| 1. |
- Khan, Inayat Ali, et al.
(författare)
-
Stable and Efficient PtRu Electrocatalysts Supported on Zn-BTC MOF Derived Microporous Carbon for Formic Acid Fuel Cells Application
- 2020
-
Ingår i: Frontiers in Chemistry. - : Frontiers Media S.A.. - 2296-2646. ; 8
-
Tidskriftsartikel (refereegranskat)abstract
- Highly efficient, well-dispersed PtRu alloy nanoparticles supported on high surface area microporous carbon (MPC) electrocatalysts, are prepared and tested for formic acid oxidation reaction (FAOR). The MPC is obtained by controlled carbonization of a zincbenzenetricarboxylate metal-organic framework (Zn-BTC MOF) precursor at 950◦C, and PtRu (30 wt.%) nanoparticles (NPs) are prepared and deposited via a polyol chemical reduction method. The structural and morphological characterization of the synthesized electrocatalysts is carried out using powder X-ray diffraction (PXRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), an energy dispersive X-ray (EDX) technique, and gas adsorption analysis (BET). The FAOR performance of the catalysts is investigated through cyclic voltammetry (CV), chronoamperometry (CA), and electrochemical impedance spectroscopy (EIS). A correlation between high electrochemical surface area (ECSA) and high FAOR performance of the catalysts is observed. Among the materials employed, Pt1Ru2/MPC 950 with a high electrochemical surface area (25.3 m2 g −1 ) consequently showed superior activity of the FAOR (Ir = 9.50 mA cm−2 and Jm = 2,403 mA mg−1 Pt ) at room temperature, with improved tolerance and stability toward carbonaceous species. The superior electrochemical performance, and tolerance to CO-poisoning and long-term stability is attributed to the high surface area carbon support (1,455 m2 g −1 ) and high percentage loading of ruthenium (20 wt.%). The addition of Ru promotes the efficiency of electrocatalyst by offering FAOR via a bifunctional mechanism.
|
|
| 2. |
- Hameed, Arslan, et al.
(författare)
-
ZIF-12/Fe-Cu LDH Composite as a High Performance Electrocatalyst for Water Oxidation
- 2021
-
Ingår i: Frontiers in Chemistry. - : Frontiers Media S.A.. - 2296-2646. ; 9
-
Tidskriftsartikel (refereegranskat)abstract
- Layered double hydroxides (LDH) are being used as electrocatalysts for oxygen evolution reactions (OERs). However, low current densities limit their practical applications. Herein, we report a facile and economic synthesis of an iron-copper based LDH integrated with a cobalt-based metal-organic framework (ZIF-12) to form LDH-ZIF-12 composite (1) through a co-precipitation method. The as-synthesized composite 1 requires a low overpotential of 337 mV to achieve a catalytic current density of 10 mA cm−2 with a Tafel slope of 89 mV dec−1. Tafel analysis further demonstrates that 1 exhibits a slope of 89 mV dec−1 which is much lower than the slope of 284 mV dec−1 for LDH and 172 mV dec−1 for ZIF-12. The slope value of 1 is also lower than previously reported electrocatalysts, including Ni-Co LDH (113 mV dec−1) and Zn-Co LDH nanosheets (101 mV dec−1), under similar conditions. Controlled potential electrolysis and stability test experiments show the potential application of 1 as a heterogeneous electrocatalyst for water oxidation.
|
|
| 3. |
- Khan, Inayat, et al.
(författare)
-
Zinc-Coordination Polymer-Derived Porous Carbon-Supported Stable PtM Electrocatalysts for Methanol Oxidation Reaction
- 2021
-
Ingår i: ACS Omega. - : American Chemical Society (ACS). - 2470-1343. ; 6:10, s. 6780-6790
-
Tidskriftsartikel (refereegranskat)abstract
- Porous carbon (PC) is obtained by carbonizing a zinc-coordination polymer (MOF-5) at 950 °C and PtM (M = Fe, Co, Ni, Cu, Zn) nanoparticles (NPs), which are deposited on PC using the polyol method. Structural and morphological characterizations of the synthesized materials are carried out by powder X-ray diffraction (PXRD), X-ray photoelectron spectroscopy (XPS), and high-resolution transmission electron microscopy (HRTEM), and the porosity was determined using a N2 adsorption/desorption technique. The results revealed that PtM NPs are alloyed in the fcc phase and are well dispersed on the surface of PC. The electrochemical results show that PtM/PC 950 catalysts have higher methanol oxidation reaction (MOR) performances than commercial Pt/C (20%) catalysts. After 3000 s of chronoamperometry (CA) test, the MOR performances decreased in the order of Pt1Cu1/PC 950 > Pt1Ni1/PC 950 > Pt1Fe1/PC 950 > Pt1Zn1/PC 950 > Pt1Co1/PC 950. The high MOR activities of the synthesized catalysts are attributed to the effect of M on methanol dissociative chemisorption and improved tolerance of Pt against CO poisoning. The high specific surface area and porosity of the carbon support have an additional effect in boosting the MOR activities. Screening of the first row transition metals (d5+n, n = 1, 2, 3, 4, 5) alloyed with Pt binary catalysts for MOR shows that Pt with d8 (Ni) and d9 (Cu) transition metals, in equivalent atomic ratios, are good anode catalysts for alcohol fuel cells.
|
|