- Hirschauer, B., et al.
(författare)
-
Large area synthesis of thin alumina films by laser ablation
- 1996
-
Ingår i: Applied Surface Science. - 0169-4332 .- 1873-5584. ; 99:4, s. 285-291
-
Tidskriftsartikel (refereegranskat)abstract
- Al2O3 has been ablated on commercially available 3″ silicon wafers at different distances between the target and the substrate and laser fluencies. ‘Amorphous' Al2O3 (γ-alumina with grain size <20 nm) was grown by pulsed laser deposition at room temperature. The structure, the morphology, the profile and the composition of the produced films have been investigated. Fully oxidised thin films (thickness ≤5 μm) with high uniformity and smoothness were synthesised without additional oxygen gas during the ablation. The quality of the films was independent of the ablation fluency and of the distance between target and substrate.
|
|
| 4. |
|
|
| 5. |
- Qvarford, M., et al.
(författare)
-
Polarisation-dependent X-ray absorption in high- and low-Tc Bi2Sr2Can-1CunO4+2n superconductors
- 1993
-
Ingår i: Physica C: Superconductivity and its Applications. - : Elsevier BV. - 0921-4534. ; 214:1-2, s. 119-126
-
Tidskriftsartikel (refereegranskat)abstract
- Taking advantage of the linear polarisation of synchrotron radiation, the polarisation dependence of the O K and Cu L3 X-ray absorption edges has been compared for in situ cleaved Bi2Sr2CaCu2O8 and Bi2Sr2CuO6 single crystals. The X-ray absorption spectra were measured by means of total electron yield detection. The spectra show for both crystals that the lowest unoccupied Cu 3d and O 2p orbitals are dominantly oriented parallel to the a-b plane, but also the presence of a small amount of unoccupied orbitals oriented perpendicular to the a-b plane can be deduced from both the O K and Cu L3 absorption spectra. A shift of the order of 0.5 eV between absorption into the in-plane and the out-of-plane Cu 3d orbitals was measured for the Bi2Sr2CaCu2O8 crystal, but no such shift was found for the Bi2Sr2CuO6 crystal.
|
|
| 6. |
- Söderholm, S, et al.
(författare)
-
A photoemission spectroscopy and X-ray absorption study of Bi(2)Sr(2)CaCu(2)O(8) single crystal with adsorbed Cs: On the origin of states affected by electron doping and evidence for spatially resolved electron doping
- 1996
-
Ingår i: Journal of Physics: Condensed Matter. - : IOP Publishing. - 1361-648X .- 0953-8984. ; 8, s. 1307-1320
-
Tidskriftsartikel (refereegranskat)abstract
- The influence of electron doping, via deposition of small amounts of Cs, on the electronic structure of has been studied by high-resolution photoelectron spectroscopy (PES) and x-ray absorption spectroscopy (XAS), utilizing synchrotron radiation. The changes in the electronic structure were monitored by PES of the valence band and of the O 1s, Bi 4f, Bi 5d, Ca 2p and Sr 3d core levels, and by XAS at the O 1s, Cu 2p and Ca 2p edges. The experimental data suggest that the loss of the Fermi edge and the loss of spectral intensity down to about 2 eV below the Fermi level, and the substantial loss of spectral intensity of the pre-edge structure in the O 1s XAS spectrum are mainly due to annihilation of states with O 2p character in the Cu - O layer. It is evident from bulk- and surface-sensitive XAS spectra that the electron doping by Cs affects the electronic structure more strongly close to the surface. This implies that the doping occurs locally and that the charge transfer between the different layers in the unit cell is not uniform. Thus it seems possible to alter the electronic properties of locally through spatially resolved electron doping. When larger amounts of Cs are deposited, a chemical reaction occurs which causes a disruption of the Bi - O layer. This deposition regime is characterized by the presence of caesium oxide and reduced (metallic) Bi.
|
|
| 7. |
|
|
| 8. |
- Göthelid, M., et al.
(författare)
-
Adatom and rest-atom contributions in Ge(111)c(2×8) and Ge(111)-Sn(7×7) core-level spectra
- 1993
-
Ingår i: Physical Review B. - 0163-1829. ; 48:3, s. 2012-2015
-
Tidskriftsartikel (refereegranskat)abstract
- We have identified the adatom contribution in the Ge 3d core-level spectra from the clean Ge(111)c(2×8) surface, shifted 0.17 eV to higher binding energy compared to the bulk. This adatom component vanishes in the Ge(111)-Sn(7×7) surface core-level spectra where Sn occupies the adatom site. Moreover we report the observation of an earlier proposed difference between the rest atoms in the c(2×8) structure, and also a shift to lower binding energy for the rest atoms in both structures studied. © 1993 The American Physical Society.
|
|
| 9. |
- Göthelid, M., et al.
(författare)
-
Sn-induced surface reconstructions on the Ge(111) surface studied with scanning tunneling microscopy
- 1992
-
Ingår i: Surface Science. - 0039-6028. ; 271:3, s. L357-L361
-
Tidskriftsartikel (refereegranskat)abstract
- Scanning tunneling microscopy (STM) has been used to study different Sn induced reconstructions on the Ge(111) surface; namely the (7 × 7), (5 × 5) and ( 3 × 3) R30° structures. The first two have been confirmed to be of the dimer adatom stacking faults (DAS) type with adatoms mainly being Sn. The ( 3 × 3)R30° superstructure was found at different Sn depositions. At 0.4 monolayer (ML) Sn coverage a homogeneous Sn adatom layer is adsorbed on the(1 × 1) surface in threefold sites directly over second-layer atoms (T4), while at low coverage, 0.1 ML, the top layer is a mixture of Sn and Ge atoms. We also propose the chemical identities of the different atoms seen in the STM images as related to their apparent height. © 1992.
|
|
| 10. |
- Hammar, M., et al.
(författare)
-
Initial growth of silver on Ge(111) studied by scanning tunneling microscopy
- 1993
-
Ingår i: Physical Review B. - 0163-1829. ; 47:23, s. 15669-15674
-
Tidskriftsartikel (refereegranskat)abstract
- Scanning tunneling microscopy (STM) has been used to study the Ge(111) surface after submonolayer depositions of Ag. At the lowest coverages a (4×4) reconstruction, with small insets of a (3×1) edge structure, is observed. Based on the STM images we propose a mixed Ag and Ge adatom structure for the (4×4) reconstruction, in which the adatoms have local (1×1) and (2×2) arrangements corresponding to a Ag coverage of 6/16 monolayers. The (3×1) structure appears to have a configuration similar to the Si(111)/Ag-(3×1) reconstruction, although in this case it has a much more limited extension, restricted to a few unit cells in the near vicinity of step edges and phase boundaries. At higher coverages, after the completion of a full (4×4)/(3×1) surface, a (3 × 3) R30°structure appears showing STM images similar to those previously published for the Si(111)/Ag system. © 1993 The American Physical Society.
|
|