| 1. |
- Wachsmuth, Josua, et al.
(författare)
-
Overcoming Moisture-Induced Degradation in Organic Solar Cells
- 2023
-
Ingår i: Advanced Engineering Materials. - : John Wiley & Sons. - 1438-1656 .- 1527-2648. ; , s. 1-7
-
Tidskriftsartikel (refereegranskat)abstract
- Unencapsulated organic solar cells are prone to severe performance losses in the presence of moisture. Accelerated damp heat (85 °C/85% RH) studies are presented and it is shown that the hygroscopic hole-transporting PEDOT:PSS layer is the origin of device failure in the case of prototypical inverted solar cells. Complementary measurements unveil that under these conditions a decreased PEDOT:PSS work function along with areas of reduced electrical contact between active layer and hole-transport layer are the main factors for device degradation rather than a chemical reaction of water with the active layer. Replacements for PEDOT:PSS are explored and it is found that tungsten oxide (WO3) or phosphomolybdic acid (PMA)—materials that can be processed from benign solvents at room temperature—yields comparable performance as PEDOT:PSS and enhances the resilience of solar cells under damp heat. The stability trend follows the order PEDOT:PSS << WO3 < PMA, with PEDOT:PSS-based devices failing after few minutes, while PMA-based devices remain nearly pristine over several hours. PMA is thus proposed as a robust, solution-processable hole extraction layer that can act as a one to one replacement of PEDOT:PSS to achieve organic solar cells with significantly improved longevity.
|
|