| 1. |
- Davidsson, Kent, 1967, et al.
(författare)
-
Potassium, chlorine, and sulfur in ash, particles, deposits, and corrosion during wood combustion in a circulating fluidized-bed boiler
- 2007
-
Ingår i: Energy & Fuels. - : American Chemical Society (ACS). - 1520-5029 .- 0887-0624. ; 21:1, s. 71-81
-
Tidskriftsartikel (refereegranskat)abstract
- The effect of the addition of chlorine and/or sulfur to the fuel on fly ash composition, deposit formation, and superheater corrosion has been studied during biomass combustion in a circulating fluidized-bed boiler. The chlorine (HCl (aq)) and sulfur (SO2 (g)) were added in proportions of relevance for the potassium chemistry. The composition of the bottom and the fly ashes was analyzed. Gas and particle measurements were performed downstream of the cyclone before the convection pass and the flue gas composition was recorded in the stack with a series of standard instruments and an FTIR analyzer. At the position downstream of the cyclone, a deposit probe was situated, simulating a superheater tube. Deposits on the probe and initial corrosion were examined. It is concluded that addition of sulfur and chlorine increases the formation of submicron particles leading to deposition of potassium sulfate and chloride. The results compare well with earlier work based on laboratory-scale experiments concerning effects of chlorine and sulfur on potassium chemistry.
|
|
| 2. |
- Zamora, Juan Carlos, et al.
(författare)
-
Considerations and consequences of allowing DNA sequence data as types of fungal taxa
- 2018
-
Ingår i: IMA Fungus. - : INT MYCOLOGICAL ASSOC. - 2210-6340 .- 2210-6359. ; 9:1, s. 167-185
-
Tidskriftsartikel (refereegranskat)abstract
- Nomenclatural type definitions are one of the most important concepts in biological nomenclature. Being physical objects that can be re-studied by other researchers, types permanently link taxonomy (an artificial agreement to classify biological diversity) with nomenclature (an artificial agreement to name biological diversity). Two proposals to amend the International Code of Nomenclature for algae, fungi, and plants (ICN), allowing DNA sequences alone (of any region and extent) to serve as types of taxon names for voucherless fungi (mainly putative taxa from environmental DNA sequences), have been submitted to be voted on at the 11th International Mycological Congress (Puerto Rico, July 2018). We consider various genetic processes affecting the distribution of alleles among taxa and find that alleles may not consistently and uniquely represent the species within which they are contained. Should the proposals be accepted, the meaning of nomenclatural types would change in a fundamental way from physical objects as sources of data to the data themselves. Such changes are conducive to irreproducible science, the potential typification on artefactual data, and massive creation of names with low information content, ultimately causing nomenclatural instability and unnecessary work for future researchers that would stall future explorations of fungal diversity. We conclude that the acceptance of DNA sequences alone as types of names of taxa, under the terms used in the current proposals, is unnecessary and would not solve the problem of naming putative taxa known only from DNA sequences in a scientifically defensible way. As an alternative, we highlight the use of formulas for naming putative taxa (candidate taxa) that do not require any modification of the ICN.
|
|
| 3. |
- Alnegren, Patrik, 1988, et al.
(författare)
-
Inhibiting chromium evaporation and oxide scale growth on SOFC metallic interconnects by nano coatings
- 2014
-
Ingår i: 20th World Hydrogen Energy Conference, WHEC 2014. - 9780000000002 ; 1:2014
-
Konferensbidrag (refereegranskat)abstract
- High chromium ferritic steel is today the most commonly considered material for SOFC interconnectors due to many desirable properties, such as matching thermal expansion coefficient with other cell components but most importantly better machinability and price compared to ceramic alternatives. Yet there are some obstacles that need to be addressed before long term stability of a ferritic steel interconnector based fuel cell stack can be realized. First of all the electrical conductivity needs to remain high throughout the fuel cell stack operating life time and thus the formed oxide layers need to be electrically conductive and thin. Secondly, volatilization of chromium from the oxide scale of metallic interconnects causes rapid degradation due cathode poisoning. In the current study both oxidation and chromium evaporation of ferritic steel substrates are investigated in controlled atmospheres that simulates the environments of an operating SOFC stack. Samples coated with nanometer scale dual coatings of Co and Ce were tested. The dual coating substantially increased the performance of the ferritic substrates by i) significantly reducing oxidation rate, ii) increasing scale adherence and iii) diminishing chromium evaporation by 90 % via the formation of a Co-Mn-spinel cap layer.
|
|
| 4. |
- Canovic, Sead, 1979, et al.
(författare)
-
Oxidation of Co- and Ce-nanocoated FeCr steels: A microstructural investigation
- 2013
-
Ingår i: Surface and Coatings Technology. - : Elsevier BV. - 0257-8972. ; 215, s. 62-74
-
Tidskriftsartikel (refereegranskat)abstract
- The effect of novel Co and Ce nanocoatings on oxidation behaviour and chromium volatilization from a commercial Fe-22Cr steel (Sanergy HT) developed for solid oxide fuel cell interconnect applications is investigated. Three different coatings (10 nm Ce, 640 nm Co and 10 nm Ce + 640 nm Co) are studied. Uncoated and nanocoated samples are exposed isothermally at 850 C in the air with 3% H2O for 168 h. The detailed microstructure of the different coatings is investigated. The surface morphology and microstructure of the oxide scales are characterized by using scanning electron microscopy (SEM), transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM) and energy dispersive X-ray analysis (EDX). Cross-section TEM thin foils are prepared by using a combined FIB/SEM (focused ion beam/scanning electron microscope) instrument. A 640 nm cobalt coating strongly inhibits Cr volatilization but has only minor effects on oxidation rate. In contrast, a 10 nm Ce coating decreases the oxidation rate but has no significant effects on chromium volatilization. Combining the two coatings, i.e., applying a 640 nm Co coating on top of the 10 nm Ce, effectively reduces Cr evaporation and slows down the rate of alloy oxidation.
|
|
| 5. |
- Froitzheim, Jan, 1981, et al.
(författare)
-
Chromium evaporation of Coated and uncoated FE-22CR steels investigated by a novel denuder technique
- 2009
-
Ingår i: 3rd European Fuel Cell Technology and Applications - Piero Lunghi Conference, EFC 2009; Rome; Italy; 15 December 2009 through 18 December 2009. - 9788882862114 ; , s. 77-78
-
Konferensbidrag (refereegranskat)abstract
- The formation of volatile chromium species is a major problem concerning metallic interconnects for Solid Oxide Fuel Cells (SOFC). This problem is known and a number of routes, usually in the form of coatings, has been presented to overcome this problem. This paper investigates the influence of thin metallic films which can be applied by a low cost process. The measurements are carried out by a novel denuder technique where volatile chromium species are collected as sodium chromate. This technique allows the quantification of chromium evaporation in a time resolved manner. Coated and uncoated samples of ferritic steels developed for SOFC applications are investigated at 850°C in a N2-O2-H2O environment.
|
|
| 6. |
- Froitzheim, Jan, 1981, et al.
(författare)
-
Cr evaporation of metallic interconnects: A novel method for quantification
- 2009
-
Ingår i: ECS Transactions. - : The Electrochemical Society. - 1938-5862 .- 1938-6737. - 9781566777391 ; 25:2 PART 2, s. 1423-1428
-
Konferensbidrag (refereegranskat)abstract
- Chromium evaporation from metallic interconnects in SOFCs is commonly poisoning the cathode of SOFCs. To reduce chromium evaporation, rather thick coatings have been deposited using various coating techniques. In this study, a 22% Cr ferritic steel has been coated with thin films (
|
|
| 7. |
- Froitzheim, Jan, 1981, et al.
(författare)
-
Investigation of Chromium Volatilization from FeCr Interconnects by a Denuder Technique
- 2010
-
Ingår i: Journal of the Electrochemical Society. - : The Electrochemical Society. - 1945-7111 .- 0013-4651. ; 157:9, s. B1295-B1300
-
Tidskriftsartikel (refereegranskat)abstract
- A technique is presented for accurate and time-resolved quantification of chromium volatilization from alloys at high temperature. A denuder tube which is coated with Na2CO3 is placed downstream of the samples. CrO2(OH)(2) that evaporated from the samples is collected on the denuder and converted to the thermally stable Na2CrO4. The chromate is then dissolved in water and determined quantitatively. Three commercially available ferritic 22% Cr steels intended for use as solid oxide fuel cell interconnect materials (Sanergy HT, Crofer 22 APU, and ZMG 232) have been investigated with respect to chromium volatilization and oxidation rate. The effect on chromium volatilization of a submicrometer cobalt coating on the steel surface is reported. Comparisons are made with a conventional thick ceramic coating. The experiments are carried out at 850 degrees C in N-2 - 20% O-2 - 3% H2O atmosphere. The submicrometer Co coatings proved to be very efficient, reducing Cr volatilization by 1 order of magnitude. Microscopic studies show that both uncoated steel and steel coated with a submicrometer cobalt film develop two-layered oxide scales with the bottom part consisting of a Cr-rich corundum-type oxide. The uncoated samples develop a top layer consisting of (Cr, Mn)(3)O-4 oxide, whereas the Co-coated samples exhibit a top layer consisting of Co-rich spinel oxide. (C) 2010 The Electrochemical Society. [DOI: 10.1149/1.3462987] All rights reserved.
|
|
| 8. |
- Grolig, Jan Gustav, 1986, et al.
(författare)
-
Coated stainless steel 441 as interconnect material for solid oxide fuel cells: Evolution of electrical properties
- 2015
-
Ingår i: Journal of Power Sources. - : Elsevier BV. - 0378-7753. ; 284, s. 321-327
-
Tidskriftsartikel (refereegranskat)abstract
- AISI 441 coated. with a double layer coating of 10 nm cerium (inner layer) and 630 nm cobalt was investigated and in addition the uncoated material was exposed for comparison. The main purpose of this investigation was the development of a suitable ASR characterization method. The material was exposed to a simulated cathode atmosphere of air with 3% water at 850 degrees C and the samples were exposed for up to 1500 h. We compared two methods of ASR measurements, an in-situ method where samples were measured with platinum electrodes for longer exposure times and an ex-situ method where pre-oxidized samples were measured for only very short measurement times. It was found that the ASR of ex-situ characterized samples could be linked to the mass gain and the electrical properties could be linked to the evolving microstructure during the different stages of exposure. Both the degradation of the electric performance and the oxygen uptake (mass gain) followed similar trends. After about 1500 h of exposure an ASR value of about 15 m Omega cm(2) was reached. The in-situ measured samples suffered from severe corrosion attack during measurement. After only 500 h of exposure already a value of 35 m Omega cm(2) was obtained.
|
|
| 9. |
- Grolig, Jan Gustav, 1986, et al.
(författare)
-
Coated stainless steel 441 as interconnect material for solid oxide fuel cells: Oxidation performance and chromium evaporation
- 2014
-
Ingår i: Journal of Power Sources. - : Elsevier BV. - 0378-7753. ; 248, s. 1007-1013
-
Tidskriftsartikel (refereegranskat)abstract
- Reactive Element (RE) and RE/cobalt-coated stainless steel AISI 441 was exposed at Solid Oxide Fuel Cell (SOFC) cathode conditions (850 degrees C in air with 3% water content) for up to 500 h. The chromium evaporation was measured by applying the denuder technique. Uncoated material exhibited severe spallation which could be successfully prevented by using cerium or lanthanum coatings. By applying double layer coatings of cerium or lanthanum in combination with cobalt the oxidation rate was decreased and the chromium volatilisation was also about 90% lower than the uncoated material.
|
|
| 10. |
- Grolig, Jan Gustav, 1986, et al.
(författare)
-
Copper based conversion coatings on ferritic stainless strip steel as solid oxide fuel cell interconnects: Oxidation performance and chromium evaporation
- 2013
-
Ingår i: ECS Transactions. - : The Electrochemical Society. - 1938-5862 .- 1938-6737. ; 57:1, s. 2339-2347
-
Konferensbidrag (refereegranskat)abstract
- Ferritic stainless steels such as Crofer 22 H or Sanergy HT have been proven to be effective interconnect materials when additionally coated. These coatings, mainly based on cobalt spinels, successfully prevent chromium evaporation and are stable for long exposure times. A new approach is using copper based spinel coatings which are promising concerning price, conductivity and stability. This investigation is dedicated to a selection of copper spinel conversion coatings, their stability and ability to prevent chromium evaporation. Chromium release was monitored in humidified air (at 850 °C) using the denuder technique. The coatings were post analysed utilizing electron microscopy.
|
|