- Hanifpour, Fatemeh, et al.
(författare)
-
Investigation into the mechanism of electrochemical nitrogen reduction reaction to ammonia using niobium oxynitride thin-film catalysts
- 2022
-
Ingår i: Electrochimica Acta. - : Elsevier. - 0013-4686 .- 1873-3859. ; 403
-
Tidskriftsartikel (refereegranskat)abstract
- Niobium oxynitride (NbOxNy) thin films with varying combined non-metal vs. metal stoichiometries ( x + y ) and N/O stoichiometric ratios (y/x) are investigated for their ability to catalyze the nitrogen re-duction reaction and ammonia synthesis at ambient conditions. Electrochemical impedance spectroscopy and ammonia measurements show stark differences both in nitrogen vs. argon media on each surface and on the surfaces in the series when the combined stoichiometry of N + O vs. Nb increases. Surface stability checks at fixed intervals during the experiments and surface characterization after the experiments us -ing X-ray diffraction reveal the least changes occurred to the surface with the highest N + O stoichiometry. Based on these observations, an ammonia synthesis mechanism is proposed. Isotope labeling experiments on the most promising surface of the series, however, show no sign of catalytically produced ammonia, possibly due to the lack of stability of the surface to endure through the ammonia production cycle.
|
|
| 2. |
- Hanifpour, Fatemeh, et al.
(författare)
-
Operando quantification of ammonia produced from computationally-derived transition metal nitride electro-catalysts
- 2022
-
Ingår i: Journal of Catalysis. - : Elsevier. - 0021-9517 .- 1090-2694. ; 413, s. 956-967
-
Tidskriftsartikel (refereegranskat)abstract
- Electrochemical reduction of dinitrogen to ammonia is investigated in a micro-reactor flow-cell using thin films of VN, CrN, NbN and ZrN. Chronoamperometry loops are used for ammonia production analysis. Operando ammonia quantification is accomplished in a flow injection analyzer. Results show the effect of presence/absence of N-2(g) within both the electrochemical characterization and ammonia production for ZrN. However, no ammonia is detected from studies on CrN. VN and NbN are inactivated upon reacting their N atoms of the surface top layer(s). Results obtained from ammonia measurements, electrochemical impedance spectroscopy analysis, surface stability checks, and surface characterization using X-ray reflectivity, reveal certain trends indicating catalytic behavior for ZrN. However, the concentration of produced ammonia is below the detection limit of the methods devised to analyze the samples from isotope labeling experiments. The onset of ammonia production on ZrN appears to be in close agreement with that predicted previously by computational studies.
|
|
| 3. |
- Ingason, Arni Sigurdur, et al.
(författare)
-
A Nanolaminated Magnetic Phase: Mn2GaC
- 2014
-
Ingår i: Materials Research Letters. - : Taylor & Francis. - 2166-3831. ; 2:2, s. 89-93
-
Tidskriftsartikel (refereegranskat)abstract
- Layered magnetic materials are fascinating from the point of view of fundamental science as well as applications. Discoveries such as giant magnetoresistance (GMR) in magnetic multilayers have revolutionized data storage and magnetic recording, and concurrently initiated the search for new layered magnetic materials. One group of inherently nanolaminated compounds are the so called Mn+1AXn (MAX) phases. Due to the large number of isostructural compositions, researchers are exploring the wide range of interesting properties, and not primarily functionalization through optimization of structural quality. Magnetic MAX phases have been discussed in the literature, though this is hitherto an unreported phenomenon. However, such materials would be highly interesting, based on the attractive and useful properties attained with layered magnetic materials to date. Here we present a new MAX phase, (Cr1–xMnx)2GeC, synthesized as thin film in heteroepitaxial form, showing single crystal material with unprecedented structural MAX phase quality. The material was identified using first-principles calculations to study stability of hypothetical MAX phases, in an eort to identify a potentially magnetic material. The theory predicts a variety of magnetic behavior depending on the Mn concentration and Cr/Mn atomic conguration within the sublattice. The analyzed thin films display a magnetic signal well above room temperature and with partly ferromagnetic ordering. These very promising results open up a field of new layered magnetic materials, with high potential for electronics and spintronics applications.
|
|
| 4. |
- Ingason, Arni Sigurdur, et al.
(författare)
-
Magnetic Self-Organized Atomic Laminate from First Principles and Thin Film Synthesis
- 2013
-
Ingår i: Physical Review Letters. - : American Physical Society. - 0031-9007 .- 1079-7114. ; 110
-
Tidskriftsartikel (refereegranskat)abstract
- he first experimental realization of a magnetic Mn+1AXn (MAX) phase, (Cr0.75Mn0.25)2GeC, is presented, synthesized as a heteroepitaxial single crystal thin film, exhibiting excellent structural quality. This self-organized atomic laminate is based on the well-known Cr2GeC, with Mn, a new element in MAX phase research, substituting Cr. The compound was predicted using first-principles calculations, from which a variety of magnetic behavior is envisaged, depending on the Mn concentration and Cr/Mn atomic configuration within the sublattice. The analyzed thin films display a magnetic signal at room temperature.
|
|
| 5. |
- Leosson, K., et al.
(författare)
-
Ultra-thin gold films on transparent polymers
- 2013
-
Ingår i: Nanophotonics. - : Walter de Gruyter GmbH. - 2192-8614 .- 2192-8606. ; 2:1, s. 3-11
-
Tidskriftsartikel (refereegranskat)abstract
- Fabrication of continuous ultra-thin gold films (
|
|
| 6. |
- Magnus, F, et al.
(författare)
-
Morphology of TiN thin films grown on SiO(2) by reactive high power impulse magnetron sputtering
- 2011
-
Ingår i: Thin Solid Films. - : Elsevier. - 0040-6090 .- 1879-2731. ; 520:5, s. 1621-1624
-
Tidskriftsartikel (refereegranskat)abstract
- Thin TiN films were grown on SiO(2) by reactive high power impulse magnetron sputtering (HiPIMS) at a range of temperatures from 45 to 600 degrees C. The film properties were compared to films grown by conventional dc magnetron sputtering (dcMS) at similar conditions. Structural characterization was carried out using X-ray diffraction and reflection methods. The HiPIMS process produces denser films at lower growth temperature than does dcMS. Furthermore, the surface is much smoother for films grown by the HiPIMS process. The [200] grain size increases monotonically with increased growth temperature, whereas the size of the [111] oriented grains decreases to a minimum for a growth temperature of 400 degrees C after which it starts to increase with growth temperature. The [200] crystallites are smaller than the [111] crystallites for all growth temperatures. The grain sizes of both orientations are smaller in HiPIMS grown films than in dcMS grown films.
|
|
| 7. |
- Mockuté, Aurelija, et al.
(författare)
-
Structural and magnetic properties of (Cr1-xMnx)(5)Al-8 solid solution and structural relation to hexagonal nanolaminates
- 2014
-
Ingår i: Journal of Materials Science. - : Springer Verlag (Germany). - 0022-2461 .- 1573-4803. ; 49:20, s. 7099-7104
-
Tidskriftsartikel (refereegranskat)abstract
- Electron microscopy is used to reveal the competitive epitaxial growth of bcc structure (Cr1-x Mn (x) )(5)Al-8 and (Cr1-y Mn (y) )(2)AlC [M (n+1)AX (n) (MAX)] phase during both magnetron sputtering and arc deposition. X-ray diffraction theta-2 theta measurements display identical peak positions of (000n)-oriented MAX phase and (Cr1-x Mn (x) )(5)Al-8, due to the interplanar spacing of (Cr1-x Mn (x) )(5)Al-8 that matches exactly half a unit cell of (Cr1-y Mn (y) )(2)AlC. Vibrating sample magnetometry shows that a thin film exclusively consisting of (Cr1-x Mn (x) )(5)Al-8 exhibits a magnetic response, implying that the potential presence of this phase needs to be taken into consideration when evaluating the magnetic properties of (Cr, Mn)(2)AlC.
|
|
| 8. |
- Salikhov, Ruslan, et al.
(författare)
-
Magnetic Anisotropy in the (Cr0.5Mn0.5)(2)GaC MAX Phase
- 2015
-
Ingår i: Materials Research Letters. - : TAYLOR & FRANCIS INC. - 2166-3831. ; 3:3, s. 156-160
-
Tidskriftsartikel (refereegranskat)abstract
- Magnetic MAX phase (Cr0.5Mn0.5)(2)GaC thin films grown epitaxially on MgO(111) substrates were studied by ferromagnetic resonance at temperatures between 110 and 300 K. The spectroscopic splitting factor g = 2.00 +/- 0.01 measured at all temperatures indicates pure spin magnetism in the sample. At all temperatures we find the magnetocrystalline anisotropy energy to be negligible which is in agreement with the identified pure spin magnetism.
|
|