite (1) through a co-precipitation method. The as-synthesized composite 1 requires a low overpotential of 337 mV to achieve a catalytic current density of 10 mA cm−2 with a Tafel slope of 89 mV dec−1. Tafel analysis further demonstrates that 1 exhibits a slope of 89 mV dec−1 which is much lower than the slope of 284 mV dec−1 for LDH and 172 mV dec−1 for ZIF-12. The slope value of 1 is also lower than previously reported electrocatalysts, including Ni-Co LDH (113 mV dec−1) and Zn-Co LDH nanosheets (101 mV dec−1), under similar conditions. Controlled potential electrolysis and stability test experiments show the potential application of 1 as a heterogeneous electrocatalyst for water oxidation.

Hameed, Arslan, et al. (författare)
ZIF-12/Fe-Cu LDH Composite as a High Performance Electrocatalyst for Water Oxidation
2021
Ingår i: Frontiers in Chemistry. - : Frontiers Media S.A.. - 2296-2646. ; 9
Tidskriftsartikel (refereegranskat)abstract
- Layered double hydroxides (LDH) are being used as electrocatalysts for oxygen evolution reactions (OERs). However, low current densities limit their practical applications. Herein, we report a facile and economic synthesis of an iron-copper based LDH integrated with a cobalt-based metal-organic framework (ZIF-12) to form LDH-ZIF-12 composite (1) through a co-precipitation method. The as-synthesized composite 1 requires a low overpotential of 337 mV to achieve a catalytic current density of 10 mA cm−2 with a Tafel slope of 89 mV dec−1. Tafel analysis further demonstrates that 1 exhibits a slope of 89 mV dec−1 which is much lower than the slope of 284 mV dec−1 for LDH and 172 mV dec−1 for ZIF-12. The slope value of 1 is also lower than previously reported electrocatalysts, including Ni-Co LDH (113 mV dec−1) and Zn-Co LDH nanosheets (101 mV dec−1), under similar conditions. Controlled potential electrolysis and stability test experiments show the potential application of 1 as a heterogeneous electrocatalyst for water oxidation.

Träfflista för sökning "WFRF:(Abbas Saghir) "