| 1. |
- Balachandramurthi, Arun Ramanathan, et al.
(författare)
-
Influence of defects and as-built surface roughness on fatigue properties of additively manufactured Alloy 718
- 2018
-
Ingår i: Materials Science & Engineering. - : Elsevier BV. - 0921-5093 .- 1873-4936. ; 735, s. 463-474
-
Tidskriftsartikel (refereegranskat)abstract
- Electron beam melting (EBM) and Selective Laser Melting (SLM) are powder bed based additive manufacturing (AM) processes. These, relatively new, processes offer advantages such as near net shaping, manufacturing complex geometries with a design space that was previously not accessible with conventional manufacturing processes, part consolidation to reduce number of assemblies, shorter time to market etc. The aerospace and gas turbine industries have shown interest in the EBM and the SLM processes to enable topology-optimized designs, parts with lattice structures and part consolidation. However, to realize such advantages, factors affecting the mechanical properties must be well understood – especially the fatigue properties. In the context of fatigue performance, apart from the effect of different phases in the material, the effect of defects in terms of both the amount and distribution and the effect of “rough†as-built surface must be studied in detail. Fatigue properties of Alloy 718, a Ni-Fe based superalloy widely used in the aerospace engines is investigated in this study. Four point bending fatigue tests have been performed at 20 Hz in room temperature at different stress ranges to compare the performance of the EBM and the SLM material to the wrought material. The experiment aims to assess the differences in fatigue properties between the two powder bed AM processes as well as assess the effect of two post-treatment methods namely – machining and hot isostatic pressing (HIP). Fractography and metallography have been performed to explain the observed properties. Both HIPing and machining improve the fatigue performance; however, a large scatter is observed for machined specimens. Fatigue properties of SLM material approach that of wrought material while in EBM material defects severely affect the fatigue life. © 2018 Elsevier B.V.
|
|
| 2. |
- Balachandramurthi, Arun Ramanathan, 1989-, et al.
(författare)
-
Microstructural influence on fatigue crack propagation during high cycle fatigue testing of additively manufactured Alloy 718
- 2019
-
Ingår i: Materials Characterization. - : Elsevier BV. - 1044-5803 .- 1873-4189. ; 149, s. 82-94
-
Tidskriftsartikel (refereegranskat)abstract
- A study of the microstructure of additively manufactured Alloy 718 was performed in order to better understand the parameters that have an influence on the fatigue properties of the material. The specimens were manufactured using two powder bed fusion techniques – Electron Beam Melting (EBM) and Selective Laser Melting (SLM). Four point bending fatigue tests were performed at room temperature with a stress ratio of R = 0.1 and 20 Hz frequency, on material that was either in hot isostatically pressed (HIP) and solution treated and aged (STA) condition or in STA condition without a prior HIP treatment. The grains in the SLM material in the HIP + STA condition have grown considerably both in the hatch and the contour regions; EBM material, in contrast, shows grain growth only in the contour region. Fractographic analysis of the specimens in HIP + STA condition showed a faceted appearance while the specimens in STA condition showed a more planar crack appearance. The crack propagation occurred in a transgranular mode and it was found that precipitatessuch as NbC, TiN or δ-phase, when present, did not affect the crack path. The areas with larger grains corresponded to the faceted appearance of the fracture surface. This could be attributed to the plastic zone ahead of the crack tip being confined within one grain, in case of the larger grains, which promotes single shear crack growth mode
|
|
| 3. |
- Kumara, Chamara, et al.
(författare)
-
Microstructure modelling of laser metal powder directed energy deposition of alloy 718
- 2019
-
Ingår i: Additive Manufacturing. - : Elsevier. - 2214-8604 .- 2214-7810. ; 25, s. 357-364
-
Tidskriftsartikel (refereegranskat)abstract
- A multi-component and multi-phase-field modelling approach, combined with transformation kinetics modelling, was used to model microstructure evolution during laser metal powder directed energy deposition of Alloy 718 and subsequent heat treatments. Experimental temperature measurements were utilised to predict microstructural evolution during successive addition of layers. Segregation of alloying elements as well as formation of Laves and δ phase was specifically modelled. The predicted elemental concentrations were then used in transformation kinetics to estimate changes in Continuous Cooling Transformation (CCT) and Time Temperature Transformation (TTT) diagrams for Alloy 718. Modelling results showed good agreement with experimentally observed phase evolution within the microstructure. The results indicate that the approach can be a valuable tool, both for improving process understanding and for process development including subsequent heat treatment.
|
|