  • Biendicho, J. J., et al. (författare)
  • Synthesis and characterization of perovskite-type Sr(x)Y1-xFeO(3-delta) (0.63 <= x < 1.0) and Sr0.75Y0.25Fe1-yMyO3-delta (M=Cr, Mn, Ni), (y=0.2, 0.33, 0.5)
  • 2013
  • Ingår i: Journal of Solid State Chemistry. - : Elsevier BV. - 0022-4596 .- 1095-726X. ; 200, s. 30-38
  • Tidskriftsartikel (refereegranskat)abstract
    • Oxygen-deficient ferrates with the cubic perovskite structure SrxY1-xFeO3-delta were prepared in air (0.71 <= x <= 0.91) as well as in N-2 (x=0.75 and 0.79) at 1573 K. The oxygen content of the compounds prepared in air increases with increasing strontium content from 3-delta=2.79(2) for x=0.75 to 3-delta=2.83(2) for x=0.91. Refinement of the crystal structure of Sr0.25Y0.25FeO2.29 using TOP neutron powder diffraction (NPD) data shows high anisotropic atomic displacement parameter (ADP) for the oxygen atom resulting from a substantial cation and anion disorder. Electron diffraction (ED) and highresolution electron microscopy (HREM) studies of Sr0.75Y0.25FeO2.79 reveal a modulation along (1 0 0)(p) with G +/- similar to 0.4(1 0 0)(p) indicating a local ordering of oxygen vacancies. Magnetic susceptibility measurements at 5-390 K show spin-glass behaviour with dominating antiferromagnetic coupling between the magnetic moments of Fe cations. Among the studied compositions, Sr0.75Y0.25Fe02.79 shows the lowest thermal expansion coefficient (TEC) of 10.5 ppm/K in air at 298-673 K. At 773-1173 K TEC increases up to 17.2 ppm/K due to substantial reduction of oxygen content. The latter also results in a dramatic decrease of the electrical conductivity in air above 673 K. Partial substitution of Fe by Cr, Mn and Ni according to the formula Sr0.75Y0.25Fe1-yMyO3-delta (y=0.2, 0.33, 0.5) leads to cubic perovskites for all substituents with y=0.2. Their TECs are higher in comparison with un-doped Sr0.75Y0.25Fe02.79. Only M=Ni has increased electrical conductivity compared to un-doped Sr0.75Y0.25Fe02.79. 
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-2 av 2

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy