- Ansari, Farhan, et al.
(författare)
-
Cellulose nanofiber network for moisture stable, strong and ductile biocomposites and increased epoxy curing rate
- 2014
-
Ingår i: Composites. Part A, Applied science and manufacturing. - : Elsevier BV. - 1359-835X .- 1878-5840. ; 63, s. 35-44
-
Tidskriftsartikel (refereegranskat)abstract
- Nanocomposites with high volume fractions (15-50 vol%) of nanofibrillated cellulose (NFC) were prepared by impregnation of a wet porous NFC network with acetone/epoxy/amine solution. Infrared spectroscopy studies revealed a significant increase in curing rate of epoxy (EP) in the presence of NFC. The NFC provided extremely efficient reinforcement (at 15 vol%: 3-fold increase in stiffness and strength to 5.9 GPa and 109 MPa, respectively), and ductility was preserved. Besides, the glass transition temperature increased with increasing NFC content (from 68 degrees C in neat epoxy to 86 degrees C in 50 vol% composite). Most interestingly, the moisture sorption values were low and even comparable to neat epoxy for the 15 vol% NFC/EP. This material did not change mechanical properties at increased relative humidity (90% RH). Thus, NFC/EP provides a unique combination of high strength, modulus, ductility, and moisture stability for a cellulose-based biocomposite. Effects from nanostructural and interfacial tailoring are discussed.
|
|
| 3. |
|
|
| 4. |
|
|
| 5. |
- Borodulina, Svetlana, et al.
(författare)
-
Stress-strain curve of paper revisited
- 2012
-
Ingår i: Nordic Pulp & Paper Research Journal. - 0283-2631 .- 2000-0669. ; 27:2, s. 318-328
-
Tidskriftsartikel (refereegranskat)abstract
- We have investigated a relation between micromechanical processes and the stress-strain curve of a dry fiber network during tensile loading. By using a detailed particle-level simulation tool we investigate, among other things, the impact of "non-traditional" bonding parameters, such as compliance of bonding regions, work of separation and the actual number of effective bonds. This is probably the first three-dimensional model which is capable of simulating the fracture process of paper accounting for nonlinearities at the fiber level and bond failures. The failure behavior of the network considered in the study could be changed significantly by relatively small changes in bond strength, as compared to the scatter in bonding data found in the literature. We have identified that compliance of the bonding regions has a significant impact on network strength. By comparing networks with weak and strong bonds, we concluded that large local strains are the precursors of bond failures and not the other way around.
|
|
| 6. |
|
|
| 7. |
- Galland, Sylvain, 1987-, et al.
(författare)
-
Cellulose nanofibers decorated with magnetic nanoparticles : synthesis, structure and use in magnetized high toughness membranes for a prototype loudspeaker
- 2013
-
Ingår i: Journal of Materials Chemistry C. - 2050-7526. ; 1:47, s. 7963-7972
-
Tidskriftsartikel (refereegranskat)abstract
- Magnetic nanoparticles are the functional component for magnetic membranes, but they are difficult to disperse and process into tough membranes. Here, cellulose nanofibers are decorated with magnetic ferrite nanoparticles formed in situ which ensures a uniform particle distribution, thereby avoiding the traditional mixing stage with the potential risk of particle agglomeration. The attachment of the particles to the nanofibrils is achieved via aqueous in situ hydrolysis of metal precursors onto the fibrils at temperatures below 100 °C. Metal adsorption and precursor quantification were carried out using Induction Coupled Plasma-Optical Emission Spectroscopy (ICP-OES). FE-SEM was used for high resolution characterization of the decorated nanofibers and hybrid membranes, and TEM was used for nanoparticle size distribution studies. The decorated nanofibers form a hydrocolloid. Large (200 mm diameter) hybrid cellulose/ferrite membranes were prepared by simple filtration and drying of the colloidal suspension. The low-density, flexible and permanently magnetized membranes contain as much as 60 wt% uniformly dispersed nanoparticles (thermogravimetric analysis data). Hysteresis magnetization was measured by a Vibrating Sample Magnetometer; the inorganic phase was characterized by XRD. Membrane mechanical properties were measured in uniaxial tension. An ultrathin prototype loudspeaker was made and its acoustic performance in terms of output sound pressure was characterized. A full spectrum of audible frequencies was resolved.
|
|
| 8. |
|
|
| 9. |
|
|
| 10. |
- Galland, Sylvain, 1987-
(författare)
-
Compression-moulded and multifunctional cellulose network materials
- 2013
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Cellulose-based materials are widely used in a number of important applications (e.g. paper, wood, textiles). Additional developments are suggested by the growing interest for natural fibre-based composite and nanocomposite materials. The motivation is not only in the economic and ecological benefits, but is also related to advantageous properties and characteristics. The objective of this thesis is to provide a better understanding of process-structure-property relationships in some novel cellulose network materials with advanced functionalities, and showing potential large-scale processability. An important result is the favourable combination of mechanical properties observed for network-based cellulose materials.Compression-moulding of cellulose pulp fibres under high pressure (45 MPa) and elevated temperature (120 – 180 oC) provides an environmentally friendly process for preparation of stiff and strong cellulose composite plates. The structure of these materials is characterized at multiple scales (molecular, supra-molecular and microscale). These observations are related to measured reduction in water retention ability and improvement in mechanical properties.In a second part, cellulose nanofibrils (NFC) are functionalized with in-situ precipitated magnetic nanoparticles and formed into dense nanocomposite materials with high inorganic content. The precipitation conditions influence particle size distributions, which in turn affect the magnetic properties of the material. Besides, the decorated NFC network provides high stiffness, strength and toughness to materials with very high nanoparticle loading (up to 50 vol.%).Subsequently, a method for impregnation of wet NFC network templates with a thermosetting epoxy resin is developed, enabling the preparation of well-dispersed epoxy-NFC nanocomposites with high ductility and moisture durable mechanical properties. Furthermore, cellulose fibrils interact positively with the epoxy during curing (covalent bond formation and accelerated curing). Potential large scale development of epoxy-NFC and magnetic nanocomposites is further demonstrated with the manufacturing of 3D shaped compression-moulded objects.Finally, the wet impregnation route developed for epoxy is adapted to prepare UV-curable NFC nanocomposite films with a hyperbranched polymer matrix. Different chemical modifications are applied to the NFC in order to obtain moisture durable oxygen barrier properties.
|
|