- Fredriksson, Hasse, 1939-, et al.
(författare)
-
Thoughts about the Initial Solidification Process during Continuous Casting of Steel
- 2002
-
Ingår i: Scandinavian journal of metallurgy. - : Wiley. - 0371-0459 .- 1600-0692. ; 31, s. 292-297
-
Tidskriftsartikel (övrigt vetenskapligt/konstnärligt)abstract
- The initial solidification during continuous casting is very important for the surface quality of the strand. Oscillation marks are formed by the movement of the mould. One mainly distinguishes between two different types of marks, namely folding marks and overflow marks. The formation of these can be described by the heat flow and the surface tension balance. A theoretical analysis outlining the most important parameters controlling the formation of these marks is presented. A metallographic analysis of the formation was also performed. The theory and observations have been used to analyse the effect of casting speed and oscillation frequency on the formation of different types of marks. It is shown that a meniscus is formed at the top of the growing shell. The maximum height of the meniscus determines the ideal distance between the marks. The mould frequency is related to this height. A frequency that is far from ideal causes overflow marks and folding marks with macrosegregation and cracks. The distance between the marks is, in such cases, not constant. The depth of the marks is calculated from the heat flow and the surface tension balance.
|
|