- Ilyas, Muhammad Tasaduq, et al.
(författare)
-
Substantial performance of copper sulfide nanotubes at high current densities for energy storage applications
- 2024
-
Ingår i: Journal of Energy Storage. - : Elsevier. - 2352-152X .- 2352-1538. ; 85
-
Tidskriftsartikel (refereegranskat)abstract
- This study presents the direct growth of CuS nanotubes (NTs) on nickel foam using a facile solution synthesis route. The structural, elemental and morphological analyses of CuS NTs grown Ni foam were conducted through X-ray diffraction, energy dispersive X-ray spectroscopy, scanning electron microscope, and field emission scanning electron microscope. The electrochemical performance of the prepared electrodes was comprehensively characterized by cyclic voltammetry (CV), galvanostatic charge discharge and electrochemical impedance spectroscopy. The CuS NTs grown electrodes delivered a specific capacitance of 1539 Fg−1 at 1 mVs−1 and 1365 Fg−1 at 5 Ag−1, demonstrating a remarkable rate capability of 66 % at an extremely high current density of 25 Ag−1. Notably, the CuS NTs electrode demonstrated good cyclic stability, as evidenced by a charge retention of 75.5 % after 3000 cycles at a high current density of 20 Ag−1. The charge storage mechanism was predominantly diffusion controlled, accomplished by analyzing CV data. Overall, this work evinces that the as-synthesized CuS NTs hold a significant promise as electrode materials for high-performance electrochemical energy storage applications.
|
|
| 2. |
- Raza, Mohsin Ali, et al.
(författare)
-
Synthesis and characterization of zinc aluminate electrodes for supercapacitor applications
- 2024
-
Ingår i: Electrochimica Acta. - : Elsevier. - 0013-4686 .- 1873-3859. ; 475
-
Tidskriftsartikel (refereegranskat)abstract
- We report, for the first time, the thorough electrochemical characterization of zinc aluminate spinel. Four different stoichiometric composition of zinc aluminate (ZnAl1.5O3.25, ZnAl2O4, ZnAl2.87O5.30, and ZnAl4O7) were prepared by solution combustion method. The obtained powders after calcination at 1000 °C were characterized through scanning electron microscope (SEM), energy dispersive x-ray spectroscopy (EDX) and x-ray diffraction to analyze the morphology, elemental composition and structure, respectively, of the zinc aluminate compositions. The electrodes were prepared by coating slurry of zinc aluminate, carbon black and polyvinylidene fluoride on nickel foam in a ratio of 8:1:1. The electrochemical characterization was carried out by cyclic voltammetry (CV), galvanostatic charge discharge (GCD) and electrochemical impedance spectroscopy (EIS). ZnAl1.5O3.25 exhibited the highest specific capacity of 546 C/g at 1 mV/s and 336 C/g at 1 A/g, as appraised by CV and GCD analysis, respectively. EIS test revealed that ZnAl1.5O3.25 had the modest impedance value. The energy density value for ZnAl1.5O3.25 sample was 16.79 Wh/kg at 1 A/g with a power density of 179.9 W/kg. The as developed electrodes showed predominantly pseudo-capacitive charge storage mechanism.
|
|