1.
  • Venkatesh, Lakshmi Narayanan, et al. (författare)
  • Morphology-Dependent Hardness of Cr7C3-Ni-Rich Alloy Composite vs Orientation Independent Hardness of Cr7C3 Primary Phase in a Laser Clad Microstructure
  • 2017
  • Ingår i: Metallurgical and Materials Transactions. A. - : Springer Science and Business Media LLC. - 1073-5623 .- 1543-1940. ; 48A:4, s. 1534-1539
  • Tidskriftsartikel (refereegranskat)abstract
    • Microstructural evolution with superheating was studied in chromium carbide-nickel coatings deposited by laser cladding. At lower superheating, selective growth of aOE (c) 0001 > direction from the high density of Cr7C3 grains nucleated resulted in a columnar structure with (0001) texture. Increased superheating lead to the loss of columnar structure as well as the (0001) texture. The hexagonal Cr7C3 showed an unusual isotropic nanoindentation hardness evidently correlated with its low c/a ratio. However, the rod-like morphology of the carbide dendrites resulted in significant anisotropy in the hardness of the composite.
  •  
2.
  • Venkatesh, Lakshmi Narayanan, et al. (författare)
  • Room temperature and 600 °C erosion behaviour of various chromium carbide composite coatings
  • 2019
  • Ingår i: Wear. - : Elsevier BV. - 0043-1648 .- 1873-2577. ; 422-423, s. 44-53
  • Tidskriftsartikel (refereegranskat)abstract
    • In this study, the erosion behaviour of laser clad chromium carbide-Ni rich alloy composite coatings with a wide range of carbide contents at room temperature and 600 °C were investigated. The variation in carbide content of the coatings was due to dilution from the substrate and the high cooling rate in the laser cladding process preventing re-solidification of the molten carbides. Erosion rate was observed to be a function of carbide content alone and was significantly higher at 600 °C as compared to room temperature. Erosion wear ratio (E90/E30) was also dependent on carbide content but decreased at higher temperature and higher carbide contents. A comparison of erosion behaviour with detonation and plasma sprayed counterparts showed the superior performance of laser clad coatings at 600 °C. The poor erosion performance of the detonation and plasma sprayed coatings was due to weak splat bonding. Thick oxide layer formed on the steel substrate after pre-oxidation resulted in its poor erosion performance.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-2 av 2

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy