| 1. |
- Folkeson, Nicklas, 1981, et al.
(författare)
-
Fireside corrosion of stainless and low alloyed steels in a waste-fired CFB boiler; The effect of adding sulphur to the fuel
- 2008
-
Ingår i: Materials Science Forum. ; 595-598, s. 289-297
-
Tidskriftsartikel (refereegranskat)abstract
- Corrosion field tests have been carried out in the superheater region of a commercial waste-fired 75MW CFBC boiler using air cooled probes. Exposure time was 24 and 1000 hours. The effect of adding sulphur to the fuel on the corrosion of two high alloyed steels and a low alloyed steel was studied. The fuel consisted of 50% household waste and 50% industrial waste. The exposed samples were analyzed by ESEM/EDX and XRD. Metal loss was determined after 1000 hours. Both materials suffered significant corrosion in the absence of sulphur addition and the addition of sulphur to the fuel reduced corrosion significantly. The rapid corrosion of the high alloyed steel in the absence of sulphur addition is caused by the destruction of the chromium-containing protective oxide by formation of calcium chromate. Adding sulphur to the fuel inhibited chromate formation and increased the sulphate/chloride ratio in the deposit. Iron(II) chloride formed on the low alloyed steel regardless of whether sulphur was added or not.
|
|
| 2. |
|
|
| 3. |
- Pettersson, Carolina, 1980, et al.
(författare)
-
KCl-Induced High Temperature Corrosion of the Austenitic Fe-Cr-Ni Alloys 304L and Sanicro 28 at 600 °C
- 2006
-
Ingår i: Corrosion Science. ; 48:6, s. 1368-1378
-
Tidskriftsartikel (refereegranskat)abstract
- The influence of KCl(s) on the high temperature oxidation of the austenitic alloys 304L and Sanicro 28 at 600 °C in O2 + H2O environment is reported. 0.10 mg/cm2 KCl(s) was added before exposure. The samples are investigated by grazing angle XRD, SEM/EDX, and AES. In the absence of KCl, both alloys show protective behaviour in dry O2. In O2 + H2O environment, alloy 304L suffers local breakaway corrosion while Sanicro 28 still shows protective behaviour. The oxidation of both alloys is strongly accelerated by KCl. KCl reacts with chromium in the normally protective corundum-type oxide, forming K2CrO4. This depletes the scale in chromia and leads to the formation of a non-protective, iron-rich scale. The significance of KCl-induced corrosion in real applications is discussed and the oxidation behaviour of the two steels is compared.
|
|
| 4. |
- Pettersson, Jesper, 1978, et al.
(författare)
-
A pilot plant study of the effect of alkali salts on initial stages of the high temperature corrosion of alloy 304L
- 2004
-
Ingår i: Materials Science Forum. - 1662-9752 .- 0255-5476. ; 461-464, s. 965-972
-
Tidskriftsartikel (refereegranskat)abstract
- Alloy 304L was exposed for between 15 min to 12 hr in the 12MW CFB research boiler at the Chalmers university of technology using an air-cooled probe. The base fuel consisted of a mixture of 67% wood chips and 33% pellets. In addition to the base fuel experiment, a number of exposures were performed where S and Cl was added to the fuel in the form Of SO2(g) and HCl(aq) in order to control the flue gas chemistry in the superheater region. After the exposures the samples were analysed by ESEM/EDX, XRD and SAM. Burning a mixture of woodchips/pellets without adding sulphur or chlorine results in the formation of K2SO4 deposits on the corrosion probes. When HCl is added to the fuel KCl deposits form. The simultaneous addition of HCl and SO, results in a deposit consisting of a mixture of KCl and K2SO4. In all environments studied an oxide in the 100nm range forms. With time, the oxide becomes covered by ash deposits. After exposure to the biomass flue gas environment, the oxide is enriched in K, especially the outer part. Chlorine is not present in the oxide even when the KCl(s) forms on the surface. It is suggested that potassium chromate formation occurs by the reaction of potassium chloride with chromium oxide.
|
|
| 5. |
|
|
| 6. |
- Pettersson, Jesper, 1978, et al.
(författare)
-
The influence of sulphur additions on the corrosive environment in a waste-fired CFB boiler
- 2005
-
Ingår i: Materials Science Forum. - 1662-9752 .- 0255-5476. ; 522-523, s. 563-570
-
Tidskriftsartikel (refereegranskat)abstract
- Corrosion/deposition field tests have been carried out in the superheater region of a commercial waste-fired 75MW CFBC boiler using air cooled probes. The influence of material temperature (450-500 degrees C), flue gas temperature, temperature variations (i.e. thermal cycling) and additives to the fuel (elemental sulphur and dolomite) on deposition and corrosion was studied. The results presented here mainly consider the influence of sulphur additions to the fuel. The fuel was a mixture of 50% household waste and 50% industrial waste. After exposure the samples were analyzed by ESEM/EDX, XRD, AAS, FIB and IC. With no additional sulphur, alkali chlorides made up a large part of the deposit/corrosion product layer and in some cases chromate (VI) was detected. It is suggested that the chromate (VI) has formed by reaction of the protective oxide with alkali chlorides in the deposit. Adding sulphur to the fuel changed the composition of the deposits, alkali chlorides being largely replaced by alkali sulphates. No chromates(VI) were detected in the sulphur-added runs. It is suggested that adding sulphur to the fuel may decrease fireside corrosion because it changes the composition of the deposit. Alkali sulphates are much less corrosive than alkali chlorides partly because they do not form chromate(VI).
|
|
| 7. |
|
|
| 8. |
- Alamaa, Linda, et al.
(författare)
-
De reaktionära
- 2023
-
Ingår i: Fronesis. ; :76-77, s. 8-16
-
Tidskriftsartikel (övrigt vetenskapligt/konstnärligt)
|
|
| 9. |
- Enquist, Karl, et al.
(författare)
-
Membrane-integration characteristics of two ABC transporters, CFTR and P-glycoprotein
- 2009
-
Ingår i: Journal of Molecular Biology. - : Elsevier BV. - 0022-2836 .- 1089-8638. ; 387:5, s. 1153-1164
-
Tidskriftsartikel (refereegranskat)abstract
- To what extent do corresponding transmembrane helices in related integral membrane proteins have different membrane-insertion characteristics? Here, we compare, side-by-side, the membrane insertion characteristics of the 12 transmembrane helices in the adenosine triphosphate-binding cassette (ABC) transporters, P-glycoprotein (P-gp) and the cystic fibrosis transmembrane conductance regulator (CFTR). Our results show that 10 of the 12 CFTR transmembrane segments can insert independently into the ER membrane. In contrast, only three of the P-gp transmembrane segments are independently stable in the membrane, while the majority depend on the presence of neighboring loops and/or transmembrane segments for efficient insertion. Membrane-insertion characteristics can thus vary widely between related proteins.
|
|
| 10. |
|
|