1. |
- Abelev, B, et al.
(författare)
-
Directed Flow of Charged Particles at Midrapidity Relative to the Spectator Plane in Pb-Pb Collisions at sqrt[s_{NN}]=2.76 TeV.
- 2013
-
Ingår i: Physical Review Letters. - 1079-7114. ; 111:23
-
Tidskriftsartikel (refereegranskat)abstract
- The directed flow of charged particles at midrapidity is measured in Pb-Pb collisions at sqrt[s_{NN}]=2.76 TeV relative to the collision symmetry plane defined by the spectator nucleons. A negative slope of the rapidity-odd directed flow component with approximately 3 times smaller magnitude than found at the highest RHIC energy is observed. This suggests a smaller longitudinal tilt of the initial system and disfavors the strong fireball rotation predicted for the LHC energies. The rapidity-even directed flow component is measured for the first time with spectators and found to be independent of pseudorapidity with a sign change at transverse momenta p_{T} between 1.2 and 1.7 GeV/c. Combined with the observation of a vanishing rapidity-even p_{T} shift along the spectator deflection this is strong evidence for dipolelike initial density fluctuations in the overlap zone of the nuclei. Similar trends in the rapidity-even directed flow and the estimate from two-particle correlations at midrapidity, which is larger by about a factor of 40, indicate a weak correlation between fluctuating participant and spectator symmetry planes. These observations open new possibilities for investigation of the initial conditions in heavy-ion collisions with spectator nucleons.
|
|
2. |
- Abelev, B., et al.
(författare)
-
Multiplicity dependence of two-particle azimuthal correlations in pp collisions at the LHC
- 2013
-
Ingår i: Journal of High Energy Physics. - 1029-8479. ; :9
-
Tidskriftsartikel (refereegranskat)abstract
- We present the measurements of particle pair yields per trigger particle obtained from di-hadron azimuthal correlations in pp collisions at root s = 0.9, 2.76, and 7TeV recorded with the ALICE detector. The yields are studied as a function of the charged particle multiplicity. Taken together with the single particle yields the pair yields provide information about parton fragmentation at low transverse momenta, as well as on the contribution of multiple parton interactions to particle production. Data are compared to calculations using the PYTHIA6, PYTHIA8, and PHOJET event generators.
|
|
3. |
|
|
4. |
- Nilsson, M, et al.
(författare)
-
Biodegradation and biocompatability of a calcium sulphate-hydroxyapatite bone substitute.
- 2004
-
Ingår i: Journal of Bone and Joint Surgery: British Volume. - 2044-5377. ; 86:1, s. 120-125
-
Tidskriftsartikel (refereegranskat)abstract
- An injectable material consisting of calcium sulphate mixed with hydroxyapatite was investigated as a possible alternative to autograft in the restoration of bone defects. The material was studied both in vitro in simulated body fluid (SBF) and in vivo when implanted in rat muscles and into the proximal tibiae of rabbits. Variation in the strength and weight of the material during ageing in SBF was measured. Tissue response, material resorption and bone ingrowth were studied in the animal models. A good tissue response was observed in both the rat muscles and rabbit tibiae without inflammatory reactions or the presence of fibrous tissue. Ageing in SBF showed that during the first week carbonated hydroxyapatite precipitated on the surfaces of the material and this may enhance bone ingrowth.
|
|
5. |
- Nilsson, Malin K, et al.
(författare)
-
Factors influencing the compressive strength of an injectable calcium sulfate-hydroxyapatite cement.
- 2003
-
Ingår i: Journal of Materials Science: Materials in Medicine. - 1573-4838. ; 14:5, s. 399-404
-
Tidskriftsartikel (refereegranskat)abstract
- A biphasic injectable bone substitute, suitable for filling bone defects, that sets in the body, based on calcium sulfate and hydroxyapatite (HA), is presented. For applications in bone defects the compressive strength is important to assure support of the defect site during loading when the patient is weight bearing. To control the strength, the influence of four different factors; the liquid-to-powder (L/P) ratio, the HA particle morphology, the HA content and the amount of accelerator, were investigated. alpha-Calcium sulfate hemihydrate (CSH) and four different HA powders (three sintered and one spray-dried) were used. All differed in size and morphology. CSH and each HA powder were mixed together with distilled water to form the bone substitute. An accelerator, in form of calcium sulfate dihydrate, was added to the powder phase to obtain an adequate setting time. Cylindrical specimens were compression tested. A lower L/P-ratio gave stronger cement, but was more difficult to inject. The shape and the morphology of the HA particles influenced the strength, and reducing the amount of HA increased the strength. The amount of accelerator (calcium sulfate dihydrate) had no influence. (C) 2003 Kluwer Academic Publishers.
|
|