- Olabarrieta, Idoia, et al.
(författare)
-
Aging properties of films of plasticized vital wheat gluten cast from acidic and basic solutions
- 2006
-
Ingår i: Biomacromolecules. - : American Chemical Society (ACS). - 1525-7797 .- 1526-4602. ; 7:5, s. 1657-1664
-
Tidskriftsartikel (refereegranskat)abstract
- In order to understand the mechanisms behind the undesired aging of films based on vital wheat gluten plasticized with glycerol, films cast from water/ethanol solutions were investigated. The effect of pH was studied by casting from solutions at pH 4 and pH 11. The films were aged for 120 days at 50% relative humidity and 23 C, and the tensile properties and oxygen and water vapor permeabilities were measured as a function of aging time. The changes in the protein structure were determined by infrared spectroscopy and size-exclusion and reverse-phase high-performance liquid chromatography, and the film structure was revealed by optical and scanning electron microscopy. The pH 11 film was mechanically more stable with time than the pH 4 film, the latter being initially very ductile but turning brittle toward the end of the aging period. The protein solubility and infrared spectroscopy measurements indicated that the protein structure of the pH 4 film was initially significantly less polymerized/ aggregated than that of the pH 11 film. The polymerization of the pH 4 film increased during storage but it did not reach the degree of aggregation of the pH 11 film. Reverse-phase chromatography indicated that the pH 11 films were to some extent deamidated and that this increased with aging. At the same time a large fraction of the aged pH 11 film was unaffected by reducing agents, suggesting that a time-induced isopeptide cross-linking had occurred. This isopeptide formation did not, however, change the overall degree of aggregation and consequently the mechanical properties of the film. During aging, the pH 4 films lost more mass than the pH 11 films mainly due to migration of glycerol but also due to some loss of volatile mass. Scanning electron and optical microscopy showed that the pH 11 film was more uniform in thickness and that the film structure was more homogeneous than that of the pH 4 film. The oxygen permeability was also lower for the pH 11 film. The fact that the pH 4 film experienced a larger and more rapid change in its mechanical properties with time than the pH 11 film, as a consequence of a greater loss of plasticizer, was presumably due to its initial lower degree of protein aggregation/ polymerization. Consequently, the cross-link density achieved at pH 4 was too low to effectively retain volatiles and glycerol within the matrix.
|
|
| 5. |
- Olabarrieta, Idoia, et al.
(författare)
-
Properties of new and aged montmorillonite-wheat gluten composite films
- 2006
-
Ingår i: Journal of Agricultural and Food Chemistry. - : American Chemical Society (ACS). - 0021-8561 .- 1520-5118. ; 54:4, s. 1283-1288
-
Tidskriftsartikel (refereegranskat)abstract
- The properties of new and aged glycerol-plasticized vital wheat gluten films containing ≤4.5 wt % natural or quaternary ammonium salt modified montmorillonite clay were investigated. The films were cast from pH 4 or pH 11 ethanol/water solutions. The films, aged for ≤120 days, were characterized by tensile testing, X-ray diffraction, and transmission electron microscopy. In addition, water vapor permeability (11% relative humidity) and the content of volatile components were measured. The large reduction in the water vapor permeability with respect to the pristine polymer suggests that the clay platelets were evenly distributed within the films and oriented preferably with the platelet long axis parallel to the film surface. The film prepared from pH 11 solution containing natural clay was, as revealed by transmission electron microscopy and X-ray diffraction, almost completely exfoliated. This film was consequently also the strongest, the stiffest, and the most brittle and, together with the pH 11 film containing modified clay, it also showed the greatest decrease in water vapor permeability. The large blocking effect of the clay had no effect on the aging kinetics of the films. During aging, the pH 4 and pH 11 film strength and the pH 4 film stiffness increased and the pH 4 film ductility decreased at the same rate with or without clay. This suggests that the aging was not diffusion rate limited, that is, that the loss of volatile components or the migration of glycerol or glycerol/wheat gluten phase separation was not limited by diffusion kinetics. The aging rate seemed to be determined by slow structural changes, possibly involving protein denaturation and aggregation processes.
|
|