1.	Cong, D. Y., et al. (författare) Neutron diffraction study on crystal structure and phase transformation in Ni-Mn-Ga ferromagnetic shape memory alloys 2007 Ingår i: Powder Diffraction. - : Cambridge University Press (CUP). - 0885-7156 .- 1945-7413. ; 22:4, s. 307-311 Tidskriftsartikel (refereegranskat)abstract Crystal structure and phase transformation behaviors in two Ni-Mn-Ga ferromagnetic shape memory alloys (FSMAs) with compositions of Ni48Mn30Ga22 and Ni53Mn25Ga22 (at. %) as a function of temperature were investigated by in situ neutron diffraction experiments. Neutron diffraction technique proves to be highly efficient in characterizing structural transformation in Ni-Mn-Ga FSMAs, which consist of nearby elements in the periodic table. Our neutron results show that Ni48Mn30Ga22 has a cubic, L-21 Heusler structure from 373 to 293 K. Its crystal structure changes into a seven-layered orthorhombic martensitic structure when cooled to 243 K, and no further transformation is observed upon cooling to 19 K. Neutron diffraction results also show that Ni53Mn25Ga22 has a tetragonal 14/mmm martensitic structure from 20 to 403 K. A pre-transformation around room temperature is observed from an abrupt jump in unit-cell volume of Ni53Mn25Ga22, which corresponds with an endothermic peak detected in a heated DSC curve.

Cong, D. Y., et al. (författare)
Neutron diffraction study on crystal structure and phase transformation in Ni-Mn-Ga ferromagnetic shape memory alloys
2007
Ingår i: Powder Diffraction. - : Cambridge University Press (CUP). - 0885-7156 .- 1945-7413. ; 22:4, s. 307-311
Tidskriftsartikel (refereegranskat)abstract
- Crystal structure and phase transformation behaviors in two Ni-Mn-Ga ferromagnetic shape memory alloys (FSMAs) with compositions of Ni48Mn30Ga22 and Ni53Mn25Ga22 (at. %) as a function of temperature were investigated by in situ neutron diffraction experiments. Neutron diffraction technique proves to be highly efficient in characterizing structural transformation in Ni-Mn-Ga FSMAs, which consist of nearby elements in the periodic table. Our neutron results show that Ni48Mn30Ga22 has a cubic, L-21 Heusler structure from 373 to 293 K. Its crystal structure changes into a seven-layered orthorhombic martensitic structure when cooled to 243 K, and no further transformation is observed upon cooling to 19 K. Neutron diffraction results also show that Ni53Mn25Ga22 has a tetragonal 14/mmm martensitic structure from 20 to 403 K. A pre-transformation around room temperature is observed from an abrupt jump in unit-cell volume of Ni53Mn25Ga22, which corresponds with an endothermic peak detected in a heated DSC curve.