| 1. |
- Chudinova, Ekaterina A., et al.
(författare)
-
Adhesion, proliferation, and osteogenic differentiation of human mesenchymal stem cells on additively manufactured Ti6Al4V alloy scaffolds modified with calcium phosphate nanoparticles
- 2019
-
Ingår i: Colloids and Surfaces B. - : Elsevier BV. - 0927-7765 .- 1873-4367. ; 176, s. 130-139
-
Tidskriftsartikel (refereegranskat)abstract
- In the present study, biocomposites based on 3D porous additively manufactured Ti6Al4V (Ti64) scaffolds modified with biocompatible calcium phosphate nanoparticles (CaPNPs) were investigated. Ti64 scaffolds were manufactured via electron beam melting technology using an Arcam machine. Electrophoretic deposition was used to modify the scaffolds with CaPNPs, which were synthesized by precipitation in the presence of polyethyleneimine (PEI). Dynamic light scattering revealed that the CaP/PEI nanoparticles had an average size of 46 ± 18 nm and a zeta potential of +22 ± 9 mV. Scanning electron microscopy (SEM) revealed that the obtained spherical CaPNPs had an average diameter of approximately 90 nm. The titanium-based scaffolds coated with CaPNPs exhibited improved hydrophilic surface properties, with a water contact angle below 5°. Cultivation of human mesenchymal stem cells (hMSCs) on the CaPNPs-coated Ti64 scaffolds indicated that the improved hydrophilicity was beneficial for the attachment and growth of cells in vitro. The Ti6Al4V/CaPNPs scaffold supported an increase in the alkaline phosphatase (ALP) activity of cells. In addition to the favourable cell proliferation and differentiation, Ti6Al4V/CaPNPs scaffolds displayed increased mineralization compared to non-coated Ti6Al4V scaffolds. Thus, the developed composite 3D scaffolds of Ti6Al4V functionalized with CaPNPs are promising materials for different applications related to bone repair.
|
|
| 2. |
- Surmeneva, Maria A., et al.
(författare)
-
In situ synthesis of a binary Ti–10at% Nb alloy by electron beam melting using a mixture of elemental niobium and titanium powders
- 2020
-
Ingår i: Journal of Materials Processing Technology. - : Elsevier BV. - 0924-0136 .- 1873-4774. ; 282
-
Tidskriftsartikel (refereegranskat)abstract
- This study reports the results of the preliminary assessment to fabricate Ti-10at% Nb alloy by electron beam melting (EBM®) from a blend of elemental Nb and Ti powders. The microstructure of the EBM-manufactured Ti-10at% Nb alloys is sensitive to the following factors: different sintering properties of Nb and Ti powders, powder particle properties, material viscosities at varying melt pool temperatures, β-stabilizer element content and the EBM® process parameters. Three phases were observed in as-manufactured Ti-10at% Nb alloy: μm-size Nb phase, a Nb-rich β-solid solution surrounding Nb phase, lamellar structured α-phase and β-solid solution with different distribution and volume fraction. Thus, the combination of powder particle characteristics, very short time material spends in molten condition and sluggish kinetics of mixing and diffusional process in Ti-Nb alloy results in heterogeneous microstructures depending on the local Nb content in the powder blend and the EBM® process conditions.
|
|
| 3. |
- Surmeneva, Maria, et al.
(författare)
-
Decreased bacterial colonization of additively manufactured Ti6Al4V metallic scaffolds with immobilized silver and calcium phosphate nanoparticles
- 2019
-
Ingår i: Applied Surface Science. - : Elsevier BV. - 0169-4332 .- 1873-5584. ; 480, s. 822-829
-
Tidskriftsartikel (refereegranskat)abstract
- The design of an ideal bone graft substitute has been a long-standing effort, and a number of strategies have been developed to improve bone regeneration. Electron beam melting (EBM) is an additive manufacturing method allowing for the production of porous implants with highly defined external dimensions and internal architectures. The increasing surface area of the implant may also increase the abilities of pathogenic microorganisms to adhere to the surfaces and form a biofilm, which may result in serious complications. The aim of this study was to explore the modifications of Ti6Al4V alloy scaffolds to reduce the abilities of bacteria to attach to the EBM-manufactured implant surface. The layers composed of silver (Ag), calcium phosphate (CaP) nanoparticles (NPs) and combinations of both were formed on the EBM-fabricated metallic scaffolds by electrophoretic deposition in order to provide them with antimicrobial properties. The assay of bacterial colonization on the surface was performed with the exposure of scaffold surfaces to Staphylococcus aureus cells for up to 17 h. Principal component analysis (PCA) was used to assess the relationships between different surface features of the studied samples and bacterial adhesion. The results indicate that by modifying the implant surface with appropriate nanostructures that change the hydrophobicity and the surface roughness at the nano scale, physical cues are provided that disrupt bacterial adhesion. Our results clearly show that AgNPs at a concentration of approximately 0.02 mg/сm 2 that were deposited together with CaPNPs covered by positively charge polyethylenimine (PEI) on the surface of EBM-sintered Ti6Al4V scaffolds hindered bacterial growth, as the total number of attached cells (NAC) of S. aureus remained at the same level during the 17 h of exposure, which indicates bacteriostatic activity.
|
|