| 1. |
- Mahade, Satyapal, 1987-, et al.
(författare)
-
Incorporation of graphene nano platelets in suspension plasma sprayed alumina coatings for improved tribological properties
- 2021
-
Ingår i: Applied Surface Science. - : Elsevier BV. - 0169-4332 .- 1873-5584. ; 570
-
Tidskriftsartikel (refereegranskat)abstract
- Graphene possesses high fracture toughness and excellent lubrication properties, which can be exploited to enhance tribological performance of coating systems utilized to combat wear. In this work, suspension plasma spray (SPS) process was employed to deposit a composite, graphene nano-platelets (GNP) incorporated alumina coating. For comparison, monolithic alumina was also deposited utilizing identical spray conditions. The as-deposited coatings were characterized in detail for their microstructure, porosity content, hardness, fracture toughness and phase composition. Raman analysis of the as-deposited composite coating confirmed retention of GNP. The composite coating also showed good microstructural integrity, comparable porosity, higher fracture toughness and similar alumina phase composition as the monolithic alumina coating. The as-deposited coatings were subjected to dry sliding wear tests. The GNP incorporated composite coating showed lower CoF and lower specific wear rate than the pure alumina coating. Additionally, the counter surface also showed a lower wear rate in case of the composite coating. Post-wear analysis performed by SEM/EDS showed differences in the coating wear track and in the ball wear track of monolithic and composite coatings. Furthermore, Raman analysis in the wear track of composite coating confirmed the presence of GNP. The micro-indentation and wear test results indicate that the presence of GNP in the composite coating aided in improving fracture toughness, lowering CoF and specific wear rate compared to the monolithic coating. Results from this work demonstrated retention of GNP in an SPS processed coating, which can be further exploited to design superior wear-resistant coatings.
|
|
| 2. |
- Lindberg, Siv M, et al.
(författare)
-
A product semantic study of the influence of the sense of touch on the evaluation of wood-based materials
- 2013
-
Ingår i: Materials & design. - : Elsevier BV. - 0264-1275 .- 1873-4197 .- 0261-3069. ; 52, s. 300-307
-
Tidskriftsartikel (refereegranskat)abstract
- Based on product semantics, this study investigated how the tactile attributes of wood and wood-based composites are perceived and interpreted semantically. The wood-based samples included ash, birch, elm, oak, pine, OSB (oriented strand board), two wood pulp-reinforced polylactide composites, Comp A and B and one wood-fiber reinforced polypropene composite, Comp C. The subjects rated the samples by the descriptive words natural, exclusive, eco-. friendly, rough, inexpensive, reliable, warm, modern, snug and solid. The most significant differences between the samples were found for roughness and for the descriptors, reliable, natural and solid. A principal component analysis yielded three attributes based on the tactile perceptions: reliable, old-. fashioned and smooth. The solid wood pieces were perceived as natural and oak was perceived as being exclusive. The composite materials presented a greater variation in terms of perceived attributes than the wood specimens.
|
|
| 3. |
- Åkerfeldt, Maria, 1982, et al.
(författare)
-
Textile piezoelectric sensors – melt spun bi-component poly(vinylidene fluoride) fibres with conductive cores and poly(3,4-ethylene dioxythiophene)-poly(styrene sulfonate) coating as the outer electrode
- 2014
-
Ingår i: Fashion and Textiles. - : Springer Science and Business Media LLC. - 2198-0802. ; 1:1
-
Tidskriftsartikel (refereegranskat)abstract
- The work presented here addresses the outer electroding of a fully textile piezoelectric strain sensor, consisting of bi-component fibre yarns of β-crystalline poly(vinylidene fluoride) (PVDF) sheath and conductive high density polyethylene (HDPE)/carbon black (CB) core as insertions in a woven textile, with conductive poly(3,4-ethylene dioxythiophene)-poly(styrene sulfonate) (PEDOT:PSS) coatings developed for textile applications. Two coatings, one with a polyurethane binder and one without, were compared for the application and evaluated as electrode material in piezoelectric testing, as well as tested for surface resistivity, tear strength, abrasion resistance and shear flexing. Both coatings served their function as the outer electrodes in the system and no difference in this regard was detected between them. Omission of the binder resulted in a surface resistivity one order of magnitude less, of 12.3 Ω/square, but the surface resistivity of these samples increased more upon abrasion than the samples coated with binder. The tear strength of the textile coated with binder decreased with one third compared to the uncoated substrate, whereas the tear strength of the coated textile without binder increased with the same amount. Surface resistivity measurements and scanning electron microscopy (SEM) images of the samples subjected to shear flexing showed that the coatings without the binder did not withstand this treatment, and that the samples with the binder managed this to a greater extent. In summary, both of the PEDOT:PSS coatings could be used as outer electrodes of the piezoelectric fibres, but inclusion of binder was found necessary for the durability of the coating.
|
|
| 4. |
- Grolig, Jan Gustav, 1986
(författare)
-
Coated Ferritic Stainless Steels as Interconnects in Solid Oxide Fuel Cells - Material Development and Electrical Properties
- 2015
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Solid oxide fuel cells (SOFCs) are attracting increasing interest as devices with potentialuses in decentralized and clean electricity and heat production. Several challengeswith respect to materials have to be overcome to achieve efficiencies and life-spansthat are sufficient for long-term applications.An important element of an SOFC stack is the interconnect component, which connectstwo adjacent fuel cell elements. Interconnects, which are commonly composedof ferritic stainless steels, have to be corrosion-resistant, mechanically stable and costoptimized.This work aimed to investigate economic solutions for interconnect materials and tounderstand the underlying mechanisms of degradation and electrical conduction ofthese materials. Mainly two substrates, a commercially available steel (AISI 441) anda ferritic stainless steel that was optimized for an SOFC application (Sandvik SanergyHT) were combined with different barrier coatings and exposed to a cathode-sideatmosphere. A method was developed that allows for the electrical characterizationof promising material systems and model alloys, thereby facilitating a fundamentalunderstanding of the dominant electrical conduction processes linked to the oxidescales that grow on interconnects. The AISI 441 steel coated with reactive elementsand cobalt showed good corrosion and chromium evaporation profiles, while AISI 441coated with cerium and cobalt also had promising electrical properties. The SanergyHT steel was examined with coatings of copper and iron and copper and manganese,respectively. The corrosion and chromium evaporation profiles of Sanergy HT wereimproved by coating with copper and iron. The copper and iron-coated Sanergy HTshowed lower area specific resistance values than cobalt-coated Sanergy HT. Chromia,which is the main constituent of oxide scales, was synthesized using differentmethods. The electrical properties of chromia were found to be sensitive to not onlyimpurities, but also heat treatment. Finally the electrical properties of cobalt- andcobalt cerium-coated Sanergy HT steels were investigated. It was revealed that theaddition of cerium improved the conductivity of the interconnect by both slowingdown chromia growth and preventing the outward diffusion of iron into the spinel.
|
|
| 5. |
- Duan, Shanghong, 1992, et al.
(författare)
-
Determination of transverse and shear moduli of single carbon fibres
- 2020
-
Ingår i: Carbon. - : Elsevier BV. - 0008-6223 .- 1873-3891. ; 158C, s. 772-782
-
Tidskriftsartikel (refereegranskat)abstract
- Carbon fibres are extensively used for their high specific mechanical properties. Exploiting their high axial stiffness and strength, they are employed to reinforce polymer matrix materials in advanced composites. However, carbon fibres are not isotropic. Data of the elastic properties in the other directions of the fibres are still largely unknown. Furthermore, standardised methods to characterise these properties are lacking. In the present work, we propose a methodology to determine the transverse and shear moduli of single carbon fibres. An experimental procedure is developed to fabricate high-quality, flat fibre cross-sections in both longitudinal and transverse directions using Focused Ion Beam, which gives full control of the specimen geometry. Indentation modulus on those surfaces are obtained using both Atomic Force Microscopy (AFM) and nanoindentation tests. Hysteresis was found to occur in the nanoindentation tests. The hysteresis response was due to nano-buckling and reversible shear deformation of the carbon crystals. For this reason, indentation tests using AFM is recommended. From the AFM indentation tests the transverse and shear moduli of three different carbon fibres (IMS65, T800 and M60J) are successfully determined.
|
|
| 6. |
- Johansen, Marcus, 1994, et al.
(författare)
-
Mapping nitrogen heteroatoms in carbon fibres using atom probe tomography and photoelectron spectroscopy
- 2021
-
Ingår i: Carbon. - : Elsevier BV. - 0008-6223. ; 179, s. 20-27
-
Tidskriftsartikel (refereegranskat)abstract
- Carbon fibres show great potential as multifunctional negative electrode for novel structural battery composites – a rechargeable electrochemical cell with structural function. The electrochemical performance of carbon materials can be enhanced with nitrogen heteroatoms, which conveniently are inherent in polyacrylonitrile (PAN)-based carbon fibres. However, it is not fully understood how the electrochemical performance is governed by microstructure and composition of the carbon fibres, particularly the distribution and chemical states of nitrogen heteroatoms. Here we reveal the atom-by-atom three-dimensional spatial distribution and the chemical states of nitrogen in three PAN-carbon fibre types (M60J, T800 and IMS65), using atom probe tomography (APT) and synchrotron hard X-ray photoelectron spectroscopy (HAXPES), and correlate the results to electrochemical performance. The findings pave the way for future tailoring of carbon fibre microstructure for multifunctional applications.
|
|
| 7. |
- Johansen, Marcus, 1994
(författare)
-
Microstructure of Carbon Fibres for Multifunctional Composites: 3D Distribution and Configuration of Atoms
- 2021
-
Licentiatavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Lightweight energy storage is a must for increased driving range of electric vehicles. “Mass-less” energy storage can be achieved by directly storing energy in structural components. In such multifunctional devices called structural composite batteries, carbon fibres carry mechanical load and simultaneously act as negative battery electrode by hosting lithium ions in its microstructure. Little is known of how the microstructure of carbon fibres is optimised for multifunctionality, and deeper understanding of the configuration and the distribution of atoms in carbon fibres is needed. Here synchrotron hard X-ray photoelectron spectroscopy and atom probe tomography are used to reveal the chemical states and three-dimensional distribution of atoms in commercial carbon fibres. This thesis presents the first ever guide for how to perform atom probe tomography on carbon fibres, and the first ever three-dimensional atomic reconstruction of a carbon fibre. The results show that the chemical states and distribution of nitrogen heteroatoms in carbon fibres affect the electrochemical performance of the fibres. Carbon fibres performed electrochemically better with higher amount of nitrogen with pyridinic and pyrrolic configurations. Additionally, the nitrogen concentration varies throughout the carbon fibre, which may suggest that the electrochemical properties also vary throughout the carbon fibre. The knowledge provided by this thesis can lead to future carbon fibre designs with enhanced electrochemical performance for multifunctional applications.
|
|
| 8. |
- André, Alann, et al.
(författare)
-
Finite element delamination study of a notched composite plate under flexural loads
- 2009
-
Ingår i: ICCM-17, 17th International Conference on Composite Materials, Edinburgh, UK. - London : IOM Communications.
-
Konferensbidrag (refereegranskat)abstract
- The delamination process in notched composite plates under flexural loading has been investigated using finite element analysis. Cohesive elements implemented in the commercial finite element package ABAQUS have been used in the region around the drilled-hole, and positioned between layers where delamination was observed during experiments presented in an accompanying paper. The delamination initiation and subsequent propagation was studied between the layers at the tension side separately and simultaneously. For all FE models, the load displacement curve was in good agreement with the one from experiments. However, the amount of damage reported from the fractography study was more extensive than that predicted by the models. Finally, it was shown that the models with only one cohesive layer show significantly different results to that of the model with four cohesive layers in terms of size of the degradation area.
|
|
| 9. |
|
|
| 10. |
- André, Benny
(författare)
-
Nanocomposites for Use in Sliding Electrical Contacts
- 2011
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- In this thesis nanocomposite materials for use in high performance electrical contacts are tested. Self mating silver as coatings on cupper substrates are the most used material combination in power connectors today. In this work two new concepts were tested. The first one was to change one of the mating surfaces to a hard thin coating and keep the other surface made of silver. Tested coatings were nanocomposites with hard carbides in a matrix of amorphous carbon. TiC/a-C and Ti-Ni-C/a-C were tested both electrically and tribologically. The total amount of carbon and the amount of carbon matrix was important, both for the electrical and the tribological properties. The Ti-Ni-C coating also showed that substituting Ti in TiC with the weak carbide former Ni changed the stability of the carbides. The substitution resulted in more a-C matrix and less C in the carbides. Thin coatings of nc-TiC/a-C and Ti-Ni-C/a-C showed high potential as material candidates for use in electrical contacts. The other tested concept was to modify the used silver instead of replacing it. This was done by embedding nanoparticles of solid lubricant IF-WS2 in the silver. The results from reciprocating sliding displayed low friction and high wear resistance. The modified silver surfaces lasted for 8000 strokes with a friction of about 0.3 while at the same time allowing for a low contact resistance. The results for surfaces of pure silver coating displayed a friction of 0.8-1.2 and that the silver was worn through already after 300 strokes. A new method to investigate inherent hardness and residual stress of thin coatings, on complex geometries or in small areas, was also developed. An ion beam was used to create stress free coating as free standing micro pillars. Hardness measured on the pillars and on as-deposited coating were then used to calculate the residual stress in the coatings.
|
|