- D'Ippolito, Veronica, et al.
(författare)
-
Color mechanisms in spinel: cobalt and iron interplay for the blue color
- 2015
-
Ingår i: Physics and chemistry of minerals. - : Springer Science and Business Media LLC. - 0342-1791 .- 1432-2021. ; 42:6, s. 431-439
-
Tidskriftsartikel (refereegranskat)abstract
- Six natural, blue colored spinel crystals were studied chemically by electron microprobe and laser ablation inductively coupled plasma mass spectrometry (LAICP-MS) techniques and optically by UV–VIS–NIR–MIR spectroscopy in the range 30,000–2,000 cm−1 to investigate the causes of their blue color hues. The positions of the absorption bands vary only marginally with the principal composition of the samples (gahnite vs. spinel s.s .). Although blue colors in spinels are frequently the result of various electronic processes in Fe cations, we demonstrate by comparison with synthetic Co-bearing samplesthat Co acts as an important chromophore also in natural spinels. Already at concentration levels of a few ppm (e.g.,>10 ppm), cobalt gives rise to absorption bands at ~18,000, 17,000 and 16,000 cm−1 that result in distinct blue coloration. In spinels with insignificant Co contents, different shades of paler blue (from purplish to greenish blue) colors are caused by electronic transitions in TFe2+, MFe2+, MFe3+ and Fe2+–Fe3+ cation pairs.
|
|
| 5. |
- D'Ippolito, Veronica, et al.
(författare)
-
Crystallographic and spectroscopic characterisation of a natural Zn-rich spinel approaching the endmember gahnite (ZnAl2O4) composition
- 2013
-
Ingår i: Mineralogical magazine. - : Mineralogical Society. - 0026-461X .- 1471-8022. ; 77, s. 2941-2953
-
Tidskriftsartikel (refereegranskat)abstract
- The crystal chemistry of a natural, gem-quality, blue-grey Zn-rich spinel crystal from Jemaa, Kaduna State, Nigeria, was studied using electron microprobe, single-crystal X-ray diffraction, optical absorption and Raman spectroscopies. The composition of the crystal approaches the gahnite endmember (ZnAl2O4), ∼94 mol.%, with the remainder being dominated by a hercynite component (FeAl2O4). The unit-cell dimension is 8.0850(3) Å and the tetrahedral and octahedral bond distances are determined asT–O 1.9485(6) Å andM–O 1.9137(3) Å. Crystal chemical analysis resulted in the empirical structural formulaT(Zn0.94Fe2+0.03Al0.03)M(Al1.96Fe2+0.03Fe3+0.01)O4, which shows Zn and Al almost fully ordered in the tetrahedrally and octahedrally coordinatedTandMsites, respectively. Raman spectra obtained using the excitation of the blue 473.1 nm line of a Nd:YAG laser display three of the five Raman-active modes predicted for the general oxide spinel group of minerals. These are the Egmode at 420.6 cm–1and the T2gmodes at 510 cm–1and 661 cm–1, due to vibrations in the AlO6octahedra. Optical absorption spectra recorded in the UV/VIS-NIR-MIR range 2000 29000 cm–1show a dominant absorption band at ∼5000 cm–1which is caused by spin-allowed electronicd–dtransitions in Fe2+located at theTsites. The blue-grey hue exhibited by the sample is mainly due to spin-forbidden electronic transitions inTFe2+and toMFe2+↔MFe3+intervalence charge transfer, and the poor saturation of the colour is due to the small concentration of Fe2+and Fe3+.
|
|