1. |
- Aberg, Jonas, et al.
(författare)
-
In vivo evaluation of an injectable premixed radiopaque calcium phosphate cement.
- 2011
-
Ingår i: International journal of biomaterials. - : Hindawi Limited. - 1687-8795 .- 1687-8787. ; 2011
-
Tidskriftsartikel (refereegranskat)abstract
- In this work a radiopaque premixed calcium phosphate cement (pCPC) has been developed and evaluated in vivo. Radiopacity was obtained by adding 0-40 % zirconia to the cement paste. The effects of zirconia on setting time, strength and radiopacity were evaluated. In the in vivo study a 2 by 3.5mm cylindrical defect in a rat vertebrae was filled with either the pCPC, PMMA or bone chips. Nano-SPECT CT analysis was used to monitor osteoblast activity during bone regeneration. The study showed that by adding zirconia to the cement the setting time becomes longer and the compressive strength is reduced. All materials evaluated in the in vivo study filled the bone defect and there was a strong osteoblast activity at the injury site. In spite of the osteoblast activity, PMMA blocked bone healing and the bone chips group showed minimal new bone formation. At 12 weeks the pCPC was partially resorbed and replaced by new bone with good bone ingrowth. The radiopaque pCPC may be considered to be used for minimal invasive treatment of vertebral fractures since it has good handling, radiopacity and allows healing of cancellous bone in parallel with the resorption of the cement.
|
|
2. |
- Hulsart-Billström, Gry, et al.
(författare)
-
Osteogenic potential of Sr-doped calcium phosphate hollow spheres in vitro and in vivo
- 2013
-
Ingår i: Journal of Biomedical Materials Research. Part A. - : Wiley. - 1549-3296 .- 1552-4965. ; 101:8, s. 2322-2331
-
Tidskriftsartikel (refereegranskat)abstract
- Treatment of osteoporotic fractures with conventional surgical methods is associated with a high rate of complications. Intense search for new treatment options includes development of specific biomaterials aimed to be part of the surgical armamentarium. Strontium doped calcium phosphate spheres (SrCPS) is a new material that might be of interest due to the influence on osteoclast and osteoblast activity. In the present study, we successfully constructed hollow spherical SrCPS particles with a diameter of ∼700 nm and shell thickness of ∼150 nm. The Sr content was about 20 wt %. Cell viability and cytotoxicity were investigated in vitro with concentrations from 0 to 1000 μg/mL of SrCPS in medium extract in a day chase study. The in vivo biocompatibility was tested in a delayed bone-healing model in a rat vertebral defect by histology, μCT, and nanoSPECT. The SrCPS showed no toxicity in vitro with comparable cell number in all concentrations. Increased metabolism was seen in the cell viability study in cells exposed to 400 and 600 μg/mL. SPECT showed good biocompatibility with no local adverse effects and an increased osteoblast activity as compared to adjacent vertebra. SrCPS implantation induced bone formation and resulted in complete resorption and defect consolidation.
|
|