- Ahmed, Istaq, 1972, et al.
(författare)
-
Structural study and proton conductivity in Yb-doped BaZrO3
- 2007
-
Ingår i: Solid State Ionics. - 0167-2738. ; 178:(7-10), s. 515-520
-
Tidskriftsartikel (refereegranskat)abstract
- Traditional solid state sintering has been used to prepare the perovskite BaZr0.9Yb0.1O3-delta. Analysis of X-ray powder diffraction data shows that an increase of the unit cell parameter, a, was observed compared to undoped BaZrO3. Rietveld analysis of room temperature neutron powder diffraction data confirmed cubic symmetry (space group Pm-3m). Dynamic thermogravimetric analysis (TGA) indicates that the hydration process occurs below 200 degrees C. The strong O-H stretch band, 2500-3500 cm(-1), in the infrared absorbance spectrum clearly manifests the presence of protons in the hydrated material. Proton conductivity was investigated on hydrated and as-prepared samples under dry and wet atmospheres, respectively. Keywords: X-ray diffraction; neutron diffraction; Rietveld refinement; proton conductor; perovskite
|
|
| 3. |
- Lin, Yuan-Chih, 1987, et al.
(författare)
-
Understanding the Interactions between Vibrational Modes and Excited State Relaxation in Y₃₋ₓCeₓAl₅O₁₂: Design Principles for Phosphors Based on 5d-4f Transitions
- 2018
-
Ingår i: Chemistry of Materials. - : American Chemical Society (ACS). - 1520-5002 .- 0897-4756. ; 30:6, s. 1865-1877
-
Tidskriftsartikel (refereegranskat)abstract
- The oxide garnet Y 3 Al 5 O 12 (YAG), when a few percent of the activator ions Ce 3+ substitutes for Y 3+ , is a luminescent material widely used in phosphor-converted white lighting. However, fundamental questions surrounding the defect chemistry and luminescent per formance of this material remain, especially in regard to the nature and role of vibrational dynamics. Here, we provide a complete phonon assignment of YAG and establish the general spectral trends upon variation of the Ce 3+ dopant concentration and temperature, which are shown to correlate with the macroscopic luminescence properties of Y 3-x Ce x Al 5 O 12 . Increasing the Ce 3+ concentration and/or temperature leads to a red-shift of the emitted light, as a result of increased crystal-field splitting due to a larger tetragonal distortion of the CeO 8 moieties. Decreasing the Ce 3+ concentration or cosubstitution of smaller and/or lighter atoms on the Y sites creates the potential to suppress thermal quenching of luminescence because the frequencies of phonon modes important for nonradiative relaxation mechanisms are upward-shifted and hence less readily activated. It follows that design principles for finding new Ce 3+ -doped oxide phosphors emitting at longer wavelengths require tetragonally distorted environments around the CeO 8 moieties and a sufficiently rigid host structure and/or low activator-ion concentration to avoid thermal quenching of luminescence.
|
|
| 4. |
- Lin, Yuan-Chih, 1987, et al.
(författare)
-
Vibrationally induced color shift tuning of photoluminescence in Ce³⁺-doped garnet phosphors
- 2019
-
Ingår i: Journal of Materials Chemistry C. - : Royal Society of Chemistry (RSC). - 2050-7534 .- 2050-7526. ; 7:41, s. 12926-12934
-
Tidskriftsartikel (refereegranskat)abstract
- A critical challenge in the field of phosphor converted white light emitting diodes (pc-WLEDs) pertains to understanding and controlling the variation of emission color with device temperature. Here we, through a combined photoluminescence (PL) and Raman spectroscopy study of the three garnet type phosphors Ce3+-doped Y3Al5O12 (YAG:Ce3+), Ca3Sc2Si3O12 (CSS:Ce3+), and Sr3Y2Ge3O12 (SYG:Ce3+), show that the color of the PL is systematically shifted upon changing the operation temperature of the phosphor. A general trend is observed that the PL exhibits a red-shift as a function of increasing temperature, until the point at which the vibrational modes of the CeO8 moieties, which induce dynamical tetragonal distortions of the CeO8 dodecahedra, are fully activated. Upon further temperature increase, the PL turns to a blue-shift because of a counteracting and predominating effect of thermal lattice expansion that progressively makes the CeO8 dodecahedra more cubal like. Since this behavior is the result of the symmetry relations intrinsic to the garnet structure, the present mechanism can be generally applicable to materials of this type. It thereby provides a route for tuning the PL of this important class of phosphor materials.
|
|
| 5. |
- Svenningsson, Leo, 1990, et al.
(författare)
-
Molecular Orientation Distribution of Regenerated Cellulose Fibers Investigated with Polarized Raman Spectroscopy
- 2019
-
Ingår i: Macromolecules. - : American Chemical Society (ACS). - 1520-5835 .- 0024-9297. ; 52:10, s. 3918-3924
-
Tidskriftsartikel (refereegranskat)abstract
- The molecular orientation distribution of polymeric fibers influences physical properties. We present a novel method of analyzing polarized Raman experiments to determine molecular orientation, which is based on exchanging the Legendre polynomial approach with a wrapped Lorentzian function, as determined from a prescreening of X-ray scattering patterns. This method removes the need for performing right angle scattering experiments while avoiding common approximations. The molecular orientation of regenerated cellulose fibers, using the presented method, is shown to correlate well with X-ray scattering and an analogous experiment using solid-state NMR spectroscopy. Challenges of quantitatively measuring molecular anisotropy occur with semi-crystalline, partially modified, or composite materials. As such, a plethora of techniques, each with a unique chemical selectivity, is paramount for material characterization.
|
|
| 6. |
- Ahmed, Istaq, 1972, et al.
(författare)
-
Crystal structure and proton conductivity of BaZr0.9Sc0
- 2008
-
Ingår i: Journal of the American Ceramic Society. - : Wiley. - 0002-7820 .- 1551-2916. ; 91:9, s. 3039-3044
-
Tidskriftsartikel (refereegranskat)abstract
- Solid-state sintering has been used to prepare the perovskite BaZr0.9Sc0.1O3-delta. Analysis of X-ray powder diffraction data shows that an increase of the unit cell parameter, a, was observed after deuteration. Rietveld analysis of room-temperature neutron powder diffraction data confirmed cubic symmetry (space group Pm-3m). Dynamic thermogravimetric analysis indicates that the hydration process occurs below 335 degrees C and approximately 58% of the theoretical number of protonic defects can be filled. The presence of protons/deutrons is seen from the strong O-H/O-D stretch band in the infrared spectrum of the hydrated/deuterated samples. The proton conductivity of a prehydrated sample was investigated under dry and wet Ar atmospheres
|
|
| 7. |
- Ahmed, Istaq, 1972, et al.
(författare)
-
Location of deuteron sites in the proton conducting perovskite BaZr0.50In0.50O3-y
- 2008
-
Ingår i: Journal of Alloys and Compounds. - : Elsevier BV. - 0925-8388. ; 450:1-2, s. 103-110
-
Tidskriftsartikel (refereegranskat)abstract
- High-resolution neutron powder diffraction data have been collected on deuterated and dried samples of the perovskite BaZr0.5In0.5O2.75 at 5 K and room temperature, respectively. Inspection of Fourier nuclear density maps for the deuterated phase have allowed the deuteron position to be refined on a 12h (1/2, y, 0) crystallographic site, with y = 0.217(4) yielding a chemically reasonable O-D distance of 0.92(2) angstrom. Evidence for anisotropy of the deuteron position is also found consistent with a 24k crystallographic site (0.56, 0.21, 0) indicative of displacements of the ion towards neighbouring oxygen ions. The presence of static oxygen disorder in both the dried and deuterated samples is apparent from the structural analyses. Raman spectra confirm short range deviations from cubic symmetry for both dried and hydrated samples.
|
|
| 8. |
- Ahmed, Istaq, 1972, et al.
(författare)
-
Proton conduction in Perovskite Oxide BaZr0.5Yb0.5O3-δ Prepared by Wet Chemical Route
- 2008
-
Ingår i: Journal of the Electrochemical Society. - : The Electrochemical Society. - 1945-7111 .- 0013-4651. ; 155:11, s. 97-102
-
Tidskriftsartikel (refereegranskat)abstract
- A wet chemical route has been used to synthesize the oxygen deficient perovskite Ba Zr0.5 Yb0.5 O3-δ. Analysis of X-ray powder diffraction data showed that both dried and hydrated samples adopt cubic crystal structures of space group Pm 3- m. Dynamic thermogravimetric analysis showed a significant mass loss for the hydrated sample compared to the dried sample, indicating that ∼28% of the oxygen vacancies are filled by protonic defects. The strong O-H stretch band, 2500-3500 cm-1, in the IR absorbance spectrum also clearly manifests the presence of significant levels of protons in the hydrated material. Proton conductivity was investigated on prehydrated (under dry Ar) and as-prepared (under wet Ar) samples. The heating cycle of the prehydrated sample showed higher proton conductivity compared to the cooling cycle, especially in the intermediate temperature range (150-550°C). Finally, comparison with data for Ba Zr0.9 Yb0.1 O3-δ revealed that the more heavily doped sample showed higher proton conductivity compared to the more lightly doped sample. © 2008 The Electrochemical Society.
|
|
| 9. |
|
|
| 10. |
- Ahmed, Istaq, 1972, et al.
(författare)
-
Synthesis and structural characterization of perovskite type proton conducting BaZr1-xInxO3-delta (0.0 <= x <= 0.75)
- 2006
-
Ingår i: Solid State Ionics. - : Elsevier BV. - 0167-2738 .- 1872-7689. ; 177:17-18, s. 1395-1403
-
Tidskriftsartikel (refereegranskat)abstract
- Solid state sintering has been used to prepare the cubic perovskite structured compounds BaZr1-xInxO3-delta (0.0 <= x <= 0.75). Analysis of X-ray powder diffraction (XRPD) data reveals that the unit cell parameter, a, increases linearly with an increased Indium concentration. XRPD data was also used to demonstrate the completion of sample hydration, which was reached when the materials showed a set of single-phase Bragg-peaks. Dynamic thermogravimetric analysis (TGA) data showed that approx. 89% of the total number of available oxygen vacancies can be filled in BaZr1-xInxO3-delta for x=0.50, and that the maximum water uptake occurs below 300 degrees C. Rietveld analysis of the room temperature neutron powder diffraction (NPD) data confirmed the average cubic symmetry (space group Pm-3m), and an expansion of the unit cell parameter after the hydration reaction. The strong O-H stretch band, 2500-3500 cm(-1), in the infrared absorbance spectrum clearly manifests the presence of protons in the hydrated material. Proton conductivity of hydrated BaZr1-xInxO3-delta, x=0.75 was investigated during heating and cooling cycles under dry argon atmosphere. The total conductivity during the heating cycle was nearly two orders of magnitude greater than that of cooling cycle at 300 degrees C, whilst these values were similar at higher temperatures i.e. T > 600 degrees C.
|
|