| 1. |
- Banerjee, Amitava
(författare)
-
Materials Modelling for Energy Harvesting : From Conversion to Application through Storage
- 2019
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- In this Ph.D. thesis, ab initio density functional theory along with molecular dynamics and global optimization methods are used to unveil and understand the structures and properties of energy relevant materials. In this connection, the following applications are considered: i. electrocatalyst for solar fuel production through water splitting, ii. hybrid perovskite solar cell for generation of electrical energy and iii. Battery materials to store the electrical energy. The water splitting mechanism in terms of hydrogen evolution and oxygen evolution reactions (HER and OER) on the catalytic surfaces has been envisaged based on the free energy diagram, named reaction coordinate, of the reaction intermediates. The Ti-functionalized two-dimensional (2D) borophene monolayer has been emerged as a promising material for HER and OER mechanisms as compared to the pristine borophene sheet. Further investigation in the series of this noble metal free monolayer catalyst is 2D Al2C monolayer both in form of pristine and functionalized with nitrogen (N), phosphorous (P), boron (B), and sulphur (S). It has been observed that only B substituted Al2C shows very close to thermoneutral, that could be the most promising candidate for HER on functionalized Al2C monolayer. The adsorption of O* intermediate is stronger in S-substituted Al2C, whereas it is less strongly adsorbed on N-substituted Al2C. The subsequent consideration is being the case of n-type doping (W) along with Ti codoped in BiVO4 to enhance the efficiency of BiVO4 photoanode for water splitting. The determined adsorption energy and corresponding Gibbs free energies depict that the Ti site is energetically more favorable for water splitting. Moreover, the Ti site possesses a lower overpotential in the W–Ti codoped sample as compared to the mono-W doped sample. We have also explored the effect of mixed cation and mixed anion substitution in the hybrid perovskite in terms of structural stability, electronic properties and optical response of hybrid perovskite crystal structures. It has been found that the insertion of bromine (Br) into the system could modulate the stability of the Guanidinium lead iodide (GAPbI3) hybrid perovskite. Moreover, the band gap of the mixed hybrid perovskite is increased with the inclusion of smaller Br anion while replacing partially the larger iodine (I) anion. Finally the electrochemical storage mechanism for Sodium (Na) and lithium (Li) ion insertion has been envisaged in inorganic electrode (eldfellite, NaFe(SO4)2) as well as in more sustainable organic electrode (di-lithium terephthalate, Li2TP). The full desodiation capability of the eldfellite enhances the capacity while the activation energies (higher than 1 eV) for the Na+ ion diffusion for the charged state lower the ionic insertion rate. The key factor as the variation of Li-O coordination in the terephthalate, for the disproportionation redox reaction in Li2TP is also identified.
|
|
| 2. |
- Stefanov, Bozhidar, 1988-
(författare)
-
Photocatalytic TiO2 thin films for air cleaning : Effect of facet orientation, chemical functionalization, and reaction conditions
- 2015
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Poor indoor air quality is a source of adverse health effects. TiO2 coatings deposited on well-illuminated surfaces, such as window panes, can be used to fully mineralize indoor air pollutants by photocatalysis. In such applications it is important to ensure stable photocatalytic activity for a wide range of operating conditions, such as relative humidity and temperature, and to avoid deactivation of the catalyst.In this thesis photocatalytic removal of the indoor-pollutant acetaldehyde (CH3CHO) on nanostructured TiO2 films is investigated, and in particular it is proposed how such films can be modified and operated for maximum performance. Catalyst deactivation can be reduced by purposefully changing the surface acidity of TiO2 by covalently attaching SO4 to the surface. Moreover, the overall photocatalytic activity on anatase TiO2 films can be improved by increasing the fraction of exposed reactive {001} surfaces, which otherwise are dominated by {101} surfaces.In the first part of the thesis mode-resolved in-situ FTIR is used to elucidate the reaction kinetics of CH3CHO adsorption and photo-oxidation on the TiO2 and SO4 – modified TiO2 surfaces. Surface concentrations of main products and corresponding reaction rates were determined. Formate is the major reaction product, whose further oxidation limits the complete oxidation to gaseous species, and is responsible for photocatalyst deactivation by site inhibition. The oxidation reaction is characterized by two reaction pathways, which are associated with two types of surface reaction sites. On the sulfate modified TiO2 catalyst fewer intermediates are accumulated, and this catalyst resists deactivation much better than pure TiO2. A hitherto unknown intermediate – surface-bound acetaldehyde dimer with an adsorption band at 1643 cm−1 was discovered, using interplay between FTIR spectroscopy and DFT calculations.The second part of the thesis treats the effect of increasing the relative abundance of exposed {001} facets on the photocatalytic activity of anatase TiO2 films prepared by DC magnetron sputtering. A positive effect was observed both for liquid-phase photo-oxidation of methylene blue, and for gas-phase photocatalytic removal of CH3CHO. In both cases it was found that the exposed {001} surfaces were an order of magnitude more reactive, compared to the {101} ones. Furthermore, it was found that the reactive films were more resilient towards deactivation, and exhibited almost unchanged activity under varying reaction conditions. Finally, a synergetic effect of SO4 – modification and high fraction of exposed {001} surfaces was found, yielding photocatalysts with sustained high activity.The results presented here for facet controlled and chemically modified TiO2 films are of interest for applications in the built environment for indoor air purification and as self-cleaning surfaces.
|
|
| 3. |
- Backholm, Jonas, 1977-
(författare)
-
Electrochromic Properties of Iridium Oxide Based Thin Films
- 2008
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Electrochromic iridium oxide (IrOx) and iridium-tantalum oxide (IrTaOx) thin films were prepared by reactive magnetron sputtering. Composition, density, and structure were determined using Rutherford backscattering spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and electron energy loss spectroscopy. The electronic density of states (DOS) and the solid phase chemical diffusion coefficient (D) were determined for hydrogen in IrOx and IrTaOx by potentiostatic intermittent titration technique (PITT), and electrochemical impedance spectroscopy (EIS). The complex refractive indices were determined for colored and bleached IrOx and IrTaOx by inverting transmission and reflectance, measured using spectrophotometry in the 300-2500 nm wavelength range. A very porous structure, with a stoichiometry of IrO2.2, was found for IrOx. It contained ~4 nm sized grains. The IrTaOx had a denser structure built up by ~4 nm sized grains. The composition of IrTaOx was found to vary on a nanometer scale, with an average composition of IrTa1.4O5.6. It was found that DOS can be measured using PITT and EIS in the presence of spontaneous side reactions, even for systems influenced by non-negligible charge transfer kinetics and Ohmic drops. It was found that the measured DOS is 30-50% of the theoretically calculated DOS and that D is in the 10-10 – 10-11 cm2/s range for both materials. The hydrogen diffusion mechanism was described by an anomalous diffusion model, possibly indicating percolation or diffusion paths described by a fractal network. The refractive indices were found to be ~1.3 and ~2 for IrOx and IrTaOx, respectively, and independent of coloration state, whereas the extinction coefficients were found to modulate by ~30% for IrOx and ~50% for IrTaOx, making IrTaOx more favorable for electrochromic applications. A modulation peak was found at ~660 nm for both IrOx and IrTaOx associated with the removal of intraband transitions within the Ir t2g band.
|
|
| 4. |
|
|