| 1. |
- Hagleitner, Daniel R., et al.
(författare)
-
Bulk and surface characterization of In2O3(001) single crystals
- 2012
-
Ingår i: Physical Review B (Condensed Matter and Materials Physics). - 1098-0121. ; 85:11
-
Tidskriftsartikel (refereegranskat)abstract
- A comprehensive bulk and surface investigation of high-quality In2O3(001) single crystals is reported. The transparent-yellow, cube-shaped single crystals were grown using the flux method. Inductively coupled plasma mass spectrometry (ICP-MS) reveals small residues of Pb, Mg, and Pt in the crystals. Four-point-probe measurements show a resistivity of 2.0 +/- 0.5 x 10(5) Omega cm, which translates into a carrier concentration of approximate to 10(12) cm(-3). The results from x-ray diffraction (XRD) measurements revise the lattice constant to 10.1150(5) angstrom from the previously accepted value of 10.117 angstrom. Scanning tunneling microscopy (STM) images of a reduced (sputtered/annealed) and oxidized (exposure to atomic oxygen at 300 degrees C) surface show a step height of 5 angstrom, which indicates a preference for one type of surface termination. The surfaces stay flat without any evidence for macroscopic faceting under any of these preparation conditions. A combination of low-energy ion scattering (LEIS) and atomically resolved STM indicates an indium-terminated surface with small islands of 2.5 angstrom height under reducing conditions, with a surface structure corresponding to a strongly distorted indium lattice. Scanning tunneling spectroscopy (STS) reveals a pronounced surface state at the Fermi level (E-F). Photoelectron spectroscopy (PES) shows additional, deep-lying band gap states, which can be removed by exposure of the surface to atomic oxygen. Oxidation also results in a shoulder at the O 1s core level at a higher binding energy, possibly indicative of a surface peroxide species. A downward band bending of 0.4 eV is observed for the reduced surface, while the band bending of the oxidized surface is of the order of 0.1 eV or less.
|
|