- Bykov, Maxim, et al.
(författare)
-
High-pressure synthesis of ultraincompressible hard rhenium nitride pernitride Re-2(N-2)(N)(2) stable at ambient conditions
- 2019
-
Ingår i: Nature Communications. - : NATURE PUBLISHING GROUP. - 2041-1723. ; 10
-
Tidskriftsartikel (refereegranskat)abstract
- High-pressure synthesis in diamond anvil cells can yield unique compounds with advanced properties, but often they are either unrecoverable at ambient conditions or produced in quantity insufficient for properties characterization. Here we report the synthesis of metallic, ultraincompressible (K-0 = 428(10) GPa), and very hard (nanoindentation hardness 36.7(8) GPa) rhenium nitride pernitride Re-2(N-2)(N)(2). Unlike known transition metals pernitrides Re-2(N-2)(N)(2) contains both pernitride N-2(4-) and discrete N3- anions, which explains its exceptional properties. Re-2(N-2)(N)(2) can be obtained via a reaction between rhenium and nitrogen in a diamond anvil cell at pressures from 40 to 90 GPa and is recoverable at ambient conditions. We develop a route to scale up its synthesis through a reaction between rhenium and ammonium azide, NH4N3, in a large-volume press at 33 GPa. Although metallic bonding is typically seen incompatible with intrinsic hardness, Re-2(N-2)(N)(2) turned to be at a threshold for superhard materials.
|
|
| 2. |
- Bykova, Elena, et al.
(författare)
-
Novel Class of Rhenium Borides Based on Hexagonal Boron Networks Interconnected by Short B-2 Dumbbells
- 2022
-
Ingår i: Chemistry of Materials. - : American Chemical Society (ACS). - 0897-4756 .- 1520-5002. ; 34:18, s. 8138-8152
-
Tidskriftsartikel (refereegranskat)abstract
- Transition metal borides are known due to their attractive mechanical, electronic, refractive, and other properties. A new class of rhenium borides was identified by synchrotron single-crystal X-ray diffraction experiments in laser-heated diamond anvil cells between 26 and 75 GPa. Recoverable to ambient conditions, compounds rhenium triboride (ReB3) and rhenium tetraboride (ReB4) consist of close-packed single layers of rhenium atoms alternating with boron networks built from puckered hexagonal layers, which link short bonded (similar to 1.7 angstrom) axially oriented B-2 dumbbells. The short and incompressible Re-B and B-B bonds oriented along the hexagonal c-axis contribute to low axial compressibility comparable with the linear compressibility of diamond. Sub-millimeter samples of ReB3 and ReB4 were synthesized in a large-volume press at pressures as low as 33 GPa and used for material characterization. Crystals of both compounds are metallic and hard (Vickers hardness, H-V = 34(3) GPa). Geometrical, crystal-chemical, and theoretical analysis considerations suggest that potential ReBx compounds with x > 4 can be based on the same principle of structural organization as in ReB3 and ReB4 and possess similar mechanical and electronic properties.
|
|