| 1. |
- Bernaczyk, Arkadiusz, et al.
(författare)
-
Investigations on the Characterization of Various Adhesive Joints by Means of Nanoindentation and Computer Tomography
- 2022
-
Ingår i: Materials. - : MDPI. - 1996-1944. ; 15:23, s. 8604-8604
-
Tidskriftsartikel (refereegranskat)abstract
- The mechanical properties of cured wood adhesive films were tested in a dry state by means of nanoindentation. These studies have found that the application of adhesives have an effect on the accuracy of the hardness and elastic modulus determination. The highest values of hardness among the tested adhesives at 20 °C have condensation resins: MF (0.64 GPa) and RPF (0.52 GPa). Then the decreasing EPI (0.43 GPa), PUR (0.23 GPa) and PVAc (0.14 GPa) adhesives. The values of the elastic modulus look a little bit different. The highest values among the tested adhesives at 20 °C have EPI (11.97 GPa), followed by MF (10.54 GPa), RPF (7.98 GPa), PVAc (4.71 GPa) and PUR (3.37 GPa). X-ray micro-computed tomography was used to evaluate the adhesive joint by the determination of the voids. It has been proven that this value depends on the type of adhesive, glue quantity and reactivity. The highest values of the void ratio achieve the PUR (17.26%) adhesives, then PVAc (13.97%), RRF (6.88%), MF (1.78%) and EPI (0.03%). The ratio of the gaps increases with the higher joint thickness. A too high proportion of voids may weaken the adhesive joint.
|
|
| 2. |
- Tsolaki, Elena, et al.
(författare)
-
Multiscale multimodal characterization and simulation of structural alterations in failed bioprosthetic heart valves
- 2023
-
Ingår i: Acta Biomaterialia. - 1878-7568 .- 1742-7061. ; 169, s. 138-154
-
Tidskriftsartikel (refereegranskat)abstract
- Calcific degeneration is the most frequent type of heart valve failure, with rising incidence due to the ageing population. The gold standard treatment to date is valve replacement. Unfortunately, calcification oftentimes re-occurs in bioprosthetic substitutes, with the governing processes remaining poorly understood. Here, we present a multiscale, multimodal analysis of disturbances and extensive mineralisation of the collagen network in failed bioprosthetic bovine pericardium valve explants with full histoanatomical context. In addition to highly abundant mineralized collagen fibres and fibrils, calcified micron-sized particles previously discovered in native valves were also prevalent on the aortic as well as the ventricular surface of bioprosthetic valves. The two mineral types (fibres and particles) were detectable even in early-stage mineralisation, prior to any macroscopic calcification. Based on multiscale multimodal characterisation and high-fidelity simulations, we demonstrate that mineral occurrence coincides with regions exposed to high haemodynamic and biomechanical indicators. These insights obtained by multiscale analysis of failed bioprosthetic valves serve as groundwork for the evidence-based development of more durable alternatives. Statement of significance: Bioprosthetic valve calcification is a well-known clinically significant phenomenon, leading to valve failure. The nanoanalytical characterisation of bioprosthetic valves gives insights into the highly abundant, extensive calcification and disorganization of the collagen network and the presence of calcium phosphate particles previously reported in native cardiovascular tissues. While the collagen matrix mineralisation can be primarily attributed to a combination of chemical and mechanical alterations, the calcified particles are likely of host cellular origin. This work presents a straightforward route to mineral identification and characterization at high resolution and sensitivity, and with full histoanatomical context and correlation to hemodynamic and biomechanical indicators, hence providing design cues for improved bioprosthetic valve alternatives.
|
|