| 1. |
- Andriollo, Tito, et al.
(författare)
-
Uncovering the local inelastic interactions during manufacture of ductile cast iron : How the substructure of the graphite particles can induce residual stress concentrations in the matrix
- 2018
-
Ingår i: Journal of the mechanics and physics of solids. - : Elsevier. - 0022-5096 .- 1873-4782. ; 111, s. 333-357
-
Tidskriftsartikel (refereegranskat)abstract
- Recent X-ray diffraction (XRD) measurements have revealed that plastic deformation and a residual elastic strain field can be present around the graphite particles in ductile cast iron after manufacturing, probably due to some local mismatch in thermal contraction. However, as only one component of the elastic strain tensor could be obtained from the XRD data, the shape and magnitude of the associated residual stress field have remained unknown. To compensate for this and to provide theoretical insight into this unexplored topic, a combined experimental-numerical approach is presented in this paper. First, a material equivalent to the ductile cast iron matrix is manufactured and subjected to dilatometric and high-temperature tensile tests. Subsequently, a two-scale hierarchical top-down model is devised, calibrated on the basis of the collected data and used to simulate the interaction between the graphite particles and the matrix during manufacturing of the industrial part considered in the XRD study. The model indicates that, besides the viscoplastic deformation of the matrix, the effect of the inelastic deformation of the graphite has to be considered to explain the magnitude of the XRD strain. Moreover, the model shows that the large elastic strain perturbations recorded with XRD close to the graphite–matrix interface are not artifacts due to e.g. sharp gradients in chemical composition, but correspond to residual stress concentrations induced by the conical sectors forming the internal structure of the graphite particles. In contrast to common belief, these results thus suggest that ductile cast iron parts cannot be considered, in general, as stress-free at the microstructural scale.
|
|
| 2. |
- Liu, Qiang, 1985-
(författare)
-
Microstructure Evaluation and Wear-Resistant Properties of Ti-alloyed Hypereutectic High Chromium Cast Iron
- 2013
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- High chromium cast iron (HCCI) is considered as one of the most useful wear resistance materials and their usage are widely spread in industry. The mechanical properties of HCCI mainly depend on type, size, number, morphology of hard carbides and the matrix structure (γ or α). The hypereutectic HCCI with large volume fractions of hard carbides is preferred to apply in wear applications. However, the coarser and larger primary M7C3 carbides will be precipitated during the solidification of the hypereutectic alloy and these will have a negative influence on the wear resistance.In this thesis, the Ti-alloyed hypereutectic HCCI with a main composition of Fe-17mass%Cr-4mass%C is studied based on the experimental results and calculation results. The type, size distribution, composition and morphology of hard carbides and martensite units are discussed quantitatively. For a as-cast condition, a 11.2μm border size is suggested to classify the primary M7C3 carbides and eutectic M7C3 carbides. Thereafter, the change of the solidification structure and especially the refinement of carbides (M7C3 and TiC) size by changing the cooling rates and Ti addition is determined and discussed. Furthermore, the mechanical properties of hypereutectic HCCI related to the solidification structure are discussed.Mechanical properties of HCCI can normally be improved by a heat treatment process. The size distribution and the volume fraction of carbides (M7C3 and TiC) as well as the matrix structure (martensite) were examined by means of scanning electron microscopy (SEM), in-situ observation by using Confocal Laser Scanning Microscope (CLSM), Transmission electron microscopy (TEM) and electron backscattered diffraction (EBSD). Especially for the matrix structure and secondary M7C3 carbides, EBSD and CLSM are useful tools to classify the fcc (γ) and bcc (α) phases and to study the dynamic behavior of secondary M7C3 carbides. In conclusion, low holding temperatures close to the eutectic temperature and long holding times are the best heat treatment strategies in order to improve wear resistance and hardness of Ti-alloyed hypereutectic HCCI.Finally, the maximum carbides size is estimated by using statistics of extreme values (SEV) method in order to complete the size distribution results. Meanwhile, the characteristic of different carbides types will be summarized and classified based on the shape factor.
|
|