Ultrastrong translucent glass ceramic with nanocrystalline, biomimetic structure
- 2018
-
Ingår i: Nano letters (Print). - : American Chemical Society (ACS). - 1530-6984 .- 1530-6992. ; 18:11, s. 7146-7154
-
Tidskriftsartikel (refereegranskat)abstract
- Transparent/translucent glass ceramics (GCs) have broad applications in biomedicine, armor, energy, and constructions. However, GCs with improved optical properties typically suffer from impaired mechanical properties, compared to traditional sintered full-ceramics. We present a method of obtaining high-strength, translucent GCs by preparing ZrO2-SiO2 nanocrystalline glass ceramics (NCGCs), with a microstructure of monocrystalline ZrO2 nanoparticles (NPs), embedded in an amorphous SiO2 matrix. The ZrO2-SiO2 NCGC with a composition of 65%ZrO2-35%SiO2 (molar ratio, 65Zr) achieved an average flexural strength of 1 GPa. This is one of the highest flexural strength values ever reported for GCs. ZrO2 NPs have a core-shell structure, and the shell is a thin (2–3 nm) amorphous Zr/Si interfacial layer that provides strong bonding between the ZrO2 NPs and SiO2 matrix. The diffusion of Si atoms into the ZrO2 NPs forms a Zr-O-Si superlattice. Electron tomography results show that some of the ZrO2 NPs are connected in one direction, forming in situ ZrO2 nanofibers (with length of ~500 nm), and that the ZrO2 nanofibers are stacked in an ordered way in all three dimensions. The nano-architecture of the ZrO2 nanofibers mimics the architecture of mineralized collagen fibril in cortical bone. Strong interface bonding enables efficient load transfer from the SiO2 matrix to the 3D nano-architecture built by ZrO2 nanofibers and NPs, and the 3D nano-architecture carries the majority of the external load. These two factors synergistically contribute to the high strength of the 65Zr NCGC. This study deepens our fundamental understanding of the microstructure-mechanical strength relationship, which could guide the design and manufacture of other high-strength, translucent GCs.
|
|