- Adachi, N., et al.
(författare)
-
Epitaxial Bi3Fe5O12(001) films grown by pulsed laser deposition and reactive ion beam sputtering techniques
- 2000
-
Ingår i: Journal of Applied Physics. - : AIP Publishing. - 0021-8979 .- 1089-7550. ; 88:5, s. 2734-2739
-
Tidskriftsartikel (refereegranskat)abstract
- We report on processing and comparative characterization of epitaxial Bi3Fe5O12 (BIG) films grown onto Gd-3(ScGa)(5)O-12[GSGG,(001)] single crystal using pulsed laser deposition (PLD) and reactive ion beam sputtering (RIBS) techniques. A very high deposition rate of about 0.8 mu m/h has been achieved in the PLD process. Comprehensive x-ray diffraction analyses reveal epitaxial quality both of the films: they are single phase, exclusively (001) oriented, the full width at half maximum of the rocking curve of (004) Bragg reflection is 0.06 deg for PLD and 0.05 deg for RIBS film, strongly in-plane textured with cube-on-cube film-to-substrate epitaxial relationship. Saturation magnetization 4 pi M-s and Faraday rotation at 635 nm were found to be 1400 Gs and -7.8 deg/mu m in PLD-BIG, and 1200 Gs and -6.9 deg/mu m in RIBS-BIG. Ferromagnetic resonance (FMR) measurements performed at 9.25 GHz yielded the gyromagnetic ratio gamma=1.797x10(7) l/s Oe, 1.826x10(7) l/s Oe; the constants of uniaxial magnetic anisotropy were K-u(*)=-8.66x10(4) erg/cm(3), -8.60x10(4) erg/cm(3); the cubic magnetic anisotropy K-1=-2.7x10(3) erg/cm(3),-3.8x10(3) erg/cm(3); and the FMR linewidth Delta H=25 and 34 Oe for PLD and RIBS films correspondingly. High Faraday rotation, low microwave loss, and low coercive field less than or equal to 40 Oe of BIG/GSGG(001) films promise their use in integrated magneto-optic applications.
|
|
| 2. |
- Ansari, Nazanin, et al.
(författare)
-
Multicolor filter all-garnet magneto-optical photonic crystals
- 2012
-
Ingår i: Optics Letters. - 0146-9592 .- 1539-4794. ; 37:17, s. 3552-3554
-
Tidskriftsartikel (refereegranskat)abstract
- We demonstrate a multicolor optical filter and isolator based on a double-cavity magneto-optical (MO) photonic crystal. Being grown as a heteroepitaxial all-garnet multilayer, it compromises a strong MO response and high optical transmittance. Low-loss, high Faraday rotation passbands as well as strong light rejection within the stop band were achieved by optimization of distance between cavities and repetition number of distributed Bragg reflectors.
|
|
| 3. |
- Balinsky, Michael, et al.
(författare)
-
Spin Pumping and the Inverse Spin-Hall Effect via Magnetostatic Surface Spin-Wave Modes in Yttrium-Iron Garnet/Platinum Bilayers
- 2015
-
Ingår i: IEEE Magnetics Letters. - 1949-307X .- 1949-3088. ; 6:3000604
-
Tidskriftsartikel (refereegranskat)abstract
- Spin pumping at a boundary between a yttrium-iron garnet (YIG) film and a thin platinum (Pt) layer is studied under conditions in which a magnetostatic surface spin wave (MSSW, or Damon-Eshbach mode) is excited in YIG by a narrow strip-line antenna. It is shown that the voltage created by the inverse spin-Hall effect (ISHE) in Pt is strongly dependent on the wavevector of the excited MSSW. For YIG film thicknesses of 41 and 0.9 mu m, the maximum ISHE voltage corresponds to the maximum of efficiently excited MSSW wavevectors and does not coincide with the maximum of absorbed microwave power. For a thinner (0.175 mu m) YIG film, the maximum of the ISHE voltage moves closer to the ferromagnetic resonance and almost coincides with the region of the maximum microwave absorption. We show that the effect is related to the change in the thickness profile and the wavenumber spectrum of the excited MSSW taking place when the YIG film thickness is increased.
|
|
| 4. |
- Belotelov, V. I., et al.
(författare)
-
Magnetophotonic intensity effects in hybrid metal-dielectric structures
- 2014
-
Ingår i: Physical Review B. Condensed Matter and Materials Physics. - 1098-0121 .- 1550-235X. ; 89:4, s. 045118-
-
Tidskriftsartikel (refereegranskat)abstract
- The magneto-optical properties of a hybrid metal-dielectric structure consisting of a one-dimensional gold grating on top of a magnetic waveguide layer are studied experimentally and theoretically. It is demonstrated that a magnetic field applied in the longitudinal configuration (in the plane of the magnetic film and perpendicular to the slits in the gold grating) to the metal-dielectric structure modifies the field distribution of the optical modes and thus changes the mode excitation conditions. In the optical far field, this manifests in the alteration of the optical transmittance or reflectance when the structure becomes magnetized. This magneto-optical effect is shown to represent a novel class of effects related to the magnetic-field-induced modification of the Bloch modes of the periodic hybrid structure. That is why we define this effect as "longitudinal magnetophotonic intensity effect" (LMPIE). The LMPIE has two contributions, odd and even in magnetization. While the even LMPIE is maximal for the light polarized perpendicular to the grating slits (TM) and minimal for the orthogonal polarization (TE), the odd LMPIE takes maximum values at some intermediate polarization and vanishes for pure TM and TE polarizations. Two principal modes of the magnetic layer - TM and TE - acquire in the longitudinal magnetic field additional field components and thus turn into quasi-TM and quasi-TE modes, respectively. The largest LMPIE is observed for excitation of the antisymmetrical quasi-TE mode by TM-polarized light. The value of the LMPIE measured for the plasmonic structure with a magnetic film of Bi2Dy1Fe4Ga1O12 composition is about 1% for the even effect and 2% for the odd one. However, the plasmonic structure with a magnetic film with a higher concentration of bismuth (Bi2.97Er0.03Fe4Al0.5Ga0.5O12) gives significantly larger LMPIE: even LMPIE reaches 24% and odd LMPIE is 9%. Enhancement of the magneto-optical figure of merit (defined as the ratio of the specific Faraday angle of a magnetic film to its absorption coefficient) of the magnetic films potentially causes the even LMPIE to exceed 100% as is predicted by calculations. Thus, the nanostructured material described here may be considered as an ultrafast magnetophotonic light valve.
|
|
| 5. |
- Belotelov, V. I., et al.
(författare)
-
Plasmon-mediated magneto-optical transparency
- 2013
-
Ingår i: Nature Communications. - : Springer Science and Business Media LLC. - 2041-1723. ; 4, s. 2128-
-
Tidskriftsartikel (refereegranskat)abstract
- Magnetic field control of light is among the most intriguing methods for modulation of light intensity and polarization on sub-nanosecond timescales. The implementation in nanostructured hybrid materials provides a remarkable increase of magneto-optical effects. However, so far only the enhancement of already known effects has been demonstrated in such materials. Here we postulate a novel magneto-optical phenomenon that originates solely from suitably designed nanostructured metal-dielectric material, the so-called magneto-plasmonic crystal. In this material, an incident light excites coupled plasmonic oscillations and a waveguide mode. An in-plane magnetic field allows excitation of an orthogonally polarized waveguide mode that modifies optical spectrum of the magneto-plasmonic crystal and increases its transparency. The experimentally achieved light intensity modulation reaches 24%. As the effect can potentially exceed 100%, it may have great importance for applied nanophotonics. Further, the effect allows manipulating and exciting waveguide modes by a magnetic field and light of proper polarization.
|
|
| 6. |
- Blomqvist, Mats, et al.
(författare)
-
Electro-optic effect in ferroelectric Na0.5K0.5NbO3 thin films on oxide substrates
- 2006
-
Ingår i: Integrated Ferroelectrics. - : Informa UK Limited. - 1058-4587 .- 1607-8489. ; 80:1, s. 97-106
-
Tidskriftsartikel (refereegranskat)abstract
- We have deposited Na0.5NbO3 (NKN) films oil single crystal Al2O3(1 (1) under bar 02) and SrTiO3(001) substrates using rf-magnetron sputtering of a stoichiometric, high-density ceramic target. Using x-ray diffraction it was confirmed that NKN grows preferentially c-axis oriented on sapphire substrate and epitaxially oil the perovskite SrTiO3(001) substrate. Electro-optical (EO) properties were measured in visible light through a transverse method. With an applied dc field up to 20 kV/cm, the effective linear EO response was determined to r(eff) = 28 pm/V for NKN/Al2O3 and r(eff) = I I pm/V for NKN/SrTiO3, where a superlinear dependence was observed.
|
|
| 7. |
- Blomqvist, Mats, et al.
(författare)
-
Electrooptic ferroelectric Na0.5K0.5NbO3 films
- 2005
-
Ingår i: IEEE Photonics Technology Letters. - : Institute of Electrical and Electronics Engineers (IEEE). - 1041-1135 .- 1941-0174. ; 17:8, s. 1638-1640
-
Tidskriftsartikel (refereegranskat)abstract
- We report on waveguiding and electrooptic properties of epitaxial Na0.5K0.5NbO3 films grown by radio-frequency magnetron sputtering on Al2O3 (1102) single crystal substrates. High optical waveguiding performance has been demonstrated in infrared and visible light. The in-plane electrooptic effect has been recorded in transmission using a transverse geometry. At dc fields, the effective linear electrooptic coefficient was determined to 28 pm/V, which is promising for modulator applications.
|
|
| 8. |
- Blomqvist, Mats, et al.
(författare)
-
High-performance epitaxial Na0.5K0.5NbO3 thin films by magnetron sputtering
- 2002
-
Ingår i: Applied Physics Letters. - : AIP Publishing. - 0003-6951 .- 1077-3118. ; 81:2, s. 337-339
-
Tidskriftsartikel (refereegranskat)abstract
- Epitaxial Na0.5K0.5NbO3 (NKN) thin films have been grown on LaAlO3 substrates by rf magnetron sputtering of a stoichiometric, high-density, ceramic target. X-ray diffraction analysis showed c-axis oriented cube-on-cube growth. Micrometer size interdigital capacitor (IDC) structures were defined on the surface of the NKN film using photolithography. The electrical characterization at 1 MHz showed dissipation factor tan delta of 0.010, tunability 16.5% at 200 kV/cm and dielectric permittivity epsilon(r)=470. The frequency dispersion of epsilon(r) between 1 kHz and 1 MHz was 8.5% and the IDCs showed very good insulating properties with leakage current density on the order of 30 nA/cm(2) at 400 kV/cm. The polarization loop exhibits weak ferroelectric hysteresis with maximum polarization 23.5 muC/cm(2) at 600 kV/cm. These results are promising for tunable microwave devices based on rf sputtered NKN thin films.
|
|
| 9. |
- Blomqvist, Mats, et al.
(författare)
-
Optical waveguiding in magnetron-sputtered Na0.5K0.5NbO3 thin films on sapphire substrates
- 2003
-
Ingår i: Applied Physics Letters. - : AIP Publishing. - 0003-6951 .- 1077-3118. ; 82:3, s. 439-441
-
Tidskriftsartikel (refereegranskat)abstract
- Preferentially oriented perovskite-structured Na0.5K0.5NbO3 (NKN) thin films have been deposited on hexagonal Al2O3(01 (1) under bar2) substrates using rf magnetron sputtering of a stoichiometric, high-density, ceramic target. Structural and film surface properties were measured using x-ray diffraction and atomic force microscopy, respectively. Optical and waveguiding properties were characterized using a prism-coupling technique. We observed sharp and distinguishable TM and TE propagation modes and measured the refractive index of NKN thin films of different thicknesses. The ordinary and extraordinary refractive indices were calculated to be n(o)=2.247+/-0.002 and n(e)=2.216+/-0.002 for a 2.0-mum-thick film at 632.8 nm. This implies a birefringence Deltan=n(e)-n(o)=-0.031+/-0.002 in the film. These first results show the potential use of rf-sputtered NKN films as an electro-optical active material.
|
|
| 10. |
- Blomqvist, Mats, et al.
(författare)
-
Rf-magnetron sputtered ferroelectric (Na,K)NbO3 films
- 2002
-
Ingår i: Proceedings of the 13th IEEE International Symposium on Applications of Ferroelectronics. - 0780374142 ; , s. 195-198
-
Konferensbidrag (refereegranskat)abstract
- Sodium potassium niobate (Na,K)NbO3 (NKN) thin films were grown by rf-magnetron sputtering from stoichiometric Na0.5K0.5NbO3 target on LaAlO3 (LAO) single crystals and polycrystalline Pt80Ir20 (PtIr) substrates. NKN films on polycrystalline PtIr substrates were found to be preferentially (004 oriented while XRD measurements reveal epitaxial quality of NKN/LaAlO3 film structures. The ferroelectric state in NKN/PtIr films at room temperature is indicated by polarization loops with polarization as high as 33.4 muC/cm(2) at 700 kV/crn, remnant polarization of 9.9 muC/cm(2), and coercive field of 91 kV/cm. I-V characteristics of vertical Au/NKN/PtIr capacitive cells and planar Au/NKN/LAO interdigital capacitors (IDCs) showed very good insulating properties. For NKN IDC the leakage current density was in the order of 30 nA/cm(2) at 400 kV/cm. Rf dielectric spectroscopy demonstrates low loss, low frequency dispersion, and high voltage tunability both for vertical Au/NKN/PtIr and planar interdigital Au/NKN/LAO capacitors.
|
|