| 1. |
- Elhag, Sami, et al.
(författare)
-
Low-temperature growth of polyethylene glycol-doped BiZn2VO6 nanocompounds with enhanced photoelectrochemical properties
- 2017
-
Ingår i: Journal of Materials Chemistry A. - Cambridge : Royal Society of Chemistry. - 2050-7488. ; 5:3, s. 1112-1119
-
Tidskriftsartikel (refereegranskat)abstract
- We demonstrate scalable, low-cost and low-temperature (<100 °C) aqueous chemical growth of bismuth–zinc vanadate (BiZn2VO6) nanocompounds by BiVO4 growth on ZnO nanobelts (NBs). The nanocompounds were further doped with polyethylene glycol (PEG) to tune the electronic structure of the materials, as a means to lower the charge carrier recombination rate. The chemical composition, morphology, and detailed nanostructure of the BiZn2VO6 nanocompounds were characterized. They exhibit rice-like morphology, are highly dense on the substrate and possess a good crystalline quality. Photoelectrochemical characterization in 0.1 M lithium perchlorate in carbonate propylene shows that BiZn2VO6 nanocompounds are highly suitable as anodes for solar-driven photoelectrochemical applications, providing significantly better performance than with only ZnO NBs. This performance could be attributed to the heterogeneous catalysis effect at nanocompound and ZnO NB interfaces, which have enhanced the electron transfer process on the electrode surface. Furthermore, the charge collection efficiency could be significantly improved through PEG doping of nanocompounds. The photocurrent density of PEG-doped BiZn2VO6 nanocompounds reached values of 2 mA cm−2 at 1.23 V (vs. Ag/AgCl), over 60% larger than that of undoped BiZn2VO6 nanocompounds. Photoluminescence emission experiments confirmed that PEG plays a crucial role in lowering the charge carrier recombination rate. The presented BiZn2VO6 nanocompounds are shown to provide highly competitive performance compared with other state-of-the art photoelectrodes.
|
|
| 2. |
|
|
| 3. |
- Abbasi, Mazhar Ali, et al.
(författare)
-
Decoration of ZnO nanorods with coral reefs like NiO nanostructures by the hydrothermal growth method and their luminescence study
- 2014
-
Ingår i: Materials. - : MDPI. - 1996-1944. ; 7:1, s. 430-440
-
Tidskriftsartikel (refereegranskat)abstract
- Composite nanostructures of coral reefs like p-type NiO on n-type ZnO nanorods have been decorate on fluorine-doped tin oxide glass substrates by the hydrothermal growth. Structural characterization was performed by field emission scanning electron microscopy, high-resolution transmission electron microscopy and X-ray diffraction techniques. This investigation has shown that the adopted synthesis has led to high crystalline quality nanostructures. Morphological study shows that the coral reefs like nanostructures are densely packed on the ZnO nanorods. Cathodoluminescence (CL) spectra for the synthesized composite nanostructures were dominated by a near band gap emission at 380 nm and by a broad interstitial defect related luminescence centered at ~630 nm. Spatially resolved CL images reveal that the luminescence originates mainly from the ZnO nanorods.
|
|
| 4. |
- Abrikosov, Igor, et al.
(författare)
-
Phase Stability and Elasticity of TiAlN
- 2011
-
Ingår i: Materials. - : MDPI. - 1996-1944. ; 4:9, s. 1599-1618
-
Tidskriftsartikel (refereegranskat)abstract
- We review results of recent combined theoretical and experimental studies of Ti1−xAlxN, an archetypical alloy system material for hard-coating applications. Theoretical simulations of lattice parameters, mixing enthalpies, and elastic properties are presented. Calculated phase diagrams at ambient pressure, as well as at pressure of 10 GPa, show a wide miscibility gap and broad region of compositions and temperatures where the spinodal decomposition takes place. The strong dependence of the elastic properties and sound wave anisotropy on the Al-content offers detailed understanding of the spinodal decomposition and age hardening in Ti1−xAlxN alloy films and multilayers. TiAlN/TiN multilayers can further improve the hardness and thermal stability compared to TiAlN since they offer means to influence the kinetics of the favorable spinodal decomposition and suppress the detrimental transformation to w-AlN. Here, we show that a 100 degree improvement in terms of w-AlN suppression can be achieved, which is of importance when the coating is used as a protective coating on metal cutting inserts.
|
|
| 5. |
- Alling, Björn, et al.
(författare)
-
Pressure enhancement of the isostructural cubic decomposition in Ti1−xAlxN
- 2009
-
Ingår i: Applied Physics Letters. - : AIP Publishing. - 0003-6951 .- 1077-3118. ; 95:181906
-
Tidskriftsartikel (refereegranskat)abstract
- The influence of pressure on the phase stabilities of Ti1−xAlxN solid solutions has been studied using first principles calculations. We find that the application of hydrostatic pressure enhances the tendency for isostructural decomposition, including spinodal decomposition. The effect originates in the gradual pressure stabilization of cubic AlN with respect to the wurtzite structure and an increased isostructural cubic mixing enthalpy with increased pressure. The influence is sufficiently strong in the composition-temperature interval corresponding to a shoulder of the spinodal line that it could impact the stability of the material at pressures achievable in the tool-work piece contact during cutting operations
|
|
| 6. |
- Almer, Jonathan, et al.
(författare)
-
Microstructural evolution during tempering of arc-evaporated Cr-N coatings
- 2000
-
Ingår i: Journal of Vacuum Science & Technology. A. Vacuum, Surfaces, and Films. - : American Vacuum Society. - 0734-2101 .- 1520-8559. ; 18:1, s. 121-130
-
Tidskriftsartikel (refereegranskat)abstract
- Cr-N coatings were arc-deposited at 50 and 300 V. The changes in the coating microstructure and phase content during tempering were monitored. As a result, the phase stability and activation energies for defect diffusion were determined as a function of ion energy.
|
|
| 7. |
- Amini, Shahram, et al.
(författare)
-
On the Stability of Mg Nanograins to Coarsening after Repeated Melting
- 2009
-
Ingår i: NANO LETTERS. - : American Chemical Society (ACS). - 1530-6984 .- 1530-6992. ; 9:8, s. 3082-3086
-
Tidskriftsartikel (refereegranskat)abstract
- Herein we report on the extraordinary thermal stability of similar to 35 nm Mg-nanograins that constitute the matrix of a Ti2AlC-Mg composite that has previously been shown to have excellent mechanical properties. The microstructure is so stable that heating the composite three times to 700 degrees C, which is 50 degrees C over the melting point of Mg, not only resulted in the repeated melting of the Mg, but surprisingly and within the resolution of our differential scanning calorimeter, did not lead to any coarsening. The reduction in the Mg melting point due to the nanograins was similar to 50 degrees C. X-ray diffraction and neutron spectroscopy results suggest that thin, amorphous, and/or poorly crystallized rutile, anatase, and/or magnesia layers separate the Mg nanograins and prevent them from coarsening. Clearly that layer is thin enough, and thus mechanically robust enough, to survive the melting and solidification stresses encountered during cycling. Annealing in hydrogen at 250 degrees C for 20 h, also did not seem to alter the grain size significantly.
|
|
| 8. |
- Asif, Muhammad H., et al.
(författare)
-
Growth and Structure of ZnO Nanorods on a Sub-Micrometer Glass Pipette and Their Application as Intracellular Potentiometric Selective Ion Sensors
- 2010
-
Ingår i: Materials. - : MDPI AG. - 1996-1944. ; 3, s. 4657-4667
-
Tidskriftsartikel (refereegranskat)abstract
- This paper presents the growth and structure of ZnO nanorods on a sub-micrometer glass pipette and their application as an intracellular selective ion sensor. Highly oriented, vertical and aligned ZnO nanorods were grown on the tip of a borosilicate glass capillary (0.7 μm in diameter) by the low temperature aqueous chemical growth (ACG) technique. The relatively large surface-to-volume ratio of ZnO nanorods makes them attractive for electrochemical sensing. Transmission electron microscopy studies show that ZnO nanorods are single crystals and grow along the crystal’s c-axis. The ZnO nanorods were functionalized with a polymeric membrane for selective intracellular measurements of Na +. The membrane-coated ZnO nanorods exhibited a Na+-dependent electrochemical potential difference versus an Ag/AgCl reference micro-electrode within a wide concentration range from 0.5 mM to 100 mM. The fabrication of functionalized ZnO nanorods paves the way to sense a wide range of biochemical species at the intracellular level.
|
|
| 9. |
- Bakoglidis, Konstantinos D., et al.
(författare)
-
Low-temperature growth of low friction wear-resistant amorphous carbon nitride thin films by mid-frequency, high power impulse, and direct current magnetron sputtering
- 2015
-
Ingår i: Journal of Vacuum Science & Technology. A. Vacuum, Surfaces, and Films. - : American Vacuum Society. - 0734-2101 .- 1520-8559. ; 33:5
-
Tidskriftsartikel (refereegranskat)abstract
- Amorphous carbon nitride (a-CNx) thin films were deposited on steel AISI52100 and Si(001) substrates using mid-frequency magnetron sputtering (MFMS) with an MF bias voltage, high power impulse magnetron sputtering (HiPIMS) with a synchronized HiPIMS bias voltage, and direct current magnetron sputtering (DCMS) with a DC bias voltage. The films were deposited at a low substrate temperature of 150 °C and a N2/Ar flow ratio of 0.16 at the total pressure of 400 mPa. The negative bias voltage (Vs) was varied from 20 V to 120 V in each of the three deposition modes. The microstructure of the films was characterized by high-resolution transmission electron microscopy (HRTEM) and selected area electron diffraction (SAED), while the film morphology was investigated by scanning electron microscopy (SEM). All films possessed amorphous microstructure with clearly developed columns extending throughout the entire film thickness. Layers grown with the lowest substrate bias of 20 V exhibited pronounced intercolumnar porosity, independent of the technique used. Voids closed and dense films formed at Vs ≥ 60 V, Vs ≥ 100 V and Vs = 120 V for MFMS, DCMS and HiPIMS, respectively. X-ray photoelectron spectroscopy (XPS) revealed that the nitrogen-to-carbon ratio, N/C, of the films ranged between 0.2 and 0.24. Elastic recoil detection analysis (ERDA) showed that Ar content varied between 0 and 0.8 at% and increases as a function of Vs for all deposition techniques. All films exhibited compressive residual stress, σ, which depends on the growth method; HiPIMS produces the least stressed films with stress between – 0.4 and – 1.2 GPa for all Vs values, while for CNx films deposited by MFMS σ = – 4.2 GPa. Nanoindentation showed a significant increase in film hardness and reduced elastic modulus with increasing Vs for all techniques. The harder films were produced by MFMS with hardness as high as 25 GPa. Low friction coefficients, between 0.05 and 0.06, were recorded for all films. Furthermore, CNx films produced by MFMS and DCMS at Vs = 100 V and 120 V presented a high wear resistance with wear coefficients of k ≤ 2.3 x 10-5 mm3/Nm.
|
|
| 10. |
- Beheshti, Hooshang, et al.
(författare)
-
Electronic supply chain management applications by Swedish SMEs
- 2007
-
Ingår i: Enterprise Information Systems. - : Informa UK Limited. - 1751-7575 .- 1751-7583. ; 1:2, s. 255-268
-
Tidskriftsartikel (refereegranskat)abstract
- The Internet has become an integral part of business activities of most corporations today. Electronic supply chain management (SCM) can improve the operational efficiency of the firm by streamlining processes between the company and its suppliers, business partners, and customers. This research explores the extent and the degree of Internet application in Swedish small- and medium-sized enterprises (SMEs). The analyses of the data show that the Swedish SMEs use the Internet in their supply chain activities to a large degree. The study establishes some differences between smaller and larger organizations as well as between manufacturing and service companies.
|
|