1. |
- Hanning, Fabian, et al.
(författare)
-
The Effect of Grain Size on theSusceptibility Towards Strain Age Crackingof Wrought Haynes® 282®
- 2020
-
Ingår i: SPS 2020. - Amsterdam : IOS Press. - 9781643681467 - 9781643681474 ; 13, s. 407-416
-
Konferensbidrag (övrigt vetenskapligt/konstnärligt)abstract
- The effect of grain size on the suceptibility towards strain age cracking (SAC) has been investigated for Haynes® 282® in the tempeature range of 750 to 950°C after isothermal exposure up to 1800s. Grain growth was induced by heattreating the material at 1150°C for 2h, resulting in a fourfold increase in grain size. Hardness was significanlty reduced after heat treatment as compared to millannealed material. Large grain size resulted in intergranular fracture over a widertemperature range than small grain size material. Ductility was lowest at 850°C, while lower values were observed to be correlated to increased grain size. The rapid formation of grain boundary carbide networks in Haynes® 282® is found to be notable to compensate for higher local stresses on grain boundaries due to incresedgrain size.
|
|