| 1. |
- Folkenant, Matilda, et al.
(författare)
-
Structure and properties of Cr–C/Ag films deposited by magnetron sputtering
- 2015
-
Ingår i: Surface & Coatings Technology. - : Elsevier. - 0257-8972 .- 1879-3347. ; 281, s. 184-192
-
Tidskriftsartikel (refereegranskat)abstract
- Cr–C/Ag thin films with 0–14 at.% Ag have been deposited by magnetron sputtering from elemental targets. The samples were analyzed by X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) to study their structure and chemical bonding. A complex nanocomposite structure consisting of three phases; nanocrystalline Ag, amorphous CrCx and amorphous carbon is reported. The carbon content in the amorphous carbide phase was determined to be 32–33 at.% C, independent of Ag content. Furthermore, SEM and XPS results showed higher amounts of Ag on the surface compared to the bulk. The hardness and Young's modulus were reduced from 12 to 8 GPa and from 270 to 170 GPa, respectively, with increasing Ag content. The contact resistance was found to decrease with Ag addition, with the most Ag rich sample approaching the values of an Ag reference sample. Initial tribological tests gave friction coefficients in the range of 0.3 to 0.5, with no clear trends. Annealing tests show that the material is stable after annealing at 500 °C for 1 h, but not after annealing at 800 °C for 1 h. In combination, these results suggest that sputtered Cr–C/Ag films could be potentially applicable for electric contact applications.
|
|
| 2. |
- Folkenant, Matilda
(författare)
-
Synthesis and Characterization of Amorphous Carbide-based Thin Films
- 2015
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- In this thesis, research on synthesis, structure and characterization of amorphous carbide-based thin films is presented. Crystalline and nanocomposite carbide films can exhibit properties such as high electrical conductivity, high hardness and low friction and wear. These properties are in many cases structure-related, and thus, within this thesis a special focus is put on how the amorphous structure influences the material properties.Thin films within the Zr-Si-C and Cr-C-based systems have been synthesized by magnetron sputtering from elemental targets. For the Zr-Si-C system, completely amorphous films were obtained for silicon contents of 20 at.% or higher. Modeling of these films, as well as experimental results suggest that the films exhibit a network-type structure where the bond types influence the material properties. Higher hardness and resistivity were observed with high amounts of covalent Si-C bonds.Several studies were performed in the Cr-C-based systems. Cr-C films deposited in a wide composition range and with substrate temperatures of up to 500 °C were found to be amorphous nanocomposites, consisting of amorphous chromium carbide (a-CrCx) and amorphous carbon (a-C) phases. The carbon content in the carbidic phase was determined to about 30-35 at.% for most films. The properties of the Cr-C films were very dependent of the amount of a-C phase, and both hardness and electrical resistivity decreased with increasing a-C contents. However, electrochemical analysis showed that Cr-C films deposited at higher substrate temperature and with high carbon content exhibited very high oxidation resistance. In addition, nanocomposite films containing Ag nanoparticles within an amorphous Cr-C matrix were studied in an attempt to improve the tribological properties. No such improvements were observed but the films exhibited a better contact resistance than the corresponding binary Cr-C films. Furthermore, electrochemical analyses showed that Ag nanoparticles on the surface affected the formation of a stable passive film, which would make the Cr-C/Ag films less resilient to oxidation than the pure Cr-C films.
|
|
| 3. |
- Geng, Xinjian, et al.
(författare)
-
Direct Plasmonic Solar Cell Efficiency Dependence on Spiro-OMeTAD Li-TFSI Content
- 2021
-
Ingår i: Nanomaterials. - : MDPI. - 2079-4991. ; 11:12
-
Tidskriftsartikel (refereegranskat)abstract
- The proliferation of the internet of things (IoT) and other low-power devices demands the development of energy harvesting solutions to alleviate IoT hardware dependence on single-use batteries, making their deployment more sustainable. The propagation of energy harvesting solutions is strongly associated with technical performance, cost and aesthetics, with the latter often being the driver of adoption. The general abundance of light in the vicinity of IoT devices under their main operation window enables the use of indoor and outdoor photovoltaics as energy harvesters. From those, highly transparent solar cells allow an increased possibility to place a sustainable power source close to the sensors without significant visual appearance. Herein, we report the effect of hole transport layer Li-TFSI dopant content on semi-transparent, direct plasmonic solar cells (DPSC) with a transparency of more than 80% in the 450-800 nm region. The findings revealed that the amount of oxidized spiro-OMeTAD (spiro(+)TFSI(-)) significantly modulates the transparency, effective conductance and conditions of device performance, with an optimal performance reached at around 33% relative concentration of Li-TFSI concerning spiro-OMeTAD. The Li-TFSI content did not affect the immediate charge extraction, as revealed by an analysis of electron-phonon lifetime. Hot electrons and holes were injected into the respective layers within 150 fs, suggesting simultaneous injection, as supported by the absence of hysteresis in the I-V curves. The spiro-OMeTAD layer reduces the Au nanoparticles' reflection/backscattering, which improves the overall cell transparency. The results show that the system can be made highly transparent by precise tuning of the doping level of the spiro-OMeTAD layer with retained plasmonics, large optical cross-sections and the ultrathin nature of the devices.
|
|
| 4. |
|
|
| 5. |
- Nygren, Kristian, et al.
(författare)
-
The influence of nanoeffects on the oxidation of magnetron sputtered Cr-C/Ag thin films containing silver nanoparticles
- 2017
-
Ingår i: ChemElectroChem. - : Wiley. - 2196-0216. ; 4:2, s. 418-429
-
Tidskriftsartikel (refereegranskat)abstract
- Well-controlled functionalization of carbide-based nanocomposite films with noble-metal surface nanoparticles of different sizes may lead to new materials with novel multifunctional properties. In this work, magnetron sputtering was used to deposit nanocomposite films comprising amorphous chromium carbide (a-CrCx), amorphous carbon (a-C), and a minority of silver in the form of embedded nanoclusters. Up to 510(10) surface nanoparticles per cm(2) with different size distributions were also found to be formed, owing to the diffusion of silver from the bulk of the film. The influences of these conductive nanoparticles on the electrochemical behavior of the films were investigated in dilute sulfuric acid. Although silver is a noble metal, the oxidation potential of the nanoparticles was about 0.4V more negative than the Ag+/Ag standard potential, meaning that the nanoparticles were oxidized in the Cr passive potential region. While this effect can mainly be explained by a low concentration of Ag+ in the electrolyte, the sizes of the nanoparticles and interactions with the matrix were also found to be important. Scanning electron microscopy and X-ray photoelectron spectroscopy were used to analyze the surface chemistries. As Ag can be replaced by other noble metals, the concept is of general interest for further studies.
|
|