- Almomani, Abdulla, et al.
(författare)
-
Constitutive model calibration for the thermal viscoelastic-viscoplastic behavior of high density polyethylene under monotonic and cyclic loading
- 2023
-
Ingår i: Polymer testing. - : Elsevier BV. - 0142-9418 .- 1873-2348. ; 118
-
Tidskriftsartikel (refereegranskat)abstract
- High density polyethylene (HDPE) can show viscoelastic-viscoplastic behaviors under monotonic loads and a stress softening after reloading under cyclic ones. This sets a challenge in simultaneously representing such response in material constitutive models. In addition, due to the adoption of novel accelerated tests at higher temperatures, e.g., 95 degrees C, the need for a higher temperature calibration is motivated. Therefore, the objective of this study is threefold: (i) to investigate the capability of the three network viscoplastic (TNV) model in capturing HDPE thermo-viscoplasticity under monotonic and cyclic loads, (ii) to report observations on HDPE at various strain-rates and temperatures from 23 degrees C to 95 degrees C including the alpha-relaxation region (iii) to explore the ratcheting behavior of HDPE, i.e., cyclic creep. The FEA analysis based on the calibrated TNV model was successfully able to predict the HDPE behavior under static, quasi-static and dynamic loads. The predicted strain range Delta epsilon and midrange strain epsilon s of the cyclic creep showed good agreements. This implies that the TNV model can be a reliable candidate for HDPE engineering assessments. Findings of this work will have many industrial applications, e.g., products manufacturers or resin producers, in which HDPE is used under complex loads. Similar procedures can be followed for other thermoplastics which lays the basis for establishing a standard calibration guideline.
|
|
| 3. |
- Mourad, Abdel Hamid, I, et al.
(författare)
-
Impact Strengthening of Laminated Kevlar/Epoxy Composites by Nanoparticle Reinforcement
- 2020
-
Ingår i: Polymers. - : MDPI. - 2073-4360. ; 12:12
-
Tidskriftsartikel (refereegranskat)abstract
- Herein, we report the fabrication and characterization of high-strength Kevlar epoxy composite sheets for structural application. This process includes optimization of the curing conditions of composite preparation, such as curing time and temperature, and the incorporation of nanofillers, such as aluminum oxide (Al2O3), silicon carbide (SiC), and multi-walled carbon nanotubes (MWCNT) in different weight percentages. Differential scanning calorimetry (DSC) was utilized to investigate the thermal stability and curing behavior of the epoxy, finding that a minimum of 5 min is required for complete curing under an optimized temperature of 170 degrees C. Moreover, mechanical characterization, including flexural and drop-weight tests, were performed and found to be in good agreement with the DSC results. Our results show that nanofiller incorporation improves the mechanical properties of Kevlar epoxy composites. Among the tested samples, 0.5% MWCNT incorporation obtained the highest mechanical strength.
|
|