| 1. |
- Hieulle, Jeremy, et al.
(författare)
-
Understanding and decoupling the role of wavelength and defects in light-induced degradation of metal-halide perovskites
- 2024
-
Ingår i: Energy & Environmental Science. - : Royal Society of Chemistry. - 1754-5692 .- 1754-5706. ; 17:1, s. 284-295
-
Tidskriftsartikel (refereegranskat)abstract
- Light-induced degradation in metal halide perovskites is a major concern that can potentially hamper the commercialization of perovskite optoelectronic devices. The phenomena viz. ion migration, phase segregation, and defect intolerance are believed to be the factors behind the degradation. However, a detailed mechanistic understanding of how and why light reduces the long-term stability of perovskites is still lacking. Here, by combining multiscale characterization techniques and computational studies, we uncover the role of white light in the surface degradation of state-of-the-art FAPbI3-rich perovskite absorbers (reaching up to 22% PCE in solar cells). We unravel the degradation kinetics and found that white light triggers the chemical degradation of perovskite into secondary phases with higher work function and metallic I–V characteristics. Furthermore, we demonstrate that perovskite degradation is triggered by a combined mechanism involving both light and the presence of defects. We employ surface passivation to understand the role of defect intolerance in the degradation process. Moreover, by using filtered light we uncover the wavelength dependency of the light-induced perovskite degradation. Based on our findings, we infer some strategies for material engineering and device design that can expedite the path toward stable perovskite optoelectronic devices.
|
|
| 2. |
- Krishna, Anurag, et al.
(författare)
-
Mitigating the Heterointerface Driven Instability in Perovskite Photovoltaics
- 2023
-
Ingår i: ACS Energy Letters. - : American Chemical Society (ACS). - 2380-8195. ; 8:8, s. 3604-3613
-
Tidskriftsartikel (refereegranskat)abstract
- Metal halide perovskites have thepotential to revolutionizethefield of photovoltaics, though limited stability has impeded commercialexploitation. The soft heterointerface between the perovskite andcharge-transporting layer is one of the major bottlenecks that limitsoperational stability. Here, we present rationally designed molecularmodulators that synergistically improve the stability of the & alpha;-FAPbI(3)-based perovskite solar cells while retaining power conversionefficiency (PCE) of 24.0% with a high open-circuit voltage (V (OC)) of & SIM;1.195 V. The interfacially modifiedphotovoltaic cells exhibit high operational stability, whereby thechampion device retains & SIM;88% of initial performance after 2000h of maximum power point tracking at 40 & DEG;C and 1 sun illumination.The molecular origins of such enhanced stability and device performanceare corroborated by multiscale characterization techniques and modeling,providing insights into the origins of performance and stability enhancements.
|
|