| 1. |
- Akansel, Serkan, et al.
(författare)
-
Effect of seed layers on dynamic and static magnetic properties of Fe65Co35 thin films
- 2018
-
Ingår i: Journal of Physics D. - : IOP Publishing. - 0022-3727 .- 1361-6463. ; 51:30
-
Tidskriftsartikel (refereegranskat)abstract
- Fe65Co35 thin films have been deposited on SiO2 substrates using sputtering technique with different choices of seed layer; Ru, Ni82.5Fe17.5, Rh, Y and Zr. Best soft magnetic properties were observed with seed layers of Ru, Ni82.5Fe17.5 and Rh. Adding these seed layers, the coercivity of the Fe65Co35 films decreased to values of around 1.5 mT, which can be compared to the value of 12.5 mT obtained for films deposited without seed layer. Further investigations were performed on samples with these three seed layers in terms of dynamic magnetic properties, both on as prepared and annealed samples, using constant frequency cavity and broadband ferromagnetic resonance measurements. Damping parameters of around 8.0X10-3 and 4.5X10-3 were obtained from in-plane and out-of-plane measurements, respectively, for as prepared samples, values that were reduced to 6.5X10-3 and 4.0X10-3 for annealed samples.
|
|
| 2. |
- Akansel, Serkan, et al.
(författare)
-
Enhanced Gilbert damping in Re-doped FeCo films : Combined experimental and theoretical study
- 2019
-
Ingår i: Physical Review B. - 2469-9950 .- 2469-9969. ; 99:17
-
Tidskriftsartikel (refereegranskat)abstract
- The effects of rhenium doping in the range 0-10 at.% on the static and dynamic magnetic properties of Fe65Co35 thin films have been studied experimentally as well as with first-principles electronic structure calculations focusing on the change of the saturation magnetization (M-s) and the Gilbert damping parameter (alpha). Both experimental and theoretical results show that M-s decreases with increasing Re-doping level, while at the same time alpha increases. The experimental low temperature saturation magnetic induction exhibits a 29% decrease, from 2.31 to 1.64 T, in the investigated doping concentration range, which is more than predicted by the theoretical calculations. The room temperature value of the damping parameter obtained from ferromagnetic resonance measurements, correcting for extrinsic contributions to the damping, is for the undoped sample 2.1 x 10(-3), which is close to the theoretically calculated Gilbert damping parameter. With 10 at.% Re doping, the damping parameter increases to 7.8 x 10(-3), which is in good agreement with the theoretical value of 7.3 x 10(-3). The increase in damping parameter with Re doping is explained by the increase in the density of states at the Fermi level, mostly contributed by the spin-up channel of Re. Moreover, both experimental and theoretical values for the damping parameter weakly decrease with decreasing temperature.
|
|
| 3. |
- Akansel, Serkan, et al.
(författare)
-
Enhanched Gilbert Damping in Re doped FeCo Films : A combined experimental and theoretical study
-
Annan publikation (övrigt vetenskapligt/konstnärligt)abstract
- The effects of rhenium doping in the range 0 – 10 at% on the static and dynamic magnetic properties of Fe65Co35 thin films have been studied experimentally as well as with first principles electronic structure calculations focussing on the change of the saturation magnetization (Ms ) and the Gilbert damping parameter (α ). Both experimental and theoretical results show that Ms decreases with increasing Re doping level, while at the same time α increases. The experimental low temperature saturation magnetic induction exhibits a 29% decrease, from 2.31T to 1.64T, in the investigated doping concentration range, which is more than predicted by the theoretical calculations. The room temperature value of the damping parameter obtained from ferromagnetic resonance measurements, correcting for extrinsic contributions to the damping, is for the undoped sample 2.7X103, which is close to the Gilbert damping parameter extracted from the theoretical calculations. The room temperature experimental value for the damping parameter increases to 9X103 when doping with 10 at% Re; the corresponding increase of the Gilbert damping parameter obtained from theoretical calculations is 7.3X103. Both experimental and theoretical values for the damping parameter weakly decrease with decreasing temperature.
|
|