| 1. |
- Hultin, Olof, et al.
(författare)
-
Simplifying Nanowire Hall Effect Characterization by Using a Three-Probe Device Design
- 2017
-
Ingår i: Nano letters (Print). - : American Chemical Society (ACS). - 1530-6984 .- 1530-6992. ; 17:2, s. 1121-1126
-
Tidskriftsartikel (refereegranskat)abstract
- Electrical characterization of nanowires is a time-consuming and challenging task due to the complexity of single nanowire device fabrication and the difficulty in interpreting the measurements. We present a method to measure Hall effect in nanowires using a three-probe device that is simpler to fabricate than previous four-probe nanowire Hall devices and allows characterization of nanowires with smaller diameter. Extraction of charge carrier concentration from the three-probe measurements using an analytical model is discussed and compared to simulations. The validity of the method is experimentally verified by a comparison between results obtained with the three-probe method and results obtained using four-probe nanowire Hall measurements. In addition, a nanowire with a diameter of only 65 nm is characterized to demonstrate the capabilities of the method. The three-probe Hall effect method offers a relatively fast and simple, yet accurate way to quantify the charge carrier concentration in nanowires and has the potential to become a standard characterization technique for nanowires.
|
|
| 2. |
- Anttu, Nicklas, et al.
(författare)
-
Crystal Phase-Dependent Nanophotonic Resonances in InAs Nanowire Arrays
- 2014
-
Ingår i: Nano Letters. - : American Chemical Society (ACS). - 1530-6992 .- 1530-6984. ; 14:10, s. 5650-5655
-
Tidskriftsartikel (refereegranskat)abstract
- Nanostructures have many material, electronic, and optical properties that are not found in bulk systems and that are relevant for technological applications. For example, nanowires realized from III-V semiconductors can be grown into wurtzite crystal structure. This crystal structure does not naturally exist in bulk where these materials form the zinc-blende counterpart. Being able to concomitantly grow these nanowires in the zinc-blende and/or wurtzite crystal structure prlovides an important degree of control for the design and optimization of optoelectronic applications based on these semiconductor nanostructures. However, the refractive indices of this new crystallographic phase have so far not been elucidated. This shortcoming makes it impossible to predict and utilize he full potential of these new nanostructured materials for optoelectronics applications a careful design and optimization of optical resonances by tuning the nanostrucuted geometry is needed to achieve optimal performance. Here, we report and analyze striking differeences in the optical response of nanophotonic resonances in wurtzite and zinc-blend InAs nanowire arrays. Specifically, through reflectance measurements we find that the resonance can be tuned down to lambda approximate to 380 nm in wurtzite nanowires by decreasing the nanowire diameter. In stark contrast, a similar tuning to below approximate to 500 nm is not possible in the zinc-blende nanowires. Furthermore, we find that the wurtzite nanowires can absorb twice as strongly as the zinc-blende nanowires. We attribute these strikingly large differences in resonant behavior to large differences between the refractive indices of the two crystallographic phases realized in these nanostructures. We anticipate our finding to be relevant for other III-B materials as well as for all material systems that manifest polytypism. Taken together, our results demonstrate crystal phase engineering as a potentially new design dimension for optoelectronics applications.
|
|
| 3. |
|
|
| 4. |
|
|
| 5. |
- Astromskas, Gvidas, et al.
(författare)
-
Doping Incorporation in InAs nanowires characterized by capacitance measurements
- 2010
-
Ingår i: Journal of Applied Physics. - : AIP Publishing. - 0021-8979 .- 1089-7550. ; 108
-
Tidskriftsartikel (refereegranskat)abstract
- Sn and Se doped InAs nanowires are characterized using a capacitance-voltage technique where the threshold voltages of nanowire capacitors with different diameter are determined and analyzed using an improved radial metal-insulator-semiconductor field-effect transistor model. This allows for a separation of doping in the core of the nanowire from the surface charge at the side facets of the nanowire. The data show that the doping level in the InAs nanowire can be controlled on the level between 2×1018 to 1×1019 cm−3, while the surface charge density exceeds 5×1012 cm−2 and is shown to increase with higher dopant precursor molar fraction.
|
|
| 6. |
- Astromskas, Gvidas, et al.
(författare)
-
Temperature and frequency characterization of InAs nanowire and HfO2 interface using capacitance-voltage method
- 2011
-
Ingår i: Microelectronic Engineering. - : Elsevier BV. - 1873-5568 .- 0167-9317. ; 88:4, s. 444-447
-
Konferensbidrag (refereegranskat)abstract
- InAs/HfO2 nanowire capacitors using capacitance-voltage (CV) measurements are investigated in the range of 10 kHz to 10 MHz. The capacitors are based on vertical nanowire arrays that are coated with an 8 nm-thick HfO2 layer by atomic layer deposition. CV characteristics are measured at temperatures in the range between -140 and 40 degrees C and the CV characteristics for nanowires with different Sn and Se n-type doping levels are compared. The comparison of the data at various doping levels points towards large number of traps for highly doped samples, caused by the preferential dopant precursor incorporation at the nanowire surface. We also evaluate the frequency dispersion of the accumulation capacitance and determine values below 2% with weak temperature dependence, indicating the existence of border traps in these nanowire capacitors. (C) 2010 Elsevier B.V. All rights reserved.
|
|
| 7. |
- Astromskas, Gvidas, et al.
(författare)
-
Transient studies on InAs/HfO2 nanowire capacitors
- 2011
-
Ingår i: Applied Physics Letters. - : AIP Publishing. - 0003-6951 .- 1077-3118. ; 98:1
-
Tidskriftsartikel (refereegranskat)abstract
- Single-shot transients and deep-level transient spectroscopy are used to investigate the origins of capacitance hysteresis in n-doped InAs nanowire/HfO2 capacitors. Capacitance transients with a characteristic time in the order of 100 mu s are attributed to emission from electron traps, located in the oxide film. The trap energy is determined to be in the range from 0.12 to 0.17 eV with capture cross-sections of about 1.7 x 10(-17) cm(-2). The capture is measured to be shorter than 100 ns with no sign of capture barrier. Under the reverse bias, the transients show a reduced emission rate indicating a minority carrier assisted complex dynamics. (C) 2011 American Institute of Physics. [doi:10.1063/1.3533379]
|
|
| 8. |
- Berg, Alexander, et al.
(författare)
-
Radial Nanowire Light-Emitting Diodes in the (AlxGa1-x)yIn1-yP Material System
- 2016
-
Ingår i: Nano letters (Print). - Washington, DC : American Chemical Society (ACS). - 1530-6984 .- 1530-6992. ; 16:1, s. 656-662
-
Tidskriftsartikel (refereegranskat)abstract
- Nanowires have the potential to play an important role for next-generation light-emitting diodes. In this work, we present a growth scheme for radial nanowire quantum-well structures in the AlGaInP material system using a GaInP nanowire core as a template for radial growth with GaInP as the active layer for emission and AlGaInP as charge carrier barriers. The different layers were analyzed by X-ray diffraction to ensure lattice-matched radial structures. Furthermore, we evaluated the material composition and heterojunction interface sharpness by scanning transmission electron microscopy energy dispersive X-ray spectroscopy. The electro-optical properties were investigated by injection luminescence measurements. The presented results can be a valuable track toward radial nanowire light-emitting diodes in the AlGaInP material system in the red/orange/yellow color spectrum. © 2015 American Chemical Society.
|
|
| 9. |
- Bi, Zhaoxia, et al.
(författare)
-
InGaN Platelets : Synthesis and Applications toward Green and Red Light-Emitting Diodes
- 2019
-
Ingår i: Nano Letters. - : American Chemical Society. - 1530-6984 .- 1530-6992. ; 19:5, s. 2832-2839
-
Tidskriftsartikel (refereegranskat)abstract
- In this work, we present a method to synthesize arrays of hexagonal InGaN submicrometer platelets with a top c-plane area having an extension of a few hundred nanometers by selective area metal-organic vapor-phase epitaxy. The InGaN platelets were made by in situ annealing of InGaN pyramids, whereby InGaN from the pyramid apex was thermally etched away, leaving a c-plane surface, while the inclined {101Ì1} planes of the pyramids were intact. The as-formed c-planes, which are rough with islands of a few tens of nanometers, can be flattened with InGaN regrowth, showing single bilayer steps and high-quality optical properties (full width at half-maximum of photoluminescence at room temperature: 107 meV for In 0.09 Ga 0.91 N and 151 meV for In 0.18 Ga 0.82 N). Such platelets offer surfaces having relaxed lattice constants, thus enabling shifting the quantum well emission from blue (as when grown on GaN) to green and red. For single InGaN quantum wells grown on the c-plane of such InGaN platelets, a sharp interface between the quantum well and the barriers was observed. The emission energy from the quantum well, grown under the same conditions, was shifted from 2.17 eV on In 0.09 Ga 0.91 N platelets to 1.95 eV on In 0.18 Ga 0.82 N platelets as a result of a thicker quantum well and a reduced indium pulling effect on In 0.18 Ga 0.82 N platelets. On the basis of this method, prototype light-emitting diodes were demonstrated with green emission on In 0.09 Ga 0.91 N platelets and red emission on In 0.18 Ga 0.82 N platelets.
|
|
| 10. |
- Borg, Mattias, et al.
(författare)
-
Geometric model for metalorganic vapour phase epitaxy of dense nanowire arrays
- 2013
-
Ingår i: Journal of Crystal Growth. - : Elsevier BV. - 0022-0248. ; 366, s. 15-19
-
Tidskriftsartikel (refereegranskat)abstract
- We propose a geometric model to estimate the contribution of substrate surface diffusion to growth of dense nanowire arrays using metalorganic vapour phase epitaxy. It is shown that the nanowire mantle area becomes the most significant collector of growth material when the nanowire diameter is large and the inter-nanowire pitch is small. It is concluded that this growth regime is important for the array geometries typically used for optoelectronic and photovoltaic applications of nanowires. The growth rate under these conditions is also not constant with time, due to the growing nanowire mantle area. This result was confirmed by experiments in which dense arrays of InAs nanowires were grown and the nanowire growth rate was measured as a function of time. (C) 2013 Elsevier B.V. All rights reserved.
|
|