1.	Wang, Shuai, et al. (författare) In Situ Synthesis of Tungsten-Doped SnO2 and Graphene Nanocomposites for High-Performance Anode Materials of Lithium-Ion Batteries 2017 Ingår i: ACS Applied Materials and Interfaces. - : AMER CHEMICAL SOC. - 1944-8244 .- 1944-8252. ; 9:20, s. 17163-17171 Tidskriftsartikel (refereegranskat)abstract The composite of tungsten-doped SnO2 and reduced graphene oxide was synthesized through a simple one pot hydrothermal method. According to the structural characterization of the composite, tungsten ions were doped in the unit cells of tin dioxide rather than simply attaching to the surface. Tungsten-doped SnO2 was in situ grown on the surface of graphene sheet to form a three-dimensional conductive network that enhanced the electron transportation and lithium-ion diffusion effectively. The issues of SnO2 agglomeration and volume expansion could be also avoided because the, tungsten-doped SnO2 nanoparticles were homogeneously distributed on a graphene sheet. As a result, the nanocomposite electrodes of tungsten-doped SnO2 and reduced graphene oxide exhibited an excellent long-term cycling performance. The residual capacity was still as high as 1100 mA h g(-1) at 0.1 A g(-1) after 100 cycles. It still remained at 776 mA h g(-1) after 2000 cycles at the current density of lA g(-1).

Wang, Shuai, et al. (författare)
In Situ Synthesis of Tungsten-Doped SnO2 and Graphene Nanocomposites for High-Performance Anode Materials of Lithium-Ion Batteries
2017
Ingår i: ACS Applied Materials and Interfaces. - : AMER CHEMICAL SOC. - 1944-8244 .- 1944-8252. ; 9:20, s. 17163-17171
Tidskriftsartikel (refereegranskat)abstract
- The composite of tungsten-doped SnO2 and reduced graphene oxide was synthesized through a simple one pot hydrothermal method. According to the structural characterization of the composite, tungsten ions were doped in the unit cells of tin dioxide rather than simply attaching to the surface. Tungsten-doped SnO2 was in situ grown on the surface of graphene sheet to form a three-dimensional conductive network that enhanced the electron transportation and lithium-ion diffusion effectively. The issues of SnO2 agglomeration and volume expansion could be also avoided because the, tungsten-doped SnO2 nanoparticles were homogeneously distributed on a graphene sheet. As a result, the nanocomposite electrodes of tungsten-doped SnO2 and reduced graphene oxide exhibited an excellent long-term cycling performance. The residual capacity was still as high as 1100 mA h g(-1) at 0.1 A g(-1) after 100 cycles. It still remained at 776 mA h g(-1) after 2000 cycles at the current density of lA g(-1).