1. |
- Solangi, Muhammad Yameen, et al.
(författare)
-
In-situ growth of nonstoichiometric CrO0.87 and Co3O4 hybrid system for the enhanced electrocatalytic water splitting in alkaline media
- 2023
-
Ingår i: International journal of hydrogen energy. - : PERGAMON-ELSEVIER SCIENCE LTD. - 0360-3199 .- 1879-3487. ; 48:93, s. 36439-36451
-
Tidskriftsartikel (refereegranskat)abstract
- The development of electrocatalysts for electrochemical water splitting has received considerable attention in response to the growing demand for renewable energy sources and environmental concerns. In this study, a simple hydrothermal growth approach was developed for the in-situ growth of non-stoichiometric CrO0.87 and Co3O4 hybrid materials. It is apparent that the morphology of the prepared material shows a heterogeneous aggregate of irregularly shaped nanoparticles. Both CrO0.87 and Co3O4 have cubic crystal structures. Its chemical composition was governed by the presence of Co, Cr, and O as its main constituents. For understanding the role CrO0.87 plays in the half-cell oxygen evolu-tion reaction (OER) in alkaline conditions, CrO0.87 was optimized into Co3O4 nanostructures. The hybrid material with the highest concentration of CrO0.87 was found to be highly efficient at driving OER reactions at 255 mV and 20 mA cm(-2). The optimized material demonstrated excellent durability for 45 h and a Tafel slope of 56 mV dec(-1). Several factors may explain the outstanding performance of CrO0.87 and Co3O4 hybrid materials, including multiple metallic oxidation states, tailored surface properties, fast charge transport, and surface defects. An alternative method is proposed for the preparation of new generations of electrocatalysts for the conversion and storage of energy. (c) 2023 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.
|
|
2. |
- Tahira, Aneela, et al.
(författare)
-
Role of cobalt precursors in the synthesis of Co 3 O 4 hierarchical nanostructures toward the development of cobalt‐based functional electrocatalysts for bifunctional water splitting in alkaline and acidic media
- 2022
-
Ingår i: Journal of the Chinese Chemical Society (Taipei). - : John Wiley & Sons. - 0009-4536 .- 2192-6549. ; 69:4, s. 681-691
-
Tidskriftsartikel (refereegranskat)abstract
- The precursors have significant influence on the catalytic activity of nonprecious electrocatalysts for effective water splitting. Herein, we report active electrocatalysts based on cobalt oxide (Co3O4) hierarchical nanostructures derived from four different precursors of cobalt (acetate, nitrate, chloride, and sulfate salts) using the low-temperature aqueous chemical growth method. It has been found that the effect of precursor on the morphology of nanostructured material depends on the synthetic method. The Co3O4 nanostructures exhibited cubic phase derived from these four precursors. The Co3O4 nanostructures obtained from chloride precursor have demonstrated improved oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) compared to other precursors due relatively higher content of Co3O4 nanostructures at the surface of material. An overpotential of 400 mV versus reversible hydrogen electrode (RHE) at 10 mA cm−2 was observed for HER. The Co3O4 nanostructures derived from the chloride precursor have shown favorable reaction kinetics via 34 mV dec−1 value of the Tafel slope for HER reaction. The Co3O4 nanostructures derived from chloride precursor have also shown an excellent HER durability for 15 hr in alkaline media. Furthermore, the OER functional characterization was carried out onto Co3O4 nanostructures derived from chloride precursor exhibited 220 mV overpotential at 10 mA cm−2 and Tafel slope of 56 mV dec−1. Importantly, the reason behind the favorable catalytic activity of Co3O4 nanostructures derived from chloride precursor was linked to one order of magnitude smaller charge transfer resistance and higher amount of Co3O4 content at the surface of nanostructures than the Co3O4 nanostructures derived from other precursors. The performance of Co3O4 nanostructures derived from chloride precursor via the wet chemical method suggests that cobalt chloride precursor could be of great interest for the development of efficient, stable, nonprecious, and environmentally friendly electrocatalysts for the chemical energy conversion and storage devices.
|
|