| 1. |
- Canovic, Sead, 1979, et al.
(författare)
-
Oxidation of Co- and Ce-nanocoated FeCr steels: A microstructural investigation
- 2013
-
Ingår i: Surface and Coatings Technology. - : Elsevier BV. - 0257-8972. ; 215, s. 62-74
-
Tidskriftsartikel (refereegranskat)abstract
- The effect of novel Co and Ce nanocoatings on oxidation behaviour and chromium volatilization from a commercial Fe-22Cr steel (Sanergy HT) developed for solid oxide fuel cell interconnect applications is investigated. Three different coatings (10 nm Ce, 640 nm Co and 10 nm Ce + 640 nm Co) are studied. Uncoated and nanocoated samples are exposed isothermally at 850 C in the air with 3% H2O for 168 h. The detailed microstructure of the different coatings is investigated. The surface morphology and microstructure of the oxide scales are characterized by using scanning electron microscopy (SEM), transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM) and energy dispersive X-ray analysis (EDX). Cross-section TEM thin foils are prepared by using a combined FIB/SEM (focused ion beam/scanning electron microscope) instrument. A 640 nm cobalt coating strongly inhibits Cr volatilization but has only minor effects on oxidation rate. In contrast, a 10 nm Ce coating decreases the oxidation rate but has no significant effects on chromium volatilization. Combining the two coatings, i.e., applying a 640 nm Co coating on top of the 10 nm Ce, effectively reduces Cr evaporation and slows down the rate of alloy oxidation.
|
|
| 2. |
- Froitzheim, Jan, 1981, et al.
(författare)
-
Long term study of Cr evaporation and high temperature corrosion behaviour of Co coated ferritic steel for solid oxide fuel cell interconnects
- 2012
-
Ingår i: Journal of Power Sources. - : Elsevier BV. - 0378-7753. ; 220, s. 217-227
-
Tidskriftsartikel (refereegranskat)abstract
- The oxidation behaviour of the uncoated ferritic Fe-22Cr steel Sanergy HT is compared with an 640 nm Co coated version of the same material. The materials have been subject to corrosion and Cr volatilization measurements in air for up to 3000 h at 850 degrees C. Oxidation tests have been carried out both isothermal and discontinuously. The volatilization measurements were carried out using a recently developed denuder technique, which allows to quantify Cr evaporation in a time resolved manner. The oxidation process is studied from very initial phases (>15 s) to long term behaviour (3000 h). The formed oxide scales are analysed by XRD, SEM/EDX as well as TEM/EDX.The results show that both materials form an oxide scale with an inner layer of Cr2O3 and a spinel layer on top. In the case of the uncoated material, the spinel layer is of (Cr,Mn)(3)O-4 type while in the presence of a Co coating a (Co,Mn,Fe)(3)O-4 is formed. The Cr evaporation measurements show that despite the fact that the Co coating is very thin (640 nm) it effectively blocks Cr evaporation for at least 3000 h. This is in line with TEM analysis showing that after 3000 h there is only a low Cr content in the outer oxide scale. This long term stability indicates the suitability of the coated material as solid oxide fuel cell (SOFC) interconnect.
|
|