| 1. |
- Bianchi, Marco, et al.
(författare)
-
Robust Surface Doping of Bi2Se3 by Rubidium Intercalation
- 2012
-
Ingår i: ACS Nano. - : American Chemical Society (ACS). - 1936-086X .- 1936-0851. ; 6:8, s. 7009-7015
-
Tidskriftsartikel (refereegranskat)abstract
- Rubidium adsorption on the surface of the topological insulator Bi2Se3 is found to induce a strong downward band bending, leading to the appearance of a quantum-confined two-dimensional electron gas state (2DEG) in the conduction band. The 2DEG shows a strong Rashba-type spin orbit splitting, and it has previously been pointed out that this has relevance to nanoscale spintronics devices. The adsorption of Rb atoms, on the other hand, renders the surface very reactive, and exposure to oxygen leads to a rapid degrading of the 2DEG. We show that intercalating the Rb atoms, presumably into the van der Waals gaps in the quintuple layer structure of Bi2Se3, drastically reduces the surface reactivity while not affecting the promising electronic structure. The intercalation process is observed above room temperature and accelerated with increasing initial Rb coverage, an effect that is ascribed to the Coulomb interaction between the charged Rb ions. Coulomb repulsion is also thought to be responsible for a uniform distribution of Rb on the surface.
|
|
| 2. |
- Lock, Nina, et al.
(författare)
-
Copper doped TiO2 nanoparticles characterized by X-ray absorption spectroscopy, total scattering, and powder diffraction - a benchmark structure-property study
- 2013
-
Ingår i: Dalton Transactions. - : Royal Society of Chemistry (RSC). - 1477-9234 .- 1477-9226. ; 42:26, s. 9555-9564
-
Tidskriftsartikel (refereegranskat)abstract
- Metal functionalized nanoparticles potentially have improved properties e. g. in catalytic applications, but their precise structures are often very challenging to determine. Here we report a structural benchmark study based on tetragonal anatase TiO2 nanoparticles containing 0-2 wt% copper. The particles were synthesized by continuous flow synthesis under supercritical water-isopropanol conditions. Size determination using synchrotron PXRD, TEM, and X-ray total scattering reveals 5-7 nm monodisperse particles. The precise dopant structure and thermal stability of the highly crystalline powders were characterized by X-ray absorption spectroscopy and multi-temperature synchrotron PXRD (300-1000 K). The combined evidence reveals that copper is present as a dopant on the particle surfaces, most likely in an amorphous oxide or hydroxide shell. UV-VIS spectroscopy shows that copper presence at concentrations higher than 0.3 wt% lowers the band gap energy. The particles are unaffected by heating to 600 K, while growth and partial transformation to rutile TiO2 occur at higher temperatures. Anisotropic unit cell behavior of anatase is observed as a consequence of the particle growth (a decreases and c increases).
|
|