| 1. |
- Koo, Jun Mo, et al.
(författare)
-
Biobased thermoplastic elastomer with seamless 3D-Printability and superior mechanical properties empowered by in-situ polymerization in the presence of nanocellulose
- 2020
-
Ingår i: Composites Science And Technology. - : Elsevier BV. - 0266-3538 .- 1879-1050. ; 185
-
Tidskriftsartikel (refereegranskat)abstract
- A biobased and biocompatible thermoplastic elastomer (TPE) with superior 3D printability was demonstrated with great potential for customized manufacturing technologies and fabrication of biointegrated devices. The inherent structural and stereochemical disadvantages of biobased monomers, such as 2,5-furandicarboxylic acid, in comparison with today used petroleum based monomers like terephthalic acid generally lead to lower mechanical performance for the biobased replacement polymers. This is additionally enhanced by poor interfacial adhesion and fusion commonly encountered during customized manufacturing technologies like 3D printing. Herein, we demonstrate that in-situ polymerization in the presence of trace amounts of cellulose nanocrystals (CNCs) can homogeneously distribute the nanofiller leading to dramatically strengthened thermally 3D-printable bio-furan-based TPE. This TPE exhibited a tensile strength of 67 MPa which is 1.5-7-fold higher than the values reported for silicone and thermoplastic urethane, which are widely used in biomedical applications. In addition, the TPE had an impressive extensibility of 860% and negligible in vivo cytotoxicity; such properties have not been reported to date for bio-based or petrochemical TPEs. While a petrochemical 3D printed TPE counterpart retained only half of the tensile strength compared to the hot-pressed analogue, the 3D-printed biobased TPE insitu modified with nanocellulose maintained 70-80% of its strength under the same experimental conditions. This is explained by inter-diffusion between interfaces facilitated by the nanocellulose and the furan rings. Using the ergonomic shape of a wrist as a 3D-printable design, we successfully manufactured a wearable thermal therapeutic device from the nanocellulose modified biobased TPE, giving promise for wide variety of future applications.
|
|
| 2. |
- Koo, Jun Mo, et al.
(författare)
-
Nonstop Monomer-to-Aramid Nanofiber Synthesis with Remarkable Reinforcement Ability
- 2019
-
Ingår i: Macromolecules. - : American Chemical Society (ACS). - 0024-9297 .- 1520-5835. ; 52:3, s. 923-934
-
Tidskriftsartikel (refereegranskat)abstract
- Aramid nanofibers (ANFs), typically produced by exfoliating aramid microfibers (Kevlar) in alkaline media, exhibit excellent mechanical properties and have therefore attracted increased attention as nanoscale building blocks. However, the preparation of aramid microfibers involves laborious and hazardous processes, which limits the industrial-scale use of ANFs. This work describes a facile and direct monomer-to-ANF synthesis via an as-synthesized intermediate low-molecular-weight poly(p-phenylene terephthalamide) (PPTA) without requiring the environmentally destructive acids and high-order shearing processes. Under the employed conditions, PPTA immediately dissociates and self-assembles into ANFs within a time period of 15 h, which is much shorter than the time of 180 h (not including the Kevlar preparation time) required for the Kevlar-to-ANF conversion. Interestingly, the fabricated ANFs exhibit nanoscale dimensions and thermoplastic polyurethane (TPU) reinforcing effects similar to those of Kevlar-derived ANFs; i.e., a 1.5-fold TPU toughness improvement and a maximum ultimate tensile strength of 84 MPa are achieved at an ANF content of only 0.04 wt %. Remarkable reinforcement ability investigated by comprehensive analytical data comes from ANFs, which disturb ordered hydrogen bonding in hard segments and induce strain hardening along the elongation pathway. Thus, the developed approach paves the way to industrial-scale production of ANFs and related nanocomposites.
|
|