| 1. |
- Ferraris, Sara, et al.
(författare)
-
Chemical, mechanical and antibacterial properties of silver nanocluster/silica composite coated textiles for safety systems and aerospace applications
- 2014
-
Ingår i: Applied Surface Science. - : Elsevier BV. - 0169-4332 .- 1873-5584. ; 317, s. 131-139
-
Tidskriftsartikel (refereegranskat)abstract
- This work describes the chemical, mechanical and antibacterial properties of a novel silver nanocluster/silica composite coating, obtained by sputtering, on textiles for use in nuclear bacteriological and chemical (NBC) protection suites and for aerospace applications.The properties of the coated textiles were analyzed in terms of surface morphology, silver concentration and silver release in artificial sweat and synthetic tap water, respectively. No release of silver nanoparticles was observed at given conditions.The water repellency, permeability, flammability and mechanical resistance of the textiles before and after sputtering demonstrated that the textile properties were not negatively affected by the coating.The antibacterial effect was evaluated at different experimental conditions using a standard bacterial strain of Staphylococcus aureus and compared with the behavior of uncoated textiles.The coating process conferred all textiles a good antibacterial activity. Optimal deposition conditions were elaborated to obtain sufficient antibacterial action without altering the aesthetical appearance of the textiles.The antibacterial coating retained its antibacterial activity after one cycle in a washing machine only for the Nylon based textile.
|
|
| 2. |
- Ferraris, M., et al.
(författare)
-
Antibacterial silver nanocluster/silica composite coatings on stainless steel
- 2017
-
Ingår i: Applied Surface Science. - : Elsevier. - 0169-4332 .- 1873-5584. ; 396, s. 1546-1555
-
Tidskriftsartikel (refereegranskat)abstract
- A coating made of silver nanocluster/silica composites has been deposited, via a radio frequency (RF) co-sputtering technique, for the first time onto stainless steel (AISI 304L) with the aim to improve its antibacterial properties. Different thermal treatments after coating deposition have been applied in order to optimize the coating adhesion, cohesion and its antibacterial properties. Its applicability has been investigated at realistic conditions in a cheese production plant. The physico-chemical characteristics of the coatings have been analyzed by means of different bulk and surface analytical techniques. Field emission scanning electron microscopy (FESEM), X-ray Photoelectron Spectroscopy (XPS), contact angle measurements and atomic force microscopy (AFM) were employed to assess coating morphology, composition, surface roughness, wetting properties, size and local distribution of the nanoparticles within the coating. Tape tests were used to determine the adhesion/cohesion properties of the coating. The amount and time-dependence of released silver in solutions of acetic acid, artificial water, artificial tap water and artificial milk were determined by means of Atomic Absorption Spectroscopy (AAS). The antibacterial effect of the coating was evaluated at different experimental conditions using a standard bacterial strain of Staphylococcus aureus in compliance with National Committee for Clinical Laboratory Standards (NCCLS) and AATCC 147 standards. The Ahearn test was performed to measure the adhesion of bacteria to the coated stainless steel surface compared with a control surface. The antibacterial coating retained its antibacterial activity after thermal treatment up to 450 °C and after soaking in common cleaning products for stainless steel surfaces used for e.g. food applications. The antibacterial capacity of the coating remained at high levels for 1-5 days, and showed a good capacity to reduce the adhesion of bacteria up to 30 days. Only a few percent of silver in the coating was released into acetic acid, even after 10 days of exposure at 40 °C. Most silver (> 90%) remained also in the coating even after 240 h of continuous exposure. Similar observations were made after repeated exposure at 100 °C. Very low levels of released silver in solution were observed in artificial milk. No release of silver nanoparticles was observed either in synthetic tap water or in artificial milk at given conditions. The coating further displayed good antibacterial properties also when tested during working conditions in a cheese production plant.
|
|
| 3. |
- Ferraris, Sara, et al.
(författare)
-
Interactions Between the Physiological Environment and Titanium-Based Implant Materials: From Understanding to Control
- 2022
-
Ingår i: Nanoscale Engineering of Biomaterials. - Singapore : Springer Nature. ; , s. 3-26
-
Bokkapitel (övrigt vetenskapligt/konstnärligt)abstract
- Titanium and titanium alloys are widely used in different biomedical applications owing to their high biocompatibility, high corrosion resistance, good mechanical properties, and good osseointegration ability. Titanium and its alloys rapidly form a surface oxide layer in air and aqueous environments. This passive and thin (a few nanometers) surface oxide hinders active corrosion and ensures a low metal ion release, enhancing biocompatibility. Compared to that of other biomedical alloys, this surface oxide is exceptionally resistant to chemical attack by halides, primarily chlorides; the presence of fluorides can, in some cases, result in localized corrosion of titanium and its alloys. However, the combination of proteins, inflammatory conditions and bacteria, which for instance generate hydrogen peroxide, can result in a reduction of the corrosion resistance of titanium-based materials. Titanium and its alloying elements, such as aluminum and vanadium, can then be released as ions, which might trigger an immune system response and reduce biocompatibility. Several surface modifications have been proposed in order to improve the bone-bonding ability of titanium and its alloys, facilitate the healing process, and enhance the success of the implant with a decreased risk of micromotions. Moreover, antimicrobial ions/nanoparticles can be added to the surface to reduce the infection risk. Surface modification of titanium (e.g., with artificially grown, micrometer-thick, titanium oxide layers) can significantly increase the corrosion resistance under critical conditions (e.g., inflammatory response and infection); however, the surfaces are not completely inert and the effect of metal ion/nanoparticle release should be carefully taken into account. This chapter reviews and discusses the current strategies for modifying and controlling the surface of titanium-based implant materials, with particular focus on corrosion resistance, bone integration, inflammatory and infection control, and interactions with the physiological environment.
|
|
| 4. |
- Hedberg, Yolanda, Docent, 1985-, et al.
(författare)
-
Surface modified Ti6Al4V for enhanced bone bonding ability - Effects of silver and corrosivity at simulated physiological conditions from a corrosion and metal release perspective
- 2020
-
Ingår i: Corrosion Science. - : Elsevier. - 0010-938X .- 1879-0496. ; 168
-
Tidskriftsartikel (refereegranskat)abstract
- Different surface treatments, with and without silver (Ag), of a Ti6Al4V alloy for increased bone bonding ability were investigated and compared with non-treated surfaces. Studies were conducted at 37 degrees C in phosphate buffered saline (PBS, pH 7.4) of varying hydrogen peroxide (H2O2) and bovine serum albumin (BSA) concentrations. Increased levels of metal release and corrosion were observed in the presence of both H2O2 and BSA due to complexation with Ti and Al in the surface oxide, respectively. Ag release was enhanced by the presence of BSA. Galvanic effects by Ag were minor, but possibly observed in the most corrosive environment.
|
|