| 1. |
- Byon, Eungsun, et al.
(författare)
-
Electrochemical property and apatite formation of metal ion implanted titanium for medical implants
- 2005
-
Ingår i: Surface & Coatings Technology. - : Elsevier BV. - 0257-8972. ; 200:1-4, s. 1018-1021
-
Tidskriftsartikel (refereegranskat)abstract
- This work is concerned with the effects of Ca-ion implantation on the electrochemical behavior and biocompatibility of commercially pure Ti. The electrochemical behavior was tested by open-circuit potential transient and polarization experiments in Hanks' solution, and the biocompatibility was evaluated by soaking in simulated body fluid solution. The Ca-implanted Ti specimen showed more active electrochemical behavior than non-implanted specimen, and easier formation of apatite with good Ca / P ratio in the range of 1.38 and 1.60, revealing its potential as a bioactive material.
|
|
| 2. |
- Sul, Young-Taeg, 1960, et al.
(författare)
-
Biomechanical Measurements of Calcium-Incorporated Oxidized Implants in Rabbit Bone: Effect of Calcium Surface Chemistry of a Novel Implant
- 2004
-
Ingår i: Clinical Implant Dentistry and Related Research. - 1523-0899. ; 6:2, s. 101-10
-
Tidskriftsartikel (refereegranskat)abstract
- BACKGROUND: In oral implantology there has been a general trend away from machine-turned minimally rough and acid-etched and blasted implants toward intermediary roughened surfaces. Mechanical interlocking at micron resolution is claimed to be the dominant reason for the fixation of such implants in bone. However, clinical demands for stronger and faster bone bonding to the implant (eg, in immediately loaded and compromised bone cases) have motivated the development of novel surfaces capable of chemical bonding. PURPOSE: The purpose of the present study is to investigate bone tissue reactions to a newly developed calciumincorporated oxidized implant. The specific aim is to assess the effect of calcium surface chemistry on the bone response. MATERIALS AND METHODS: Calcium (Ca) ion-incorporated implants were prepared by micro arc oxidation methods. Surface oxide properties were characterized by using various surface analytic techniques involving scanning electron microscopy, x-ray diffractometry, x-ray photoelectron spectroscopy, and optical interferometry. Twenty screw-shaped commercially pure (CP) titanium implants (10 turned implants [controls] and 10 Ca-incorporated implants [tests]) were inserted in the femoral condyles of 10 New Zealand White rabbits. RESULTS: After a healing period of 6 weeks, resonance frequency analyses and removal torque measurements of the Ca-incorporated oxidized implants demonstrated statistically significant improvements of implant integration with bone in comparison to machine-turned control implants (p = 0.013 and p = 0.005, respectively). CONCLUSIONS: The Ca-reinforced surface chemistry of the oxidized implants significantly improved bone responses in a rabbit model. The present study suggests that biochemical bonding at the bone-implant interface, in combination with mechanical interlocking, may play a dominant role in the fixation of Ca-incorporated oxidized implants in bone. The observed rapid and strong integration of test Ca implants may have clinical implications for immediate or early loading and improved performance in compromised bone.
|
|
| 3. |
- Kang, Byung-Soo, et al.
(författare)
-
Metal plasma immersion ion implantation and deposition (MePIIID) on screw-shaped titanium implant: The effects of ion source, ion dose and acceleration voltage on surface chemistry and morphology.
- 2011
-
Ingår i: Medical Engineering & Physics. - : Elsevier BV. - 0951-8320 .- 1350-4533. ; 33:6, s. 730-738
-
Tidskriftsartikel (refereegranskat)abstract
- The present study investigated the effect of metal plasma immersion ion implantation and deposition (MePIIID) process parameters, i.e., plasma sources of magnesium and calcium, ion dose, and acceleration voltage on the surface chemistry and morphology of screw-type titanium implants that have been most widely used for osseointegrated implants. It is found that irrespective of plasma ion source, surface topography and roughness showed no differences at the nanometer level; that atom concentrations increased with ion dose but decreased with acceleration voltage. Data obtained from X-ray photoelectron spectroscopy and auger electron spectroscopy suggested that MePIIID process produces ‘intermixed’ layer of cathodic arc deposition and plasma immersion ion implantation. The MePIIID process may create desired bioactive surface chemistry of dental and orthopaedic implants by tailoring ion and plasma sources and thus enable investigations of the effect of the surface chemistry on bone response.
|
|
| 4. |
- Sul, Young-Taeg, 1960, et al.
(författare)
-
Characteristics of the surface oxides on turned and electrochemically oxidized pure titanium implants up to dielectric breakdown: the oxide thickness, micropore configurations, surface roughness, crystal structure and chemical composition.
- 2002
-
Ingår i: Biomaterials. - 0142-9612 .- 1878-5905. ; 23:2, s. 491-501
-
Tidskriftsartikel (refereegranskat)abstract
- Titanium implants have been used widely and successfully for various types of bone-anchored reconstructions. It is believed that properties of oxide films covering titanium implant surfaces are of crucial importance for a successful osseointegration, in particular at compromized bone sites. The aim of the present study is to investigate the surface properties of anodic oxides formed on commercially pure (c.p.) titanium screw implants as well as to study 'native' oxides on turned c.p. titanium implants. Anodic oxides were prepared by galvanostatic mode in CH3COOH up to the high forming voltage of dielectric breakdown and spark formation. The oxide thicknesses, measured with Auger electron spectroscopy (AES), were in the range of about 200-1000 nm. Barrier and porous structures dominated the surface morphology of the anodic film. Quantitative morphometric analyses of the micropore structures were performed using an image analysis system on scanning electron microscopy (SEM) negatives. The pore sizes were
|
|
| 5. |
- Sul, Young-Taeg, et al.
(författare)
-
Oxidized, bioactive implants are rapidly and strongly integrated in bone : Part 1 - experimental implants
- 2006
-
Ingår i: Clinical Oral Implants Research. - Oxford : Blackwell. - 0905-7161 .- 1600-0501. ; 17:5, s. 521-526
-
Tidskriftsartikel (refereegranskat)abstract
- Objectives: The study presented was designed to investigate the speed and the strength of osseointegration of oxidized implants at early healing times in comparison which machined, turned implants. Material and methods: Screw-shaped titanium implants were prepared and divided into two groups: magnesium ion incorporated, oxidized implants (Mg implants, n=10) and machined, turned implants (controls, n=10). Mg implants were prepared using micro-arc oxidation methods. Surface oxide properties of implants such as surface chemistry, oxide thickness, morphology/pore characteristics, crystal structures and roughness were characterized with various surface analytic techniques. Implants were inserted into the tibiae of ten New Zealand white rabbits. After a follow-up period of 3 and 6 weeks, removal torque (RTQ), osseointegration speed (ΔRTQ/Δhealing time) and integration strength of implants were measured. Bonding failure analysis of the bone-to-implant interface was performed. Results: The speed the and strength of osseointegration of Mg implants were significantly more rapid and stronger than for turned implants at follow-up periods of 3 and 6 weeks. Bonding failure for Mg implants dominantly occurred within the bone tissue, whereas bonding failure for turned implants mainly occurred at the interface between implant and bone. Conclusions: Oxidized, bioactive implants are rapidly and strongly integrated in bone. The present results indicate that the rapid and strong integration of oxidized, bioactive Mg implants to bone may encompass immediate/early loading of clinical implants.
|
|
| 6. |
- Sul, Young-Taeg, 1960, et al.
(författare)
-
Oxidized, bioactive implants are rapidly and strongly integrated in bone. Part 1--experimental implants.
- 2006
-
Ingår i: Clinical Oral Implants Research. - : Wiley. - 0905-7161 .- 1600-0501. ; 17:5, s. 521-6
-
Tidskriftsartikel (refereegranskat)abstract
- OBJECTIVES: The study presented was designed to investigate the speed and the strength of osseointegration of oxidized implants at early healing times in comparison which machined, turned implants. MATERIAL AND METHODS: Screw-shaped titanium implants were prepared and divided into two groups: magnesium ion incorporated, oxidized implants (Mg implants, n=10) and machined, turned implants (controls, n=10). Mg implants were prepared using micro-arc oxidation methods. Surface oxide properties of implants such as surface chemistry, oxide thickness, morphology/pore characteristics, crystal structures and roughness were characterized with various surface analytic techniques. Implants were inserted into the tibiae of ten New Zealand white rabbits. After a follow-up period of 3 and 6 weeks, removal torque (RTQ), osseointegration speed (DeltaRTQ/Deltahealing time) and integration strength of implants were measured. Bonding failure analysis of the bone-to-implant interface was performed. RESULTS: The speed the and strength of osseointegration of Mg implants were significantly more rapid and stronger than for turned implants at follow-up periods of 3 and 6 weeks. Bonding failure for Mg implants dominantly occurred within the bone tissue, whereas bonding failure for turned implants mainly occurred at the interface between implant and bone. CONCLUSIONS: Oxidized, bioactive implants are rapidly and strongly integrated in bone. The present results indicate that the rapid and strong integration of oxidized, bioactive Mg implants to bone may encompass immediate/early loading of clinical implants.
|
|
| 7. |
- Sul, Young-Taeg, 1960, et al.
(författare)
-
Oxidized implants and their influence on the bone response.
- 2001
-
Ingår i: Journal of Materials Science: Materials in Medicine. - 0957-4530. ; 12:10-12, s. 1025-31
-
Tidskriftsartikel (refereegranskat)abstract
- Surface oxide properties are regarded to be of great importance in establishing successful osseointegration of titanium implants. Despite a large number of theoretical questions on the precise role of oxide properties of titanium implants, current knowledge obtained from in vivo studies is lacking. The present study is designed to address two aspects. The first is to verify whether oxide properties of titanium implants indeed influence the in vivo bone tissue responses. The second, is to investigate what oxide properties underline such bone tissue responses. For these purposes, screw-shaped/turned implants have been prepared by electrochemical oxidation methods, resulting in a wide range of oxide properties in terms of: (i) oxide thickness ranging from 200 to 1000 nm, (ii) the surface morphology of barrier and porous oxide film structures, (iii) micro pore configuration - pore sizes<8 microm by length, about 1.27 microm2 to 2.1 microm2 by area and porosity of about 12.7-24.4%, (iv) the crystal structures of amorphous, anatase and mixtures of anatase and rutile type, (v) the chemical compositions of TiO2 and finally, (vi) surface roughness of 0.96-1.03 microm (Sa). These implant oxide properties were divided into test implant samples of Group II, III, IV and V. Control samples (Group I) were turned commercially pure titanium implants. Quantitative bone tissue responses were evaluated biomechanically by resonance frequency analysis (RFA) and removal torque (RT) test. Quantitative histomorphometric analyses and qualitative enzyme histochemical detection of alkaline (ALP) and acidic phosphatase (ACP) activities were investigated on cut and ground sections after six weeks of implant insertion in rabbit tibia. In essence, from the biomechanical and quantitative histomorphometric measurements we concluded that oxide properties of titanium implants, i.e. the oxide thickness, the microporous structure, and the crystallinity significantly influence the bone tissue response. At this stage, however, it is not clear whether oxide properties influence the bone tissue response separately or synergistically. Copyright 2001 Kluwer Academic Publishers
|
|
| 8. |
- Sul, Young-Taeg, 1960, et al.
(författare)
-
Resonance frequency and removal torque analysis of implants with turned and anodized surface oxides.
- 2002
-
Ingår i: Clin Oral Implants Res. - 0905-7161. ; 13:3, s. 252-9
-
Tidskriftsartikel (refereegranskat)abstract
- The present experimental study was designed to address two issues. The first was to investigate whether oxide properties of titanium implants influenced bone tissue responses after an in vivo implantation time of six weeks. If such a result was found, the second aim was to investigate which oxide properties are involved in such bone tissue responses. Screw-shaped implants with a wide range of oxide properties were prepared by electrochemical oxidation methods, where the oxide thickness varied in the range of 200 nm to 1000 nm. The surface morphology was prepared in two substantially different ways, i.e. barrier and porous oxide film structures. The micropore structure revealed pore sizes of 8 microm in diameter, with a range in opening area from 1.27 microm 2 to 2.1 microm 2. Porosity ranged from 12.7% to 24.4%. The crystal structures of the titanium oxide were amorphous, anatase and a mixture of anatase and rutile type. The chemical compositions consisted mainly of TiO2. Surface roughness ranged from 0.96 microm to 1.03 microm (Sa). Each group of test samples showed its own, defined status with respect to these various parameters. The oxide properties of turned commercially pure titanium implants were used in the control group, which was characterized by an oxide thickness of 17.4 +/- 6.2 nm, amorphous type in crystallinity, TiO2 in chemical composition, and a surface roughness of 0.83 microm (Sa). Bone tissue responses were evaluated by resonance frequency measurements and removal torque tests that were undertaken six weeks after implant insertion in rabbit tibia. Implants that had an oxide thickness of approximately 600, 800 and 1000 nm demonstrated significantly stronger bone responses in the evaluation of removal torque values than did implants that had an oxide thickness of approximately 17 and 200 nm (P < 0.05). However, there were no difference between implants with oxide thicknesses of 17 and 200 nm (P = 0.99). It was concluded that oxide properties of titanium implants, which include oxide thickness, micropore configurations and crystal structures, greatly influence the bone tissue response in the evaluation of removal torque values. However, it is not fully understood whether these oxide properties influence the bone tissue response separately or synergistically.
|
|
| 9. |
- Sul, Young-Taeg, 1960, et al.
(författare)
-
The electrochemical oxide growth behaviour on titanium in acid and alkaline electrolytes.
- 2001
-
Ingår i: Medical Engineering & Physics. - 1350-4533. ; 23:5, s. 329-46
-
Tidskriftsartikel (refereegranskat)abstract
- Titanium implants have a thin oxide surface layer. The properties of this oxide layer may explain the good biocompatibility of titanium implants. Anodic oxidation results in a thickening of the oxide film, with possible improved biocompatability of anodized implants. The aim of the present study was twofold: (1) firstly, to characterize the growth behaviour of galvanostatically prepared anodic oxide films on commercially pure (c.p.) titanium and (2) secondly, to establish a better understanding of the electroche0mical growth behaviour of anodic oxide on commercially pure titanium (ASTM grade 1) after changes of the electrochemical parameters in acetic acid, phosphoric acid, calcium hydroxide, and sodium hydroxide under galvanostatic anodizing mode. The oxide thickness was measured by Ar sputter etching in Auger Electron spectroscopy (AES) and the colours were estimated by an L*a*b* system (lightness, hue and saturation) using a spectrophotometer. In the first part of our study, it was demonstrated that the interference colours were useful to identify the thickness of titanium oxide. It was also found that the anodic forming voltages with slope (dV/dt) in acid electrolytes were higher than in alkaline electrolytes. Each of the used electrolytes demonstrates an intrinsically specific growth constant (nm/V) in the range of 1.4--2.78 nm/V. In the second part of our study we found, as a general trend, that an increase of electrolyte concentration and electrolyte temperature respectively decreases the anodic forming voltage, the anodic forming rate (nm/s) and the current efficiency (nm.cm(2)/C), while an increase of the current density and the surface area ratio of the anode to cathode increase the anodic forming voltage, the anodic forming rate and the current efficiency. The effects of electrolyte concentration, electrolyte temperature, and agitation speed were explained on the basis of the model of the electrical double layer.
|
|