| 1. |
- Fazi, Andrea, 1992, et al.
(författare)
-
Characterization of as-deposited cold sprayed Cr-coating on Optimized ZIRLO™ claddings
- 2021
-
Ingår i: Journal of Nuclear Materials. - : Elsevier BV. - 0022-3115. ; 549
-
Tidskriftsartikel (refereegranskat)abstract
- As-produced Cr-coated Optimized ZIRLO™ cladding material fabricated with the cold-spray (CS) deposition process is studied. Cross-sectional electron microscopy, nano-hardness profiling, transmission electron microscopy, transmission Kikuchi diffraction, and atom probe tomography (APT) were performed to investigate the nature of the CS Cr-coating/Optimized ZIRLO™ interface, the microstructure of the coating, and the effects of the deposition on the Zr-substrate microstructure. The former surface of the Zr-substrate was found to have a highly deformed nano-crystalline microstructure, the formation of which was attributed to dynamic recrystallization occurring during coating deposition. This microstructural change, evaluated with electron backscattered diffraction and nano-hardness profiling, appeared to be confined to a depth of a few microns. Through APT analysis, a 10–20 nm thick intermixed bonding region was observed at the interface between coating and substrate. The chemical composition of this region suggests that this layer originated from a highly localized shearing and heating of a thin volume of the outermost former surface of the substrate. The study of the intermixed bonding region's crystalline structure was performed with high resolution transmission electron microscopy and revealed a distorted hexagonal close-packed structure.
|
|
| 2. |
- Fazi, Andrea, 1992, et al.
(författare)
-
Comparing CrN and TiN Coatings for Accident-Tolerant Fuels in PWR and BWR Autoclaves
- 2022
-
Ingår i: Journal of Nuclear Engineering. - : MDPI AG. - 2673-4362. ; 3:4, s. 321-332
-
Tidskriftsartikel (refereegranskat)abstract
- The development of coatings for accident-tolerant fuels (ATFs) for light water reactor (LWR) applications promises improved corrosion resistance under accident conditions and better performances during operation. CrN and TiN coatings are characterized by high wear resistance coupled with good corrosion resistance properties. They are generally used to protect materials in applications where extreme conditions are involved and represent promising candidates for ATF. Zr cladding tubes coated with 5 µm-thick CrN or TiN, exposed in an autoclave to simulated PWR chemistry and BWR chemistry, were characterized with SEM, EDS, and STEM. The investigation focused on the performance and oxidation mechanisms of the coated claddings under simulated reactor chemistry. Both coatings provided improved oxidation resistance in a simulated PWR environment, where passivating films of Cr2O3 and TiO2, less than 1 µm-thick, formed on the CrN and TiN outer surfaces, respectively. Under the more challenging BWR conditions, any formed Cr2O3 dissolved into the oxidizing water, resulting in the complete dissolution of the CrN coating. For the TiN coating, the formation of a stable TiO2 film was observed under BWR conditions, but the developed oxide film was unable to stop the flux of oxygen to the substrate, causing the oxidation of the substrate.
|
|