- Barkhordarian, Gagik, et al.
(författare)
-
Formation of Ca(BH4)(2) from hydrogenation of CaH2+MgB2 composite
- 2008
-
Ingår i: Journal of Physical Chemistry C. - : American Chemical Society (ACS). - 1932-7447 .- 1932-7455. ; 112:7, s. 2743-2749
-
Tidskriftsartikel (refereegranskat)abstract
- The hydrogenation of the CaH2+MgB2 Composite and the dehydrogenation of the resulting products are investigated in detail by in situ time-resolved synchrotron radiation powder X-ray diffraction, high-pressure differential scanning calorimetry, infrared, and thermovolumetric measurements. It is demonstrated that a Ca(BH4)(2)+MgH2 composite is formed by hydrogenating a CaH2+MgB2 composite, at 350 degrees C and 140 bar of hydrogen. Two phases of Ca(BH4)(2) were characterized: alpha- and beta-Ca(BH4)(2). alpha-Ca(BH4)(2) transforms to beta-Ca(BH4)(2) at about 130 degrees C. Under the conditions used in the present study, beta-Ca(BH4)(2) decomposes first to CaH2, Ca3Mg4H14, Mg, B (or MgB2 depending on experimental conditions), and hydrogen at 360 degrees C, before complete decomposition to CaH2, Mg, B (or MgB2), and hydrogen at 400 degrees C. During hydrogenation under 140 bar of hydrogen, beta-Ca(BH4)(2) is formed at 250 degrees C, and alpha-Ca(BH4)(2) is formed when the sample is cooled to less than 130 degrees C. Ti isopropoxide improves the kinetics of the reactions, during both hydrogenation and dehydrogenation. The dehydrogenation temperature decreases to 250 degrees C, with 1 wt % of this additive, and hydrogenation starts already at 200 degrees C. We propose that the improved kinetics of the above reactions with MgB2 (compared to pure boron) can be explained by the different boron bonding within the crystal structure of MgB2 and pure boron.
|
|
| 2. |
- Boesenberg, Ulrike, et al.
(författare)
-
Hydrogen sorption properties of MgH2-LiBH4 composites
- 2007
-
Ingår i: Acta Materialia. - : Elsevier BV. - 1873-2453 .- 1359-6454. ; 55:11, s. 3951-3958
-
Tidskriftsartikel (refereegranskat)abstract
- A detailed analysis of the reaction mechanism of the reactive hydride composite (RHC) MgH2 + 2LiBH(4) <-> MgB2 + 2LiH + 4H(2) was performed using high-pressure differential scanning calorimetry (HP-DSC) measurements and in situ synchrotron powder X-ray diffraction (XRD) measurements along with kinetic investigations using a Sievert-type apparatus. For the desorption the following two-step reaction has been observed: MgH2 + 2LiBH(4) <-> Mg + 2LiBH(4) + H-2 <-> MgB2 + 2LiH + 4H(2). However, this reaction is kinetically restricted and proceeds only at elevated temperatures. In contrast to the desorption reaction, LiBH4 and MgH2 are found to form simultaneously under fairly moderate conditions of 50 bar hydrogen pressure in the temperature range of 250-300 degrees C. As found in pure light metal hydrides, significant improvement of sorption kinetics is possible if suitable additives are used. (c) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
|
|
| 3. |
- Gosalawit-Utke, Rapee, et al.
(författare)
-
Ca(BH4)(2)-MgF2 Reversible Hydrogen Storage: Reaction Mechanisms and Kinetic Properties
- 2011
-
Ingår i: Journal of Physical Chemistry C. - : American Chemical Society (ACS). - 1932-7447 .- 1932-7455. ; 115:9, s. 3762-3768
-
Tidskriftsartikel (refereegranskat)abstract
- A composite of Ca(BH4)(2)-MgF2 is proposed as a reversible hydrogen storage system. The dehydrogenation and rehydrogenation reaction mechanisms are investigated by in situ time-resolved synchrotron radiation powder X-ray diffraction (SR-PXD) and Raman spectroscopy. The formation of an intermediate phase (CaF2-xHx) is observed during rehydrogenation. The hydrogen content of 4.3 wt % is obtained within 4 h during the first dehydrogenation at isothermal and isobaric conditions of 330 degrees C and 0.5 bar H-2, respectively. The cycling efficiency is evaluated by three release and uptake cycles together with absorbed hydrogen content in the range 5.1-5.8 wt % after 2.5 h (T = 330 degrees C and p(H-2) = 130 bar). The kinetic properties on the basis of hydrogen absorption are comparable for all cycles. As compared to pure Ca(BH4)(2) and Ca(BH4)(2)-MgH2 composite, Ca(BH4)(2)-MgF2 composite reveals the kinetic destabilization and the reproducibility of hydrogen storage capacities during cycling, respectively.
|
|
| 4. |
- Minella, Christian Bonatto, et al.
(författare)
-
Effect of Transition Metal Fluorides on the Sorption Properties and Reversible Formation of Ca(BH4)(2)
- 2011
-
Ingår i: Journal of Physical Chemistry C. - : American Chemical Society (ACS). - 1932-7447 .- 1932-7455. ; 115:5, s. 2497-2504
-
Tidskriftsartikel (refereegranskat)abstract
- Light metal borohydrides are considered as promising materials for solid state hydrogen storage. Because of the high hydrogen content of 11.5 wt % and the rather low dehydrogenation enthalpy of 32 kJ mol(-1)H(2), Ca(BH4)(2) is considered to be one of the most interesting compounds in this class of materials. In the present work, the effect of selected TM-fluoride (TM = transition metal) additives on the reversible formation of Ca(BH4)(2) was investigated by means of thermovolumetric, calorimetric, Fourier transform infrared spectroscopy, and ex situ, and in situ synchrotron radiation powder X-ray diffraction (SR-PXD) measurements. Furthermore, selected desorbed samples were analyzed by B-11{H-1} solid state magic angle spinning nuclear magnetic resonance (MAS NMR). Under the conditions used in this study (145 bar H-2 pressure and 350 degrees C), TiF4 and NbF5 were the only additives causing partial reversibility. In these two cases, B-11{H-1} MAS NMR analyses detected CaB6 and likely CaB12H12 in the dehydrogenation products. Elemental boron was found in the decomposition products of Ca(BH4)(2) samples with VF4, TiF3, and VF3. The results indicate an important role of CaB6 for the reversible formation of Ca(BH4)(2).
|
|