| 1. |
- Fang, Hailiang, et al.
(författare)
-
Insights into phase transitions and magnetism of MnBi crystals synthesized from self-flux
- 2019
-
Ingår i: Journal of Alloys and Compounds. - : ELSEVIER SCIENCE SA. - 0925-8388 .- 1873-4669. ; 781, s. 308-314
-
Tidskriftsartikel (refereegranskat)abstract
- To effectively synthesize high purity ferromagnetic low temperature phase (LTP) MnBi with optimal microstructure is still a challenge that needs to be overcome for the system to reach its full potential. Here, the phase transitions and magnetic properties of MnBi crystals are reported. The phase transition between the low and high temperature structure of MnBi was systematically investigated at different heating/cooling rates using in situ synchrotron radiation X-ray diffraction. The material crystallizes in a layered hexagonal structure giving a platelike microstructure. The magnetic characterization of the crystals reveal that the saturation magnetization varies from 645 kA/m at 50 K to 546 kA/m at 300 K. Magnetization measurements also show that the sample upon heating becomes non-magnetic and transforms to the high temperature phase (HTP) at similar to 640 K, and that it regains ferromagnetic properties and transforms back to the LTP at similar to 610 K upon subsequent cooling.
|
|
| 2. |
- Kontos, Sofia, et al.
(författare)
-
Measured and calculated properties of B-doped τ-phase MnAl : A rare earth free permanent magnet
- 2019
-
Ingår i: Journal of Magnetism and Magnetic Materials. - : Elsevier BV. - 0304-8853. ; 474, s. 591-598
-
Tidskriftsartikel (refereegranskat)abstract
- The metastable tetragonal τ-phase MnAl has been doped interstitially with B through a drop synthesis method creating the (Mn0.55Al0.45)B0.02 compound. The as-casted samples were annealed, quenched and thereafter ball-milled and relaxed in order to decrease grain size and reduce the number of crystallographic defects. The Curie temperature of the quenched sample was estimated to 655 K. The magnetization, coercivity and anisotropy were analyzed with respect to flash-milling time, relaxation time and temperature. The results show that (Mn0.55Al0.45)B0.02 could be directly obtained from drop synthesis. The highest measured saturation magnetization of 393 kA/m (measured at ±1440kA/m) was achieved with a relaxation process after 1.5h milling, giving a theoretical maximum energy product of 48 kJ/m3. The highest value of the coercivity was 355 kA/m achieved by flash-milling for 10 h. However, the high coercivity was achieved at an expense of low saturation magnetization.
|
|
| 3. |
- Li, Jiheng, et al.
(författare)
-
Effect of Initial Oriented Columnar Grains on the Texture Evolution and Magnetostriction in Fe-Ga Rolled Sheets
- 2017
-
Ingår i: Metals. - : MDPI AG. - 2075-4701. ; 7:2
-
Tidskriftsartikel (refereegranskat)abstract
- The effects of initial oriented columnar grains on the texture evolution and magnetostriction in (Fe83Ga17)(99.9)(NbC)(0.1) rolled sheets were investigated. The recrystallization texture evolution exhibited the heredity of initial orientations, concerning the formation of cube and Goss textures in the primary recrystallized sheet for the columnar-grained sample. Moreover, the growth advantage of Goss grains was more obvious than that of cube grains during the secondary recrystallization process. Because of the combined effect of this and Nb-rich precipitates as inhibitors, a sharp Goss texture and very large Goss grains were achieved in the secondary recrystallized sheet for the columnar-grained sample. For comparison, the secondary recrystallization in the equiaxed-grained sample was not fully developed although there were Nb-rich precipitates as inhibitors. We think this could be ascribed to the large particle size and premature coarsening of precipitates. Magnetostriction of the secondary recrystallized columnar-grained sheet was up to 232 ppm owing to the ideal Goss texture and quite large grain size. As for the equiaxed-grained sample, the magnetostriction was only 163 ppm in the secondary recrystallized sheet.
|
|