| 1. |
- Auenhammer, Robert, 1991, et al.
(författare)
-
Fibre orientation distribution function mapping for short fibre polymer composite components from low resolution/large volume X-ray computed tomography
- 2024
-
Ingår i: Composites Part B: Engineering. - 1359-8368. ; 275
-
Tidskriftsartikel (refereegranskat)abstract
- Short glass fibre injection moulded composites, used in interior and exterior automotive parts, are exposed to complex stress states, for example during a crash. As the fibre scale dominates the composite’s material properties, numerical models need to account for the local fibre orientation. In recent years, mould flow simulation results have been exploited to predict the fibre orientations for finite element models, albeit with limited accuracy. Alternatively, X-ray computed tomography can be used to directly image and analyse fibre orientations. Traditionally, achieving the necessary resolution to image individual fibres restricts the imaging to small regions of the component. However, this study takes advantage of recent advancements in imaging and image analysis to overcome this limitation. As a result, it introduces, for the first time, a reliable, fast, and automated fibre orientation mapping for a full component based on image analysis at the individual fibre level; even for cases where the pixel size is significantly larger than the fibre diameter. By scanning at lower resolutions, a drastically larger volume of interest can be achieved. The resulting fibre orientation analysis and mapping algorithm, based on X-ray computed tomography, is well matched to the level of information required for automotive crash modelling with a standard element-size of a few millimetres. The entire process, encompassing image acquisition, image analysis and fibre orientation mapping, can be directly integrated into an industrial full component application in a matter of hours.
|
|
| 3. |
- Örnek, Cem, et al.
(författare)
-
Time-dependent in situ measurement of atmospheric corrosion rates of duplex stainless steel wires
- 2018
-
Ingår i: NPJ MATERIALS DEGRADATION. - : Springer Nature. - 2397-2106. ; 2:1
-
Tidskriftsartikel (refereegranskat)abstract
- Corrosion rates of strained grade UNS S32202 (2202) and UNS S32205 (2205) duplex stainless steel wires have been measured, in situ, using time-lapse X-ray computed tomography. Exposures to chloride-containing (MgCl2) atmospheric environments at 50 degrees C (12-15 M Cl(-)and pH similar to 5) with different mechanical elastic and elastic/plastic loads were carried out over a period of 21 months. The corrosion rates for grade 2202 increased over time, showing selective dissolution with shallow corrosion sites, coalescing along the surface of the wire. Corrosion rates of grade 2205 decreased over time, showing both selective and pitting corrosion with more localised attack, growing preferentially in depth. The nucleation of stress corrosion cracking was observed in both wires. Stainless steel: Comprehending corrosion The corrosion of two grades of stainless steel has been studied, in situ, under atmospheric exposure conditions. Grade '2205' duplex stainless steel (DSS) has been suggested as a possible container material for the storage of intermediate-level radioactive nuclear waste in the UK because of its high resistance to corrosion and stress corrosion cracking (SCC). Now a team led by D. Engelberg from The University of Manchester, United Kingdom, have used time-lapse X-ray computed tomography to determine the corrosion rates of strained grade '2202' and '2205' DSS wires-over the course of 21 months-that had been exposed to a chloride-containing thin-film electrolyte. They saw that although the corrosion rate of grade 2202 DSS wires increased with time, the corrosion rate for grade 2205 decreased, confirming its superior corrosion resistance. They also observed the nucleation of SCC cracks in both grades of wire and demonstrated that duplex stainless steels can suffer from low-temperature SCC.
|
|