| 1. |
- Gogova, D., et al.
(författare)
-
High crystalline quality homoepitaxial Si-doped β-Ga2O3(010) layers with reduced structural anisotropy grown by hot-wall MOCVD
- 2024
-
Ingår i: Journal of Vacuum Science and Technology A: Vacuum, Surfaces and Films. - 0734-2101. ; 42:2
-
Tidskriftsartikel (refereegranskat)abstract
- A new growth approach, based on the hot-wall metalorganic chemical vapor deposition concept, is developed for high-quality homoepitaxial growth of Si-doped single-crystalline β -Ga 2 O 3 layers on (010)-oriented native substrates. Substrate annealing in argon atmosphere for 1 min at temperatures below 600 ° C is proposed for the formation of epi-ready surfaces as a cost-effective alternative to the traditionally employed annealing process in oxygen-containing atmosphere with a time duration of 1 h at about 1000 ° C. It is shown that the on-axis rocking curve widths exhibit anisotropic dependence on the azimuth angle with minima for in-plane direction parallel to the [001] and maximum for the [100] for both substrate and layer. The homoepitaxial layers are demonstrated to have excellent structural properties with a β -Ga 2 O 3 (020) rocking curve full-widths at half-maximum as low as 11 arc sec, which is lower than the corresponding one for the substrates (19 arc sec), even for highly Si-doped (low 10 19 cm − 3 range) layers. Furthermore, the structural anisotropy in the layer is substantially reduced with respect to the substrate. Very smooth surface morphology of the epilayers with a root mean square roughness value of 0.6 nm over a 5 × 5 μ m 2 area is achieved along with a high electron mobility of 69 cm 2 V − 1 s − 1 at a free carrier concentration n = 1.9 × 10 19 cm − 3 . These values compare well with state-of-the-art parameters reported in the literature for β -Ga 2 O 3 (010) homoepitaxial layers with respective Si doping levels. Thermal conductivity of 17.4 W m − 1 K − 1 is determined along the [010] direction for the homoepitaxial layers at 300 K, which approaches the respective value of bulk crystal (20.6 W m − 1 K − 1 ). This result is explained by a weak boundary effect and a low dislocation density in the homoepitaxial layers.
|
|
| 2. |
- Ashkenov, N., et al.
(författare)
-
Infrared dielectric functions and phonon modes of high-quality ZnO films
- 2003
-
Ingår i: Journal of Applied Physics. - : AIP Publishing. - 0021-8979 .- 1089-7550. ; 93:1, s. 126-133
-
Tidskriftsartikel (refereegranskat)abstract
- A study was performed on the phonon modes and infrared dielectric functions of high-quality ZnO thin films. The pulsed laser deposition technique was used to deposit the ZnO films on c-plane sapphire substrates and were investigated by high-resolution transmission electron microscopy, high-resolution x-ray diffraction and Rutherford backscattering experiments. The accurate long-wavelength dielectric constant limits of the films were also obtained and were compared with near-band-gap index-of-refraction data upon the Lyddane-Sachs-Teller relation for both film and bulk samples. It was found that the phonon modes of the film were highly consistent with those of the bulk sample.
|
|
| 3. |
- Darakchieva, V., et al.
(författare)
-
Phonons in strained AlGaN/GaN superlattices
- 2007
-
Ingår i: Physica Status Solidi. C, Current topics in solid state physics. - : Wiley. - 1610-1634 .- 1610-1642. ; 4:1, s. 170-174
-
Tidskriftsartikel (refereegranskat)abstract
- Phonons in strained AlGaN/GaN superlattices (SLs) with constant periods but different Al composition have been studied using a combination of infrared spectroscopic ellipsometry and Raman scattering spectroscopy. The following SL modes were identified: i) AlGaN localized E1(TO) modes identified for the first time and AlGaN localized A1 (LO) phonons; ii) GaN localized E2, E1(TO) and A1(LO) phonons; iii) delocalized E1(LO) phonons; iv) A1(TO) phonon; v) two modes around 660 cm-1 and 594-625 cm-1, respectively, not predicted by theory. The effects of strain and composition on the phonon frequencies were established and discussed.
|
|
| 4. |
- Kimel, Alexey, et al.
(författare)
-
The 2022 magneto-optics roadmap
- 2022
-
Ingår i: Journal of Physics D. - : Institute of Physics (IOP). - 0022-3727 .- 1361-6463. ; 55:46
-
Tidskriftsartikel (refereegranskat)abstract
- Magneto-optical (MO) effects, viz. magnetically induced changes in light intensity or polarization upon reflection from or transmission through a magnetic sample, were discovered over a century and a half ago. Initially they played a crucially relevant role in unveiling the fundamentals of electromagnetism and quantum mechanics. A more broad-based relevance and wide-spread use of MO methods, however, remained quite limited until the 1960s due to a lack of suitable, reliable and easy-to-operate light sources. The advent of Laser technology and the availability of other novel light sources led to an enormous expansion of MO measurement techniques and applications that continues to this day (see section 1). The here-assembled roadmap article is intended to provide a meaningful survey over many of the most relevant recent developments, advances, and emerging research directions in a rather condensed form, so that readers can easily access a significant overview about this very dynamic research field. While light source technology and other experimental developments were crucial in the establishment of today's magneto-optics, progress also relies on an ever-increasing theoretical understanding of MO effects from a quantum mechanical perspective (see section 2), as well as using electromagnetic theory and modelling approaches (see section 3) to enable quantitatively reliable predictions for ever more complex materials, metamaterials, and device geometries. The latest advances in established MO methodologies and especially the utilization of the MO Kerr effect (MOKE) are presented in sections 4 (MOKE spectroscopy), 5 (higher order MOKE effects), 6 (MOKE microscopy), 8 (high sensitivity MOKE), 9 (generalized MO ellipsometry), and 20 (Cotton–Mouton effect in two-dimensional materials). In addition, MO effects are now being investigated and utilized in spectral ranges, to which they originally seemed completely foreign, as those of synchrotron radiation x-rays (see section 14 on three-dimensional magnetic characterization and section 16 on light beams carrying orbital angular momentum) and, very recently, the terahertz (THz) regime (see section 18 on THz MOKE and section 19 on THz ellipsometry for electron paramagnetic resonance detection). Magneto-optics also demonstrates its strength in a unique way when combined with femtosecond laser pulses (see section 10 on ultrafast MOKE and section 15 on magneto-optics using x-ray free electron lasers), facilitating the very active field of time-resolved MO spectroscopy that enables investigations of phenomena like spin relaxation of non-equilibrium photoexcited carriers, transient modifications of ferromagnetic order, and photo-induced dynamic phase transitions, to name a few. Recent progress in nanoscience and nanotechnology, which is intimately linked to the achieved impressive ability to reliably fabricate materials and functional structures at the nanoscale, now enables the exploitation of strongly enhanced MO effects induced by light–matter interaction at the nanoscale (see section 12 on magnetoplasmonics and section 13 on MO metasurfaces). MO effects are also at the very heart of powerful magnetic characterization techniques like Brillouin light scattering and time-resolved pump-probe measurements for the study of spin waves (see section 7), their interactions with acoustic waves (see section 11), and ultra-sensitive magnetic field sensing applications based on nitrogen-vacancy centres in diamond (see section 17). Despite our best attempt to represent the field of magneto-optics accurately and do justice to all its novel developments and its diversity, the research area is so extensive and active that there remains great latitude in deciding what to include in an article of this sort, which in turn means that some areas might not be adequately represented here. However, we feel that the 20 sections that form this 2022 magneto-optics roadmap article, each written by experts in the field and addressing a specific subject on only two pages, provide an accurate snapshot of where this research field stands today. Correspondingly, it should act as a valuable reference point and guideline for emerging research directions in modern magneto-optics, as well as illustrate the directions this research field might take in the foreseeable future.
|
|
| 5. |
- Papamichail, Alexis, et al.
(författare)
-
Mg-doping and free-hole properties of hot-wall MOCVD GaN
- 2022
-
Ingår i: Journal of Applied Physics. - : AIP Publishing. - 0021-8979 .- 1089-7550. ; 131:18
-
Tidskriftsartikel (refereegranskat)abstract
- The hot-wall metal-organic chemical vapor deposition (MOCVD), previously shown to enable superior III-nitride material quality and high performance devices, has been explored for Mg doping of GaN. We have investigated the Mg incorporation in a wide doping range (2.45 × 10 18 cm-3 up to 1.10 × 10 20 cm-3) and demonstrate GaN:Mg with low background impurity concentrations under optimized growth conditions. Dopant and impurity levels are discussed in view of Ga supersaturation, which provides a unified concept to explain the complexity of growth conditions impact on Mg acceptor incorporation and compensation. The results are analyzed in relation to the extended defects, revealed by scanning transmission electron microscopy, x-ray diffraction, and surface morphology, and in correlation with the electrical properties obtained by Hall effect and capacitance-voltage (C-V) measurements. This allows to establish a comprehensive picture of GaN:Mg growth by hot-wall MOCVD providing guidance for growth parameters optimization depending on the targeted application. We show that substantially lower H concentration as compared to Mg acceptors can be achieved in GaN:Mg without any in situ or post-growth annealing resulting in p-type conductivity in as-grown material. State-of-the-art p-GaN layers with a low resistivity and a high free-hole density (0.77 ω cm and 8.4 × 10 17 cm - 3, respectively) are obtained after post-growth annealing demonstrating the viability of hot-wall MOCVD for growth of power electronic device structures.
|
|
| 6. |
- Paskova, T., et al.
(författare)
-
Strain-free low-defect-density bulk GaN with nonpolar orientations
- 2006
-
Ingår i: MRS Proceedings. - : Springer Science and Business Media LLC. - 1946-4274.
-
Konferensbidrag (refereegranskat)abstract
- Bulk GaN sliced in bars along (11-20) and (1-100) planes from a boule grown in the [0001] direction by HVPE was confirmed as strain free material with a low dislocation density by using several characterization techniques. The high-structural quality of the material allows photoluminescence studies of free excitons, principal donor bound excitons and their twoelectron satellites with regard to the optical selection rules. Raman scattering study of the bulk GaN with nonpolar orientations allows a direct access to the active phonon modes and a direct determination of their strain-free positions.
|
|
| 7. |
- Persson, P. O.Å., et al.
(författare)
-
Tuning composition in graded AlGaN channel HEMTs toward improved linearity for low-noise radio-frequency amplifiers
- 2023
-
Ingår i: Applied Physics Letters. - : AIP Publishing. - 0003-6951 .- 1077-3118. ; 122:15
-
Tidskriftsartikel (refereegranskat)abstract
- Compositionally graded channel AlGaN/GaN high electron mobility transistors (HEMTs) offer a promising route to improve device linearity, which is necessary for low-noise radio-frequency amplifiers. In this work, we demonstrate different grading profiles of a 10-nm-thick AlxGa1-xN channel from x = 0 to x = 0.1 using hot-wall metal-organic chemical vapor deposition (MOCVD). The growth process is developed by optimizing the channel grading and the channel-to-barrier transition. For this purpose, the Al-profiles and the interface sharpness, as determined from scanning transmission electron microscopy combined with energy-dispersive x-ray spectroscopy, are correlated with specific MOCVD process parameters. The results are linked to the channel properties (electron density, electron mobility, and sheet resistance) obtained by contactless Hall and terahertz optical Hall effect measurements coupled with simulations from solving self-consistently Poisson and Schrödinger equations. The impact of incorporating a thin AlN interlayer between the graded channel and the barrier layer on the HEMT properties is investigated and discussed. The optimized graded channel HEMT structure is found to have similarly high electron density (∼9 × 10 12 cm-2) as the non-graded conventional structure, though the mobility drops from ∼ 2360 cm2/V s in the conventional to ∼ 960 cm2/V s in the graded structure. The transconductance gm of the linearly graded channel HEMTs is shown to be flatter with smaller g m ′ and g m ″ as compared to the conventional non-graded channel HEMT implying improved device linearity.
|
|