| 1. |
- Afewerki, Samson, et al.
(författare)
-
Combined Catalysis for Engineering Bioinspired, Lignin-Based, Long-Lasting, Adhesive, Self-Mending, Antimicrobial Hydrogels
- 2020
-
Ingår i: ACS Nano. - : American Chemical Society (ACS). - 1936-0851 .- 1936-086X. ; 14:12, s. 17004-17017
-
Tidskriftsartikel (refereegranskat)abstract
- The engineering of multifunctional biomaterials using a facile sustainable methodology that follows the principles of green chemistry is still largely unexplored but would be very beneficial to the world. Here, the employment of catalytic reactions in combination with biomass-derived starting materials in the design of biomaterials would promote the development of eco-friendly technologies and sustainable materials. Herein, we disclose the combination of two catalytic cycles (combined catalysis) comprising oxidative decarboxylation and quinone-catechol redox catalysis for engineering lignin-based multifunctional antimicrobial hydrogels. The bioinspired design mimics the catechol chemistry employed by marine mussels in nature. The resultant multifunctional sustainable hydrogels (1) are robust and elastic, (2) have strong antimicrobial activity, (3) are adhesive to skin tissue and various other surfaces, and (4) are able to self-mend. A systematic characterization was carried out to fully elucidate and understand the facile and efficient catalytic strategy and the subsequent multifunctional materials. Electron paramagnetic resonance analysis confirmed the long-lasting quinone-catechol redox environment within the hydrogel system. Initial in vitro biocompatibility studies demonstrated the low toxicity of the hydrogels. This proof-of-concept strategy could be developed into an important technological platform for the eco-friendly, bioinspired design of other multifunctional hydrogels and their use in various biomedical and flexible electronic applications.
|
|
| 2. |
- Basu, Alex, et al.
(författare)
-
Ion-crosslinked wood-derived nanocellulose hydrogels with tunable antibacterial properties : Candidate materials for advanced wound care applications
- 2018
-
Ingår i: Carbohydrate Polymers. - : Elsevier BV. - 0144-8617 .- 1879-1344. ; 181, s. 345-350
-
Tidskriftsartikel (refereegranskat)abstract
- Development of advanced dressings with antimicrobial properties for the treatment of infected wounds is an important approach in the fight against evolution of antibiotic resistant bacterial strains. Herein, the effects of ion-crosslinked nanocellulose hydrogels on bacteria commonly found in infected wounds were investigated in vitro. By using divalent calcium or copper ions as crosslinking agents, different antibacterial properties against the bacterial strains Staphylococcus epidermidis and Pseudomonas aeruginosa were obtained. Calcium crosslinked hydrogels were found to retard S. epidermidis growth (up to 266% increase in lag time, 36% increase in doubling time) and inhibited P. aeruginosa biofilm formation, while copper crosslinked hydrogels prevented S. epidermidis growth and were bacteriostatic towards P. aeruginosa (49% increase in lag time, 78% increase in doubling time). The wound dressing candidates furthermore displayed barrier properties towards both S. epidermidis and P. aeruginosa, hence making them interesting for further development of advanced wound dressings with tunable antibacterial properties.
|
|
| 3. |
|
|
| 4. |
|
|
| 5. |
- Hulsart Billström, Gry, 1982-, et al.
(författare)
-
Thromboinflammation as bioactivity assessment of H2O2-alkali modified titanium surfaces
- 2019
-
Ingår i: Journal of materials science. Materials in medicine. - : Springer Science and Business Media LLC. - 0957-4530 .- 1573-4838. ; 30:6
-
Tidskriftsartikel (refereegranskat)abstract
- The release of growth factors from platelets, mediated by the coagulation and the complement system, plays an important role in the bone formation around implants. This study aimed at exploring the thromboinflammatory response of H2O2-alkali soaked commercially pure titanium grade 2 discs exposed to whole human blood, as a way to assess the bioactivity of the discs. Commercially pure titanium grade 2 discs were modified by soaking in H2O2, NaOH and Ca(OH)2. The platelet aggregation, coagulation activation and complement activation was assessed by exposing the discs to fresh whole blood from human donors. The platelet aggregation was examined by a cell counter and the coagulation and complement activation were assessed by ELISA-measurements of the concentration of thrombin-antithrombin complex, C3a and terminal complement complex. The modified surface showed a statistically significant increased platelet aggregation, coagulation activation and complement activation compared to unexposed blood. The surface also showed a statistically significant increase of coagulation activation compared to PVC. The results of this study showed that the H2O2-alkali soaked surfaces induced a thromboinflammatory response that indicates that the surfaces are bioactive.
|
|
| 6. |
- Janson, Oscar, et al.
(författare)
-
Debridement of Bacterial Biofilms with TiO2/H2O2 Solutions and Visible Light Irradiation
- 2018
-
Ingår i: International Journal of Biomaterials. - : Hindawi Publishing Corporation. - 1687-8787 .- 1687-8795. ; 2018
-
Tidskriftsartikel (refereegranskat)abstract
- Objectives. The aim of the study was to explore the debridement efficacy of different solutions of H2O2 and rutile particles against Staphylococcus epidermidis and Pseudomonas aeruginosa biofilms attached to titanium surfaces when exposed to visible light. Materials and Methods. Titanium discs cultivated with biofilms of Staphylococcus epidermidis or Pseudomonas aeruginosa were subjected for 1 min to suspensions consisting of rutile particles mixed with high (950 mM) or low (2 mM) concentrations of H2O2 under visible light irradiation (405 nm; 2.1 mW/cm2). Discs were rinsed and the degree of debridement was determined through scanning electron microscopy and viability assessment of the remaining bacteria using luminescence measurements and/or a metabolic activity assay. Results. Cleaning mixtures containing the higher concentration of H2O2 showed a significantly improved debridement compared to the negative control in all experiments. The addition of rutile particles was shown to have a statistically significant effect in one test with S. epidermidis. Limited evidence of the catalytic effect of visible light irradiation was seen, but effects were relatively small and statistically insignificant. Conclusions. H2O2 at a concentration of 950 mM proved to be the strongest contribution to the debridement and bactericidal effect of the cleaning techniques tested in this study.
|
|
| 7. |
|
|
| 8. |
- Janson, Oscar, et al.
(författare)
-
Evaluation of an alkali-treated and hydroxyapatite-coated orthopedic implant loaded with tobramycin
- 2019
-
Ingår i: Journal of biomaterials applications. - : SAGE Publications. - 0885-3282 .- 1530-8022. ; 34:5, s. 699-720
-
Tidskriftsartikel (refereegranskat)abstract
- An approximately 1-µm thick hydroxyapatite coating was biomimetically deposited on an alkali-treated, commercially available orthopedic screw surface (type II anodized titanium). Tobramycin loaded into the coating via a simple soaking method was shown to provide a sustained release above the minimal inhibitory concentration 0.2 µg/µl for up to two days. Agar diffusion tests showed that the tobramycin-loaded coating was able to produce a zone of inhibition against Staphylococcus aureus for up to five days. Biocompatibility testing using outgrowth endothelial cells and primary osteoblasts suggested that good cell compatibility of the coating can be expected in vivo. A rabbit distal femur condyle model was used for in vivo evaluation of the antibacterial efficacy of the tobramycin-loaded coating, and this pilot study showed that the release of tobramycin was sufficient to locally eliminate very large amounts of bacteria in vivo (inoculation dose 104–105 CFU S. aureus/test site).
|
|
| 9. |
- Janson, Oscar, et al.
(författare)
-
Organic degradation potential of a TiO2/H2O2/UV-Vis system for dental applications
- 2017
-
Ingår i: Journal of Dentistry. - : Elsevier BV. - 0300-5712 .- 1879-176X. ; 67, s. 53-57
-
Tidskriftsartikel (refereegranskat)abstract
- ObjectivesThe combination of TiO2 and H2O2 under light activation constitutes a promising method for disinfection of dental prosthetics and implants, due to production of reactive oxygen species (ROS). The aim of this work was to investigate the organic degradation ability of TiO2 particles in combination with H2O2 and under light activation utilizing the organic dye rhodamine B (RhB).MethodsFive different types of TiO2 particles, consisting of anatase, rutile, or a mixture of these crystalline phases, were combined with H2O2 and RhB, and subsequently exposed to UV (365 nm) or visible (405 nm) light at an irradiance of 2.1 mW/cm2.ResultsIt was found that rutile in combination with low concentrations of H2O2 (1.0–3.5 mM) resulted in a degradation of RhB of 96% and 77% after 10 min exposure to 365 nm and 405 nm light, respectively, which was the highest degradation of all test groups. Control measurements performed without light irradiation or irradiation at 470 nm, or without TiO2 particles resulted in little or no degradation of RhB.ConclusionsLow H2O2 concentrations (1.0 mM–3.5 mM) and visible light (405 nm) used in combination with rutile TiO2 particles showed the highest RhB degradation capacity.Clinical significanceA combination of TiO2 particles and H2O2 exposed to low energy UV or high energy visible light has an organic degradation capability that could be utilized in applications to kill or inactivate bacteria on medical devices such as dental implants for treatment against, e.g., peri-implantitis.
|
|
| 10. |
- Janson, Oscar, et al.
(författare)
-
Titanium surface modification to enhance antibacterial and bioactive properties while retaining biocompatibility
- 2019
-
Ingår i: Materials science & engineering. C, biomimetic materials, sensors and systems. - : Elsevier BV. - 0928-4931 .- 1873-0191. ; 96, s. 272-279
-
Tidskriftsartikel (refereegranskat)abstract
- Bacterial infections associated with metal implants are severe problems affecting a considerable amount of people with dental or orthopedic implants. This study aims to examine the antibacterial effect of a Titanium-peroxy gel layer on the modified surface of commercially pure titanium grade 2. Variations in a multi-step surface modification procedure were tested to determine the best combination that provided an antibacterial effect while enhancing bioactivity without compromising biocompatibility. Soaking the surfaces in 30 wt% hydrogen peroxide held at 80 °C provided antibacterial activity while subsequent surface treatments in concentrated sodium and calcium hydroxide solutions were preformed to enhance bioactivity. Staphylococcus epidermidis was used to determine the antibacterial effect through both direct contact and biofilm inhibition tests while human dermal fibroblast cells and MC3T3 pre osteoblast cells were utilized to test biocompatibility. The greatest antibacterial effect was observed with only hydrogen peroxide treatment, but the resulting surface was neither bioactive nor biocompatible. It was found that subsequent surface treatments with sodium hydroxide followed by calcium hydroxide provided a bioactive surface that was also biocompatible. Additionally, a final treatment with autoclaving showed positive effects with regards to enhanced bioactivity. This multi-step surface modification procedure offers a promising, non-antibiotic, solution for combatting infections associated with biomedical implants.
|
|